电化学沉积金属铜的分形枝晶生长控制与性能

 以CuSO_{4/sub>为前驱体,HCl为添加剂,采用电化学沉积方法,在室温条件下制得了μm级、面心立方结构分形铜的枝状晶体,研究了铜离子浓度、硫酸浓度、电流密度、沉积时间、氯离子浓度等实验参数对分形枝状铜晶体尺寸、结构的影响。结果表明：硫酸的浓度对铜沉积物结构无明显影响;随着Cu^{2+/sup>浓度的不断增大,铜沉积物的分形效果越来越明显;增大电流密度（0.4～1.6 A·cm-2/sup>）,铜沉积物由致密向多分枝的开放型转变;延长沉积时间（大于等于5 min）,可获得含大量次级分枝铜的晶体;适当增加盐酸用量（0.05～0.20 mol/L）,铜沉积物枝晶尺寸显著减小。最后讨论了分形枝晶铜在碱性条件下氧化甲醇的电化学性能。}}     

碳气凝胶及活化碳气凝胶电极材料制备与性能

 以间苯二酚(R)-甲醛(F)为原料,制备了有机气凝胶和碳气凝胶,并对其进行二氧化碳活化。X射线衍射(XRD)测试表明,二氧化碳渗入到碳气凝胶网络结构发生反应,造成(002)峰和(100)峰减弱;扫描电子显微镜(SEM)测试表明,活化没有破坏碳气凝胶的骨架结构,而是增加了大量的nm尺度微孔,从而大大提高了碳气凝胶的比表面积和微孔比例。在1 mol/L KOH电解液中进行了循环伏安和计时电位扫描测试,电极材料电化学性能稳定,具有较好的可逆性,在1 mA/s电流密度下进行充放电测试,得到活化前电极比电容为103 F/g,活化后由于比表面积的增加,比电容达到371 F/g,是一种理想的电化学电极材料。     

Mn-Cu合金成分对去合金化法制备纳米多孔铜的影响

 采用电弧熔炼制备出前驱体Mn-Cu合金,在稀盐酸溶液中自由腐蚀去合金化,制备出具有双连续结构的纳米多孔铜。研究了前驱体合金的成分对纳米多孔铜微观结构及Mn的选择性腐蚀程度的影响。结果表明：前驱体Mn-Cu合金的Cu原子分数为43%时,其去合金化受到抑制,存在明显的未完全去合金化的岛状结构;前驱体Mn-Cu合金的Cu原子分数为32%～23%时,可完全去合金化,形成平均孔径尺寸为20～100 nm,平均系带尺寸为30～80 nm,具有双连续结构的纳米多孔铜;前驱体Mn-Cu合金的Cu原子分数低至20%时,去合金化后存在大量裂纹,形成纳米颗粒聚集体。纳米多孔铜中存在少量的残余Mn,残余Mn的原子分数随着前驱体合金Mn原子分数的增高而降低。实验表明腐蚀液浓度对纳米多孔铜形貌也存在影响。     

三波长分光光度法研究：Ⅲ.两测量波长法提高测定灵敏度

本实验利用两测量波长法提高三波长光光度法的灵敏度，选择合适的波长组合，消除两种共存组分的干扰，使△Ａ＝Ａλ１＋Ａλ２－ＫＡλ３只与待测组分的浓度有关，灵敏度一般均高于单波长法。以相对误差为选择波长组合的标准，编制了程序，用计算机选择合适的波长组合，验证结果令人满意。     

Depolymerization of Free‐Radical Polymers with Spin Migrations

The mechanism of depolymerization is one of the most essential issues in chemical engineering and materials science. In this work, we investigate the depolymerization reactions of three typical free‐radical poly(alpha‐methylstyrene) tetramers by using first‐principles density functional theory. The calculated results show that these reactions all need to overcome the energy barriers in the range of 0.58 to 0.77 eV, and that breaking the C?C bond at the chain end leads to the dissociation of alpha‐methylstyrene monomers from the polymers. Electronic‐structure analysis indicates that the reactions occur easily at the CR₃ unsaturated end, and that the frontier molecular orbitals that participate in the reactions are mainly localized at the unsaturated ends. Meanwhile, spin population analysis presents the unique net spin‐transfer process in free‐radical depolymerization reactions. We hope the current findings can contribute to understanding the free‐radical depolymerization mechanism and help guide future experiments.     

