一种新的基于频域有限差分方法的小周期有机太阳能电池的光电特性

由MoO₃/Ag/MoO₃ （MAM）组成的多层膜结构非常有希望替代ITO作为有机太阳能电池中的透明阳极.然而,基于MAM结构的有机太阳能电池光吸收能力较弱.为此,引入了一种小周期短节距金属光栅,利用表面等离子激元增强活性层的光吸收.借助于频域有限差分方法求解麦克斯韦方程和半导体方程,探讨了有机太阳能电池结构的光学和电学性质.分析结果表明：与平面结构相比,活性层中的光吸收大大提高;同时,当凹槽宽度为4 nm,能量转换效率提高了49%.相关结果有助于更好地开发和利用无ITO层的有机太阳能电池.     

Formation and magnetic properties of Co–Fe-based bulk metallic glasses with supercooled liquid region

A new Co–Fe-based ferromagnetic bulk metallic glass (BMG) was synthesized by copper mould casting method. The thermal stability and crystallization processes were investigated by differential scanning calorimetry (DSC) and X-ray diffraction (XRD). The soft magnetic behavior was studied by DC magnetic measurements. The high glass formation ability was interpreted in terms of the effective suppression of nucleation and growth of the intermetallic compounds which appear in the multicomponent system during solidification. The high thermal stability indicates that the new Co–Fe-based BMG could be used as high-temperature magnetic material. The low coercivity which was as low as 8 A/m for the as-cast sample was found in the Co–Fe-based metallic glass cylinder with a diameter of 1.5 mm.     

Magnetic,structural and electrical properties of ordered and disordered Co50Fe50 films

Co₅₀Fe₅₀ films with thickness varying from 100 to 500 Å were deposited on a glass substrate by sputtering process, respectively. Two kinds of CoFe films were studied: one was the as-deposited film, and the other the annealed film. The annealing procedure was to keep the films at 400 °C for 5 h in a vacuum of 5×10⁻⁶ mbar. From the X-ray study, we find that the as-deposited film prefers the CoFe(1 1 0) orientation. Moreover, the body-centered cubic (bcc) CoFe(1 1 0) line is split into two peaks: one corresponding to the ordered body-centered tetragonal (bct) phase, and the other, the disordered bcc phase. After annealing, the peak intensity of the ordered bct phase becomes much stronger, while that of the disordered bcc phase disappears. The annealing has also caused the ordered CoFe(2 0 0) line to appear. When the amount of the ordered bct phase in Co₅₀Fe₅₀ is increased, the saturation magnetization (M_s) and coercivity (H_c) become larger, but the electrical resistivity (ρ) decreases. From the temperature coefficient of resistance (TCR) measurement, we learn that the bct grains in the CoFe film start to grow at temperature 82 °C.     

First-principles study on the origin of optical transitions to be associated with F colour centers for PbWO4 crystals

The electronic structures of PbWO₄ crystals containing F type color centers with the lattice structure optimized are studied within the framework of the fully relativistic self-consistent Direc–Slater theory, using a numerically discrete variational (DV-Xα) method. The calculated results show that F and F⁺ centers have donor energy level in forbidden band. Their optical transition energy are 1.84 eV, 2.21 eV, respectively, which corresponds to the 680 nm, 550 nm absorption bands. It predicts that the 680 nm, 550 nm absorption bands originate form the F and F⁺ centers in PbWO₄ crystals.     

Separated AlxIn1−xN quantum dots grown by plasma-reactive co-sputtering

Separated Al_xIn_1−xN quantum dots (QDs) embedded in amorphous AlN films have been produced by radio-frequency co-sputtering technique on silicon (1 1 1) and quartz glass substrates. The mean size and density of Al_xIn_1−xN QDs can be conveniently monitored by deposition parameters. Transparent electron microscope, and X-ray diffraction were used to detect the structure of the Al_xIn_1−xN QDs system; field-emission scanning-electron microscope was adopted to measure the surface morphology and anticipate the size of the QDs; X-ray photoelectronic spectroscopy was used to measure the stoichiometric ratios of the QDs.     

