用密度泛函理论研究了CF3SO3CF2CF3 F^-的碳氧键断裂反应的机理。首先，用DFT方法优化了反应物、中间体、过渡态、产物的平衡构型，分析了碳氧键断裂反应的势能面变化，发现在SN2反应机理中，除了S-O断裂SN2反应外，引起C-O键断裂的同面进攻也是一个可能的反应途径。理论计算表明，最终反应的产物是受热力学控制的，S-O键的断裂绝对地优于C-O的断裂。因此，C-O断裂的同面机理虽然是可能的，但却难以被实验观察到，本文还讨论了端基-CF3在同面SN2反应中的邻位效应，以及基组对这个效应的影响。     

PREPARATION OF MICROGEL-EPOXY RESIN TWO-PHASE POLYMERS BY IN SITU POLYMERIZATION~*

Microgel-epoxy resin two-phase polymers were prepared by in situ copolymerization of ethylenic monomers with unsaturated polyesters. The choice of monomers and the effect of monomer concentration on microgel particle size were discussed. Agglomeration of particles played a significant role in the early stage of polymerization. The microgel dispersion in epoxy resin was stable after the finish of polymerization. Upon curing the particles remained well dispersed.     

含二苯甲烷结构四元共缩聚杂萘聚芳酰胺的合成与性能

采用自制二胺1,2-二氢-2-(4-氨基苯基)-4-[4-(4-氨基苯氧基)-苯基]-二氮杂萘-1-酮、商品二胺4,4′-二氨基二苯甲烷和对苯二胺与对苯二甲酰氯进行低温溶液缩聚反应,改变三种二胺的比例,得到了一系列共聚酰胺树脂,其特性粘数为1·24~2·32dL/g,用FT-IR、1H-NMR手段研究了聚合物的结构;利用DSC和TGA研究了聚合物的耐热性能,结果表明,该类聚合物具有较高玻璃转化温度(301℃以上);氮气气氛中5%热失重温度在438℃以上;用一定比例的二胺制得的聚合物分别能溶于N-甲基吡咯烷酮、N,N-二甲基乙酰胺等非质子极性溶剂中并浇注得到韧性薄膜.     

A Novel Dihydroflavone from the Roots of Uvaria Macrophylla

A new dihydroflavone (1), named macrophyllol A, was isolated from the roots of Uvaria macrophylla. Its structure was elucidated on the basis of spectroscopic evidence.     

Dawson结构钼钒磷杂多化合物对苯酚过氧化氢羟化作用的研究

Ｄａｗｓｏｎ结构钼钒磷杂多化合物对苯酚过氧化氢羟化作用的研究于剑锋，杨宇，吴通好，孙家锺（吉林大学化学系理论化学研究所，长春，１３００２３）关键词Ｄａｗｓｏｎ结构钼钒磷杂多化合物，苯酚羟化，过氧化氢苯二酚（ＤＢＨ）是重要的化工原料．由芳香化合物羟化制...     

辐照对聚己内酯结构和性能的影响

研究了γ 辐照对不同分子量的聚己内酯 (PCL)的力学性能、热性能、结晶行为的影响 ,在此基础上 ,研究了辐射交联后的PCL的形状记忆行为 .研究结果表明 ,PCL的分子量越大 ,辐射交联所需的凝胶化剂量越低 .溶胶分数S +S1 2 与 1 D的关系很好地符合Charlesby Pinner关系式 ,说明PCL的辐射交联属于无规交联 .剂量对PCL的力学性能影响显著 ,剂量越大 ,抗张强度和断裂伸长率下降越多 ,但分子量较高的PCL的抗张强度受剂量的影响较小 .DMA分析表明 ,聚己内酯辐照交联后的弹性模量和耐热性能显著提高 .交联度较高的PCL表现出高弹态 ,可以拉伸 ,并具有较好的形状记忆行为 .DSC分析表明 ,辐射交联使PCL的结晶度有所增加 ,但也使结晶熔点有所降低     

The Adsorption of NOx on Magnesium Aluminium Hydrotalcite

Magnesium aluminium hydrotalcite (Mg-Al-HT) with molar ratio of Mg-to-Al of 3 to 1 was prepared and characterized by X-ray diffraction (XRD) and infrared spectra (IR). The performances of Mg-Al-HT for the adsorption and desorption of NOx were studied. The results indicated that the adsorption capacity of the hydrotalcite for NOx was 1398.2mg/g, and it was higher than the acticarbon‘s. The adsorption capacities depended on adsorption time and temperature.Mg-Al-HT could be regenerated by thermal decomposition, and the adsorption efficiency had not changed markedly after three cycles.     

开链冠醚Schiff碱-稀土配合物的合成、表征及近红外发光光谱研究

合成了3个新型开链冠醚Schiff碱-稀土离子三元配合物RE(H2L)(Mq)(NO3)3,其中RE=Nd3 ,Er3 ,Yb3 ,配体H2L=N,N-双(邻羟苯亚甲基)-3,6-二氧杂-1,8-二氨基辛烷,Mq为8-羟基喹哪啶.采用元素分析、红外光谱(IR)、紫外-可见吸收光谱(UV-vis)、热重-差热分析(TG-DTG)等手段对配合物的组成结构进行了表征.测定了3种新型结构稀土三元配合物在不同温度(77 K和300 K)时的近红外发光光谱.     

A New and Efficient Synthetic Method and Antibacterial Activities of Oxazolidinone Analogues

A series of novel oxazolidinone analogues were prepared by a new and efficient synthetic method and their antibacterial activities were determined. These compounds wer echaracterized by LC-MS and ^1H NMR.     

微波合成铝掺杂钻酸锂材料及性能研究

以LiOH·H2O，Al2O3和Co3O4为原料，微波加热合成Li离子电池正极材料LiAlxCo（1-x）O2．通过XRD测试表征了不同Al加入量时合成产物的晶体结构，确定当x≤0．4时，产物为单一相层状结构．计算了不同x时LiAlxCo（1-x）O2的晶胞参数，随着x的增大，a值减小，c值增大．对合成LiAlxCo（1-x）O2样品进行DSC—TGA测试，结果表明，当x不同时，合成样品的热稳定性不同．SEM测试表明，合成晶体粒度较均匀，粒径在5μm左右．电化学测试表明，LiAl0.2Co0.8O2的电化学性能最好，首次循环放电容量为127mAh／g，多次循环容量损失率小于LiCoO2．