Synthesis and properties of poly(phenylacetylenes) having two polar groups or one cyclic polar group on the phenyl ring

Phenylacetylene (PA) derivatives having two polar groups (ester, 2a – d ; amide, 4) or one cyclic polar group (imide, 5a – c ) were polymerized using (nbd)Rh⁺[(η⁶‐C₆H₅)B^?(C₆H₅)₃] catalyst to afford high molecular weight polymers (～1 × 10⁶ – 4 × 10⁶). The hydrolysis of ester‐containing poly(PA), poly( 2a) , provided poly(3,4‐dicarboxyPA) [poly ( 3 )], which could not be obtained directly by the polymerization of the corresponding monomer. The solubility properties of the present polymers were different from those of poly(PA) having no polar group; that is, poly( 2a )–poly( 2d ) dissolved in ethyl acetate and poly( 4 ) dissolved in N,N‐dimethylformamide, while poly(PA) was insoluble in such solvents. Ester‐group‐containing polymers [poly( 2a )–poly( 2d )] afforded free‐standing membranes by casting from THF solutions. The membrane of poly( 2a ) showed high carbon dioxide permselectivity against nitrogen (PCO₂/PN₂ = 62). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5943–5953, 2006     

Synthesis of TiO2–SiO2/polymer core–shell microspheres with a microphase‐inversion method

A novel microphase‐inversion method was proposed for the preparation of TiO₂–SiO₂/poly(methyl methacrylate) core–shell nanocomposite particles. The inorganic–polymer nanocomposites were first synthesized via a free‐radical copolymerization in a tetrahydrofuran solution, and the poor solvent was added slowly to induce the microphase separation of the nanocomposite and result in the formation of nanoparticles. The average particle sizes of the microspheres ranged from 70 to 1000 nm, depending on the reaction conditions. Transmission electron microscopy and scanning electron microscopy indicated a core–shell morphology for the obtained microspheres. Thermogravimetric analysis and X‐ray photoelectron spectroscopy measurements confirmed that the surface of the nanocomposite microspheres was polymer‐rich, and this was consistent with the core–shell morphology. The influence of the synthetic conditions, such as the inorganic composition and the content of the crosslinking monomer, on the particle properties was studied in detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3911–3920, 2006     

Selective and simultaneous determination of phosphate and silicate ions in leaching process waters for ceramics glaze raw materials of narutal origin by ion-exclusion chromatography coupled with UV-detection after postcolumn derivatization.

The selective and simultaneous ion-exclusion chromatography (IEC) with UV-detection on a weakly acidic cation-exchange resin column in the H+ -form (TSKgel Super IC-A/C) was developed and applied for the simultaneous determination of phosphate and silicate ions as the water quality parameters required for optimizing the water-leaching process for ceramics glaze raw materials of natural origin including feldspar, woods-ash, and straw-ash. Phosphate and silicate ions in these water-leaching process water samples were separated selectively from the coexisting anions such as sulfate, chloride, nitrate and carbonate ions, based on the ion-exclusion separation mechanism. They were detected selectively and simultaneously by a postcolumn derivatization with molybdenum-yellow using the UV-detector. Under the optimized separation and detection conditions (eluent, 0-1 mM sulfuric acid; reactant, 10 mM sodium molybdate-25 mM sulfuric acid; detector, UV at 370 nm; temperature, 45 degrees C), the linearity of calibration was in the range 0.1 - 10 ppm for both phosphate and silicate ions, and the detection limits at S/N = 3 were 2.58 ppb for silicate ions and 4.75 ppb for phosphate ions. The effectiveness of this method was demonstrated in practical applications to the water-leaching process for some ceramics glaze raw materials.     

Pyraflufen-ethyl residues in soil by solid phase extraction and high-performance liquid chromatography with UV detection.

Solid-phase extraction (SPE) procedure for cleanup followed by HPLC-UV method has been investigated for the determination of pyraflufen-ethyl residues in soil. The pesticide is extracted from the sample with acetone-water (80:20, v/v) and the extract is loaded onto an octadecyl (C(18)) column. The pesticide is eluted with acetonitrile and determined by HPLC with a UV detector. Using an acetone-water extraction followed by a C(18) cleanup, this method is characterized by recovery >90.1%, precision <5.8% RSD and sensitivity of 0.01 mg/kg. The proposed method has been successfully employed for the determination of the degradation dynamics of pyraflufen-ethyl in four agricultural soil samples under laboratory conditions.     

Effects of microstructure on the temperature dependence of relative initial permeability of NiCuZn ferrites

In the present work, ferrites with compositions of (Ni_0.27Zn_0.64Cu_x)Fe_1.98O₄ (x=0.1, 0.2) were prepared by conventional ceramic methods. The relationship between the microstructure and the temperature dependence of relative initial permeability was investigated. It was found that intergranular pores in the ferrites generate large demagnetizing fields, reducing the temperature dependence of the effective anisotropy field H_eff, and decreasing the temperature dependence of the relative initial permeability accordingly. However, intragranular pores pin the movement of domain walls. Compared with the permeability induced by domain wall motion, the permeability that resulted from the spin rotation is more sensitive to temperature. As a result, the relative initial permeability of ferrites becomes more sensitive to temperature with increasing micropores within grains.     

Influence of chemistry and hot rolling conditions on high permeability non-grain oriented silicon steel

This paper discusses the influence of chemical composition on the final electromagnetic properties in higher permeability material. Furthermore, the effect of the hot rolling practice and the end of austenite transformation temperature range on the hot band microstructure is described. The magnetic polarization J₅₀₀₀ better than 1.7 T, using hot rolling conditions 40 mm transfer bar thickness, finish mill entry temperature 1000 °C, and finishing temperature 800–840 °C and after decarburization heat treatment and grain growth treatment, was obtained.     

线圈型全光纤偏振器的研究

本文采用等效电流法对线圈型全光纤偏振器进行了分析计算.对应于保偏光纤中两正交传输基模的消光比,提出了一种分析保偏光纤弯曲损耗的新方法,这种方法基于将保偏光纤两个不同偏振模式分别等效为两个普通圆光纤的基模,等效参数通过测量不同偏振模式的模场半径来确定.实验证明这种理论计算方法与实验结果一致.最终,我们研制出的线圈型光纤偏振器在1.31μm工作波长下,实测消光比达30dB以上,工作偏振模式插入损耗≤3dB.     

半导体激光泵浦预激光锁模调Q固体激光器研究

报道半导体激光侧面泵浦预激光锁模调Ｑ的Ｎｄ：ＹＡＧ固体板条激光器，预激光锁模调Ｑ的激光脉冲宽度为３６ｐｓ，调Ｑ包纤各心的锁模单脉冲能量超过７μＪ，相应的峰值功率达２００ｋＷ。     

分布耦合系数对线性啁啾光栅色散的影响

本文从光栅反向耦合波方程出发,经相位共轭变换用Runge-Kuta-Gil方法对其数值求解。针对线性啁啾光栅耦合系数变化服从不同的分布,分析了各种分布对光栅反射谱特性和色散特性的影响。