Host dependent frequency upconversion of Er-doped oxyfluoride germanate glasses

Er³⁺-doped oxyfluoride germanate glasses have been synthesized by the conventional melting and quenching method. The Judd-Ofelt intensity parameters were calculated based on the Judd-Ofelt theory and absorption spectra measurements. With the substitution of PbF₂ for PbO, the Ω₂ parameter decreases, while the Ω₆ parameter increases. These change trends indicate that fluoride anions come to coordinate erbium cations and the covalency of the Er-O bond decreases. Structural and thermal stability properties were obtained by Raman spectra and differential thermal analysis, indicating that PbF₂ plays an important role in the formation of glass network and has an important influence on the maximum phonon energy and thermal stability of host glasses. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2, and ⁴F_9/2→⁴I_15/2, respectively, were simultaneously observed at room temperature. With increasing PbF₂ content, the intensity of red (657 nm) emissions increases significantly, while that of the green (525 and 546 nm) emission increases slightly. The results indicate that PbF₂ has more influence on the red (657 nm) emission than the green (525 and 546 nm) emissions in oxyfluoride germanate glasses. The possible upconversion luminescence mechanisms have also been estimated and discussed.     

Optical properties of methane to 288 GPa at 300 K

Optical properties of solid methane (CH₄) were studied at high pressure and room temperature using a diamond anvil cell. Reflectivity and transmission measurements were used to measure the refractive index to 288 GPa. Fabry-Perot interferometery was used to measure the sample thickness to 172 GPa. This data was fitted to the derived expression of thickness vs. pressure that was then used to calculate the thickness to 288 GPa. This in turn was combined with optical absorption experiments to obtain the absorption coefficient and hence the extinction coefficient k^*. From combined reflection and absorption experiments the refractive index n=n_s+ik^* was obtained. The index of refraction and the ratio of molar refraction to molar volume showed a large increase between 208 and 288 GPa. This behavior indicated that a phase transformation of insulator-semiconductor might have occurred in solid CH₄ by 288 GPa.     

松花江冰下声学试验技术研究

北极区域极具战略意义与商业价值,随着各国的广泛关注,针对北极地区开展的科考科研活动逐渐增多。其中北极海域的相关研究尤为重要,特别是北极水声学,是保障北极军事存在以及正常科考科研活动的重要支撑。课题组于2015年1月在哈尔滨松花江进行了冰下声学试验,主要内容包括冰下信道测试、冰层散射系数测量以及冰下水声通信试验,实现了冰下半波导现象的初步观测、冰层前向散射系数的测量、基于能量检测器的低信噪比扩频通信、基于时反镜判决反馈均衡技术的高速水声通信以及冰下12用户多址水声通信等内容。本文对本次冰下声学试验情况进行介绍,并给出了相应的试验结果及经验总结。     

基于动态光散射研究pH值对茄红素胶囊粒径的影响

用微乳化技术结合复合团聚法制备了纳米及亚微米茄红素胶囊,基于动态光散射测量分析了环境p H值对胶囊的粒径大小及其分布的影响.结果表明,对纳米茄红素胶囊,当p H值为3.5、6.0及6.8时能稳定的分散,而p H值为7.4时则会出现明显的聚集现象;对亚微米茄红素胶囊,当p H值为3.5、6.0、6.8及7.4时其粒径分布均为双峰状态,其中粒径较大的为亚微米茄红素胶囊,粒径较小的为包覆不良的颗粒,且p H=7.4时的粒径明显小于其它三种p H值时的粒径.虽然亚微米胶囊在p H=7.4时粒径明显变小的结果与纳米胶囊相同,但亚微米胶囊并不像纳米胶囊那样出现聚集现象.     

Grain size effects on microstructural stability and creep behaviour of nanotwinned Ni free-standing foils at room temperature

Creep tests were performed on the high stacking fault energy (SFE) nanotwinned (NT) Ni free-standing foils with nearly the same twin thickness at room temperature (RT) to investigate the effects of grain size and loading rate on their microstructural stability and creep behaviour. The grain growth mediated by the twinning/detwinning mechanism at low applied stresses (<800 MPa) and grain refinement via the detwinning mechanism at high applied stresses (>800 MPa) were uncovered in the present NT-Ni foils during RT creep, both of which are attributed to the interactions between dislocations and boundaries. It appears that a higher initial dislocation density leads to a faster primary creep strain rate and a slower steady-state creep strain rate. Unlike the non-twinned metals in which grain growth often enhances the creep strain rate, the twinning/detwinning-mediated grain growth process unexpectedly lowers the steady-state creep strain rate, whereas the detwinning-mediated grain refinement process accelerates the creep strain rate in the studied NT-Ni foils. A modified phase-mixture model combined with Arrhenius laws is put forward to predict the scaling behaviour between the creep strain rate and the applied stress, which also predicts the transition from grain growth-reduced to grain refinement-enhanced steady-state creep strain rate at a critical applied stress. Our findings not only provide deeper insights into the grain size effect on the mechanical behaviour of nanostructured metals with high SFE, but also benefit the microstructure sensitive design of NT metallic materials.