玻璃陶瓷材料中Tm3+离子红外到蓝色上转换发光

系统研究了PbF2+GeO2+WO3ⅩⅣTmF3玻璃陶瓷材料中,在近红外光(1.06μm)激发下,Tm3+离子的发光特性.实验中观测到Tm3+离子的两组峰值位置分别在20920cm-1和22173cm-1的蓝色上转换发光,并证实这两组上转换发光分别与吸收三个和四个光子有关,同时建立了上转换发光的模型.为了选择最佳掺杂浓度,详细地测量了Tm3+离子峰值为20920cm-1的蓝色上转换发光强度与TmF3浓度的关系.     

Direct visual evidence for chemical mechanisms of SERRS via charge transfer in Au20–pyrazine–Au20 junction

The essence of the chemical mechanism for surface‐enhanced resonance Raman scattering (SERRS) is the charge transfer (CT) between the metal and the molecule at the resonant electronic transition, which results in the mode‐selective enhancement in the SERRS spectrum. The site‐orientated CT can directly interpret the mode‐selective chemical enhancement in SERRS. However, it is a great challenge to intutively visualize the orientation and site of the CT. In this paper, for the pyrazine–Au₂ complex, a three‐dimensional (3D) cubic representation is built to provide direct visual evidence for chemical mechanisms of SERRS via CT from the Au₂ cluster to pyrazine at the resonant electronic transition. The relationship between the mode‐selective enhancements in SERRS and the site‐orientated CT was clearly revealed. The intracluster excitation (analog of plasmon excitation in large naonoparticles) was also visualized by the 3D cubic presentation, which provided the direct evidence of local electromagnetic field enhancement of SERRS. To study the quantum size effect and the coupling effect of the nanoparticles, the photoexcitation mechanisms of the Au₂₀–pyrazine complex and the Au₂₀–pyrazine–Au₂₀ junction were also investigated. The tunneling charge transfer from one Au₂₀ cluster to another Au₂₀ cluster outside the pyrazine in Au₂₀–pyrazine–Au₂₀ junction was also revealed visually. The calculated normalized extinction spectra of Au nanoparticles using the generalized Mie theory reveal that the resonance peak is red‐shifted due to the coupling between particles. Copyright © 2009 John Wiley & Sons, Ltd.     

电子琴频谱的实验研究

介绍一个学生实验，用最基本的频谱分析方法，以ＣＡＳＩＯ ＭＴ－１８电子琴作声源，对其中四种模拟乐器乐音信号的频谱进行测量及分析。     

双层有机EL器件ITO/PPV/Alq3/Al发光稳定性的研究

制备了一组由PPV和Alq3组成的双层有机EL器件ITO/PPV/Alq3/Al;比较了两个发光层厚度不同时器件发光性能的差异.测试和分析了温度、真空度、工作电压和存放时间对器件衰减规律的影响.     

羰基镍分析报警仪

羰基镍分析报警仪运用化学发光原理构成，不仅适用于羰基镍生产车间现场的检测和报警，也适于实验室的研究工作。检出限达0.037mg/m^3(0.5ppb），响应时间2min。     

外加电场对光折变高阶响应影响的微扰分析

应用微扰展开法了“跳跃模型”给出了空间电荷场前三阶分量随时间，外加电场等变化的解析表达式，同时讨论了外加电场对各阶空间电荷场建立的影响，当扩散与外加电场可比拟时，外加电场对空间电荷场的影响不大，随着空间电荷场阶数的提高，其达到最大饱和值所需的外加电磁越小，在外加电场作用下，空间电荷场各阶分量随时间呈振荡衰减，直到达到饱和，外加是场越大，振荡越强烈，周期越短，在考虑高阶分量的贡献后，空间电荷场的振荡     

一种求解虚波长路径光网络波长资源优化问题的启发式算法

本文提出了一种虚波长路径光网络的启发式路由选择算法,它可以用来解决以最小化网络所需波长数目为目标的资源优化问题.该算法应用了基于最大概率路径的选路优化策略.对一个样例网络的数值分析结果表明该算法是有效的.     

α,α′-二氧代烯酮环二氮代缩醛的NMR研究

报道了5种新的α，α′-二氧代烯酮环二氮代缩醛化合物的NMR谱，初步探讨了分子结构对化学位移的影响．     

Direct writing waveguides inside YAG crystal by femtosecond laser

A 120 fs Ti-sapphire laser was used to fabricate waveguides in YAG crystal. A 7 mm long waveguide was written at a position of 100 μm below the surface, which shows multimode propagation at 633 nm with optical attenuation of about 0.2 dB/mm. The light guiding occurs in the region around the visible laser-damaged region, indicating that the light guiding area is induced by stress. The waveguide exhibited strong birefringence property with maximum magnitude of about 1.5 × 10⁻⁵. Infrared and Raman spectroscopy analysis indicate there is no change in chemical composition in laser-modified zone.     

Novel approach to preparation of LiMn2O4 core/LiNixMn2−xO4 shell composite

Combining two methods, coating and doping, to modify spinel LiMn₂O₄, is a novel approach we used to synthesize active material. First we coated the LiMn₂O₄ particles with the nickel oxide particles by means of homogenous precipitation, and then the nickel oxide-coated LiMn₂O₄ was calcined at 750 °C to form a LiNi_xMn_2−xO₄ shell on the surface of spinel LiMn₂O₄ particles. Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), cyclic voltammetry (CV) and charge-discharge test were performed to characterize the spinel LiMn₂O₄ before and after modification. The experimental results indicated that a spinel LiMn₂O₄ core is surrounded by a LiNi_xMn_2−xO₄ shell. The resulting composite showed excellent electrochemical cycling performance with an average fading rate of 0.014% per cycle. This improved cycle stability is greatly attributed to the suppression of Jahn-Teller distortion on the surface of spinel LiMn₂O₄ particles during cycling.