Fingerprint and multicomponent quantitative analysis for the quality evaluation of Sibiraea angustata leaves by HPLC-DAD and HPLC-ESI-MS/MS combined with chemometrics

Sibiraea angustata leaves, known as a traditional Tibetan medicine, have been specially used in the treatment of indigestion and obesity. In the study, a simple and sensitive high-performance liquid chromatography (HPLC) method with a diode array detector (DAD) was established to solve the problem of lacking quality standard of S. angustata leaves, including the fingerprint analysis and quantification of six characteristic components. The analytical method was validated for linearity, repeatability, stability, recovery, and specificity. Seventeen raw samples and 1 processed sample of S. angustata leaves were collected from different locations of China to establish the fingerprint. The chemometric methods, including similarity analysis (SA), principal component analysis (PCA), and hierarchical clustering analysis (HCA), were applied to distinguish the 18 batches of S. angustata samples. The results successfully sorted these samples into five clusters and kept in line with each other. According to the result of the fingerprint analysis, 21 peaks were extracted to be the common peaks and most of them were identified by mass spectrometry (MS) with electron-spray ionization (ESI) in the negative mode. Meanwhile, the loading plot of PCA further indicated that the peaks of neochlorogenic acid, chlorogenic acid, ferulic acid, rutin, hyperin, and isoquercitrin played a greater role in the discrimination among the 21 peaks. So the six components mentioned above were investigated as index constituents to evaluate the quality of S. angustata leaves from different locations. The study demonstrated that the developed new method was a beneficial approach for authentication and quality evaluation of S. angustata leaves.     

Cun、Agn和Aun(n≤9)团簇的静电极化率

采用B3LYP密度泛函的方法计算了Cun，Agn和Aun(n≤9)团簇的静电极化率和极化率的各向异性，并与Na原子团簇进行比较，结果表明，Cun和Agn团簇的极化率与团簇大小的关系与Na原子团簇类似，而Aun团簇的极化率有所不同；Au原子的极化率较小，而从Au2至Au7，Aun团簇极化率变化趋势与Cun和Agn团簇相似。重金属元素团簇的极化率小于Na原子团簇的极化率，具有更加紧致结构。     

电化学在ICF靶制备中的新应用

报道了近年来在电解加工技术制备理论密度金属薄膜和电沉积技术制备金属纳米丝阵列材料等领域取得的进展。采用硫酸+甲醇电解液体系获得了表面粗糙度小于30nm的钛膜。采用阳极氧化铝模板电沉积技术制备出长度约10μm、直径约300nm的金纳米丝阵列。主要讨论了电解液配方及电解加工参数的选择,金属纳米丝直径与长度的控制等问题。     

靶丸X射线数字图像的轮廓分析及功率谱评价

 针对多层靶丸X射线数字图像的成像原理和轮廓边缘进行了理论分析;推导了由靶丸边缘特征点确定靶丸圆心和半径的精确最小二乘拟合算法;对于不同类型(阶跃状或屋顶状)的靶丸图像边缘,采用均化二阶微分算法或径向吸收强度最小二乘洛伦兹型拟合寻峰算法获取亚像素精度的靶丸圆周轮廓边缘数据;应用快速傅里叶变换算法对靶丸圆周轮廓数据进行分析,获得了靶丸表面外轮廓或内轮廓模数-功率谱特征曲线。     

放电等离子烧结制备纳米Ni块体材料

 采用自悬浮定向流法制备纳米Ni粉体,利用放电等离子烧结技术制备出了直径10 mm、厚2 mm,致密度为96.8 %,显微硬度为4.17 GPa的纳米块体材料。用X射线衍射仪、扫描电子显微镜和显微硬度计分析了烧结块体样品的相组成、晶粒尺寸、微观形貌和显微硬度。研究表明：随烧结温度的升高,块体样品的致密度和晶粒尺寸增大,当烧结温度为650 ℃时,致密度最高,晶粒尺寸为44.8 nm;显微硬度随烧结温度的增高先增大后减小,当烧结温度为550 ℃时,显微硬度最大为4.33 GPa;较高烧结温度下,断口微观形貌的纳米级韧窝出现,显示了韧性断裂的特征。