Highly soluble and optically transparent poly (ether imide)s based on 2,6‐ or 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and aromatic bis(ether amine)s bearing trifluoromethyl groups

Two series of novel fluorinated poly(ether imide)s (coded IIIA and IIIB ) were prepared from 2,6‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride and 2,7‐bis(3,4‐dicarboxyphenoxy)naphthalene dianhydride, respectively, with various trifluoromethyl‐substituted aromatic bis(ether amine)s by a standard two‐step process with thermal or chemical imidization of the poly(amic acid) precursors. These fluorinated poly(ether imide)s showed good solubility in many organic solvents and could be solution‐cast into transparent, flexible, and tough films. These films were nearly colorless, with an ultraviolet–visible absorption edge of 364–386 nm. They also showed good thermal stability with glass‐transition temperatures of 221–298 °C, 10% weight loss temperatures in excess of 489 °C, and char yields at 800 °C in nitrogen greater than 50%. The 2,7‐substituted IIIB series also showed better solubility and higher transparency than the isomeric 2,6‐substituted IIIA series. In comparison with nonfluorinated poly (ether imide)s, the fluorinated IIIA and IIIB series showed better solubility, higher transparency, and lower dielectric constants and water absorption. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5909–5922, 2006     

Synthesis and micellization of amphiphilic poly(sebacic anhydride)–poly(ethylene glycol)–poly(sebacic anhydride) block copolymers

Amphiphilic biodegradable block copolymers [poly(sebacic anhydride)–poly(ethylene glycol)–poly(sebacic anhydride)] were synthesized by the melt polycondensation of poly(ethylene glycol) and sebacic anhydride prepolymers. The chemical structure, crystalline nature, and phase behavior of the resulting copolymers were characterized with ¹H NMR, Fourier transform infrared, gel permeation chromatography, and differential scanning calorimetry. Microphase separation of the copolymers occurred, and the crystallinity of the poly(sebacic anhydride) (PSA) blocks diminished when the sebacic anhydride unit content in the copolymer was only 21.6%. ¹H NMR spectra carried out in CDCl₃ and D₂O were used to demonstrate the existence of hydrophobic PSA domains as the core of the micelle. In aqueous media, the copolymers formed micelles after precipitation from water‐miscible solvents. The effects on the micelle sizes due to the micelle preparation conditions, such as the organic phase, dropping rate of the polymer organic solution into the aqueous phase, and copolymer concentrations in the organic phase, were studied. There was an increase in the micelle size as the molecular weight of the PSA block was increased. The diameters of the copolymer micelles were also found to increase as the concentration of the copolymer dissolved in the organic phase was increased, and the dependence of the micelle diameters on the concentration of the copolymer varied with the copolymer composition. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1271–1278, 2006     

Synthesis and properties of noncoplanar rigid‐rod aromatic polyhydrazides and poly(1,3,4‐oxadiazole)s containing phenyl or naphthyl substituents

Two new phenyl‐ and naphthyl‐substituted rigid‐rod aromatic dicarboxylic acid monomers, 2,2′‐diphenylbiphenyl‐4,4′‐dicarboxylic acid ( 4 ) and 2,2′‐di(1‐naphthyl)biphenyl‐4,4′‐dicarboxylic acid ( 5 ), were synthesized by the Suzuki coupling reaction of 2,2′‐diiodobiphenyl‐4,4′‐dicarboxylic acid dimethyl ester with benzeneboronic acid and naphthaleneboronic acid, respectively, followed by alkaline hydrolysis of the ester groups. Four new polyhydrazides were prepared from the dicarboxylic acids 4 and 5 with terephthalic dihydrazide (TPH) and isophthalic dihydrazide (IPH), respectively, via the Yamazaki phosphorylation reaction. These polyhydrazides were amorphous and readily soluble in many organic solvents. Differential scanning calorimetry (DSC) indicated that these hydrazide polymers had glass transition temperatures in the range of 187–234 °C and could be thermally cyclodehydrated into the corresponding oxadiazole polymers in the range of 300–400 °C. The resulting poly(1,3,4‐oxadiazole)s exhibited T_g's in the range of 252–283 °C, 10% weight‐loss temperature in excess of 470 °C, and char yield at 800 °C in nitrogen higher than 54%. These organo‐soluble polyhydrazides and poly(1,3,4‐oxadiazole)s exhibited UV–Vis absorption maximum at 262–296 and 264–342 nm in NMP solution, and their photoluminescence spectra showed maximum bands around 414–445 and 404–453 nm, respectively, with quantum yield up to 38%. The electron‐transporting properties were examined by electrochemical methods. Cyclic voltammograms of the poly(1,3,4‐oxadiazole) films cast onto an indium‐tin oxide (ITO)‐coated glass substrate exhibited reversible reduction redox with E_onset at ?1.37 to ?1.57 V versus Ag/AgCl in dry N,N‐dimethylformamide solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6466–6483, 2006     

