通孔阳极氧化铝膜的制备及其性能的研究

在15% H₂SO₄阳极氧化液中添加硝酸镨制备阳极氧化铝(AAO)膜以提高AAO膜的性能,采用化学腐蚀和微波处理相结合的方法,去除AAO膜的阻挡层,制备通孔的AAO膜。分别研究镨的添加量、氧化电压对AAO膜的厚度和硬度的影响及腐蚀时间、微波处理时间分别对AAO膜的阻挡层的影响,分别用能谱和扫描电镜等对AAO膜进行了表征。在15% H₂SO₄阳极氧化液中添加硝酸镨,制备出的AAO膜具有更大的厚度和硬度,当氧化电压为23 V时,在15% H₂SO₄+0.14 Pr g·L-1混合液中制备的AAO膜的厚度和硬度分别为162 μm和275.1 HV,与在阳极氧化液为15% H₂SO₄溶液中制备的AAO膜的厚度和硬度(150 μm和224.8 HV)相比,分别提高8.0%和22.4%。当氧化电压在19～23 V范围时,AAO膜的厚度随着氧化电压的增大而增加;AAO膜的硬度随着氧化电压的增大而减小。将AAO膜在35 ℃和5% H₃PO₄溶液中腐蚀13 min,再用超声波处理10 min,可得到通孔的AAO膜。腐蚀后AAO膜表面絮状物为Al₂O₃。     

热处理温度对铜镍镀层的光谱性能的影响

采用电沉积法在镍表面制备铜镍镀层,并将该铜镍镀层在不同温度下进行热处理。分别用扫描电镜法(SEM)、能谱法(EDAX) 和X衍射法(XRD)等对热处理后的铜镍镀层进行表征,研究热处理温度对铜镍镀层的光谱性能的影响。用电镀的方法获得的铜镍镀层表面是由节瘤组成,热处理温度在25~600 ℃范围,随着热处理温度的升高,铜镍镀层表面的节瘤变小;热处理温度在600~900 ℃范围,随着热处理温度的升高,铜镍镀层表面的节瘤变小,铜镍镀层表面的节瘤间的分界线越不明显。热处理温度在25～900 ℃范围,随着热处理温度的升高,铜镍镀层中铜的含量减小,从82.52 at%减小到78.30 at%;镍的含量增加,从17.48 at%增加到21.70 at%。铜镍镀层为Cu_0.81Ni_0.19立方晶型结构,热处理温度在25～300 ℃范围,随着热处理温度的升高,Cu_0.81Ni_0.19的晶型结构更完整;热处理温度在600～900 ℃范围,铜镍镀层中可能有部分的Cu_0.81Ni_0.19立方晶型结构转变为Cu_3.8Ni立方晶型结构;随着热处理温度的升高,有利于Cu_3.8Ni(311)和Cu_0.81N_i0.19(311) 晶面的生长。     

亲水性氧化锌纳米粒子控制合成及光学性质研究

采用溶剂热分解法,以乙酰丙酮锌为原料,在亲水性有机溶剂聚乙二醇(PEG-600)、聚乙二醇单甲醚(MPEG-1000)、三甘醇(TEG)中合成了氧化锌纳米粒子.X-射线衍射(XRD)分析表明氧化锌纳米粒子为纤锌矿晶体结构.透射电镜(TEM)形貌观察结果表明,在不同溶剂PEG-600、MPEG-1000和TEG中合成的氧化锌纳米粒子其形状分别为短棒状、颗粒状以及由小晶粒团聚而成的球状粒子.合成的氧化锌纳米粒子表面修饰有亲水性有机分子,可以稳定分散于水溶液中.紫外-可见光吸收光谱和光致发光光谱研究显示,合成的氧化锌纳米粒子具有很强的紫外带隙吸收和发光性能,表明制备的氧化锌纳米粒子结晶性好,光学性能优异.     

聚乙烯醇/羧甲基壳聚糖共混水凝胶的辐射合成及性能

采用电子加速器辐照法制备了聚乙烯醇(PVA)/羧甲基壳聚糖(CMCH)共混水凝胶;研究了PVA与CMCH的配比、辐照剂量、温度以及pH值对PVA/CMCH共混水凝胶性能的影响.实验发现,PVA与CMCH在辐照剂量为40 kGy、配比为w(PVA)/w(CMCH)=5/1的条件下可得到强度较好的PVA/CMCH共混水凝胶,该水凝胶具有一定的温度和pH敏感性:在5~20℃时具有较高的溶胀率,温度在20℃以上溶胀率较低;水凝胶在pH<4.0和pH>6.0时溶胀率均较大,而当pH为4.0~6.0时溶胀率较小.     