Highly substituted poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives having bulky phenyl and fluorenyl pendant groups: Synthesis,characterization, and electro‐optical properties

Two series of poly(2,3‐diphenyl‐1,4‐phenylenevinylene) (DP‐PPV) derivatives containing multiple bulky substituents were synthesized. In the first series, two different groups were incorporated on C‐5,6 positions of the phenylene moiety to increase steric hindrance and to obtain blue‐shifted emissions. In the second series, bulky fluorenyl groups with two hexyl chains on the C‐9 position were introduced on two phenyl pendants to increase the solubility as well as steric hindrance to prevent close packing of the main chain. Polymers with high molecular weights and fine‐tuned electro‐optical properties were obtained by controlling the feed ratio of different monomers during polymerization. The maximum photoluminescent emissions of the thin films are located between 384 and 541 nm. Cyclic voltammetric analysis reveals that the band gaps of these light‐emitting materials are in the range from 2.4 to 3.3 eV. A double‐layer EL device with the configuration of ITO/PEDOT/P4/Ca/Al emitted pure green light with CIE′1931 at (0.24, 0.5). Using copolymer P6 as the emissive layer, the maximum luminescence and current efficiency were both improved when compared with the homopolymer P4. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6738–6749, 2006     

Further study of the viscoelastic phase separation of cyanate ester modified with poly(ether imide)

In this study, the viscoelastic phase separation process was studied further by time‐resolved light scattering, differential scanning calorimetry, and scanning electron microscopy in the system of poly(ether imide)‐modified bisphenol‐A dicyanate. It was observed that the evolution time of phase structure and relaxation time of diffusion flow of the bisphenol‐A dicyanate were similar with the phase diagram of curing conversion versus content of PEI. The results suggested that the viscoelastic phase separation was affected by the curing conversion of the system at the onset point of phase separation. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 517–523, 2006     

Novel photoswitching dithienylethenes with ferrocene units

Two novel dithienylethenes with ferrocene units were synthesized by Wittig reaction. The structure of 2a has been established by X‐ray diffraction studies. They could reversibly interconvert between two thermally stable forms, an open and a closed one, using light of different wavelengths as triggers. Copyright © 2006 John Wiley & Sons, Ltd.     

关于Tchebycheff—Fourier级数的（H,λ）平均的逼近

我们定义了（Ｈ，λ）求和法，它含有（Ｎ，ｐｎ），（Ｒ＾ｒｎ）和（Ｖｍｎ）求和法。讨论了函数ｆ（ｘ）∈Ｃ＾ｒ［－１，１］（ｒ∈Ｎ０）以及ｆ（ｘ）∈Ｗ＾ｒＨ＾ａ（ｒ∈Ｎ０，０＜ａ＜１）的切比晓夫－富里埃级数的逼近阶。     

气密性碳涂覆光纤筛选强度与电阻关系研究

通过实验分析确立了把光纤电阻作为衡量气密性碳涂覆光纤通过２％应变筛选的过渡标准。要拉制２％应变筛选的碳涂覆光纤，其电阻值应小于３０ｋΩ／ｃｍ。     

MnBiDy(Sm)永磁膜的结构和磁性

报道了采用真空蒸镀的方法制备的MnBiDy(Sm)永磁膜的结构和磁性.Mn:Bi:Dy(Sm)的投料比为2:1:0.10.薄膜经过退出处理(350—425℃,保温4h)后,具有NiAs型hcp结构,C轴垂直膜面,剩余磁感应强度B=3.4-6.5kG,内禀矫顽力_MH_c≈3-8kOe,最大磁能积(BH)_(max)=13.39MG·Oe.实验发现,薄膜厚度对MnBiDy(Sm)永磁膜的结构和磁性具有很大的影响. 关键词：