等离子体聚四氟乙烯的ESR研究

目前,对等离子体聚合机理,即自由基和离子聚合机理仍在争论之中^[1-6],ESR的研究对探讨等离子体聚四氟乙烯(PPTFE)聚合机理将是有价值的。     

Microphase Separation of Star-diblock Copolymer Films: a Dissipative Particle Dynamics Simulation

The microphase-separating behaviors of two types of star-diblock copolymers (A_x)₄(B_y)₄ and (A_xB_y)₄ in thin films are studied using the simulation technique of dissipative particle dynamics. A variety of ordered mesostructures have been observed and the simulated phase diagrams show obvious symmetries for the (A_x)₄(B_y)₄ films and asymmetries for the (A_xB_y)₄ films, besides, it is easier for the (A_x)₄(B_y)₄ than for the (A_xB_y)₄ to carry out microphase separation under the same conditions, which has been recognized in bulk and can be ascribed to the structural difference between the two types of star copolymers. There are some correspondences between the mesostructures formed in the film and those formed in bulk at the same composition fraction. Decreasing the thickness of film and strengthening the A-B repulsion both help the mesostructures enhance the degree of order. Composition fraction dependences of the mean-square radius of gyration in the two types of star copolymer films are almost contrary, which can be attributed to the differences in their respective structures.These findings can provide a guide to designing novel microstructures involving star-diblock copolymers via geometrical confinement.     

BTF变色对其热安定性和与PVB等相容性的影响

通过光照制备了一定量的变色苯并三呋咱氧化物（BTF）,再分别采用差热（DTA）,差示扫描量热（DSC）,真空安定性试验（VST）等热分析方法,对变色前后的BTF进行了热安定性研究及与聚乙烯醇缩丁醛（PVB）等接触材料的相容性研究,并通过热重－红外等仪器分析手段,初步探讨了BTF与PVB之间的作用机理。     

聚丙烯酰胺/聚异丙基丙烯酰胺互穿网络水凝胶的制备与性能

采用分步法用电子加速器辐射合成了聚丙烯酰胺(PAAm)/聚异丙基丙烯酰胺(PNIPAAm)互穿网络水凝胶,并考察了温度、pH值、离子强度对其溶胀性能的影响.研究表明:互穿水凝胶具有温度敏感性,且其体积相变与互穿网络中PAAm和PNIPAAm含量有关,随着网络中PAAm含量的增加水凝胶的体积相变趋于平缓,可以通过改变PAAm和PNIPAAm的组成比来控制水凝胶的体积相变行为.此外,互穿水凝胶还具有pH敏感性和一定的抗盐性.     

多孔CeO_2膜的制备及其光谱性能（英文）

以铈箔为原料,采用阳极氧化法和热处理法制备多孔的CeO_2膜。将阳极氧化铈膜分别在400,500和800℃下进行热处理,分别研究阳极氧化铈膜的晶体结构、组成和表面形貌,分别研究多孔的CeO_2膜红外光谱特征吸收和热膨胀性能。阳极氧化铈膜是Ce(OH)_3,CeF_3,Ce_2O_3,CeO_2和Ce的混合膜,并吸附水和乙二醇,其中Ce(OH)_3,CeF_3,Ce_2O_3分别为六方晶型结构,CeO_2和Ce分别为立方晶型结构。阳极氧化铈膜中的Ce(OH)_3,Ce_2O_3和Ce分别在400和500℃进行热处理时可能分别转变为CeO_2,分别在400和500℃热处理后的膜为CeF_3和CeO_2的混合膜。阳极氧化铈膜中的Ce(OH)_3,CeF_3,Ce_2O_3和Ce在800℃进行热处理时可能分别转变为CeO_2,在800℃热处理后的膜为CeO_2膜。该CeO_2膜是多孔的膜,且孔为直孔,在1 600~4 000cm~(-1)范围内具有强吸收。该CeO_2膜在170~900℃范围内热膨胀系数变化不大,该膜的热稳定性较好。     

钛合金TC4材料热处理工艺对圆筒在内爆炸载荷下膨胀半径的影响

对采用两种不同热处理工艺的钛合金TC4材料进行了Hopkinson拉伸实验、圆筒爆炸实验和数值仿真,从而确定了两种不同热处理工艺的优劣并通过微观分析揭示了钛合金TC4材料微观组织结构对内爆炸载荷下圆筒膨胀半径的影响。实验和数值分析表明:采用双重退火热处理工艺的钛合金TC4材料具有良好的动态力学性能。在相同的加载条件下,经此工艺处理的TC4圆筒在爆轰产物未泄漏之前有着充分的膨胀半径,而且也不容易形成绝热剪切破坏。同时,给出的依据高速摄影照片确定筒壳断裂点的方法是切实可行的,获得的断裂时间与数值分析结果吻合。