采用差示扫描量热/热分析-质谱(DSC/TG-MS)联用技术研究了草酸钴对高氯酸铵的原位催化. 结果表明,草酸钴原位分解生成的钴氧化物对高氯酸铵有较强的催化作用,添加2%的草酸钴使高氯酸铵的分解温度降低104 ℃, 分解放热量从655 J/g增大到 1 469 J/g. 分解的气相产物主要有H2O, NH3,O2,HCl,Cl2,NO,N2O和NO2. 由于氧在新生态的纳米钴氧化物表面形成过氧化活性离子(O-2), 使氨氧化在钴氧化物的过氧化表面活性中心进行,加速了高氯酸铵的热分解,使其表观放热量大幅度增加.     

氨基酸配位聚合物[Co(L-trp)(D-trp)]n

The coordination polymer [Co(L-trp)(D-trp)]_n (where L-trp is L-tryptophan or (S)-2-Amino-3-(3-indolyl)propionic acid and D-trp is D-tryptophan or (R)-2-Amino-3-(3-indolyl)propionic acid) was prepared by hydro-thermal method. The structure and physicochemical properties were characterized by single-crystal X-ray diffraction structure determination, infrared spectroscopy, elemental analysis and cyclic vohammogram. The crystal data for the title compound: Monoclinic, P2₁/c, β=98.024(2)°, a=1.959 5(3) nm, b=0.546 45(7) nm, c=0.905 54(17) nm, Z=2, μ=0.934 mm^-1, R₁=0.063 2, wR₂=0.155 3. The crystal structure shows a two-dimensional double chain plane structure feature. The cyrstallized coordination polymer has a centrosymmetric space group. Each Co²⁺ is coordinated with a pair of racemes, and the complex is a mesomer. CCDC: 651088.     

草酸铜原位催化高氯酸铵热分解的研究

通过TG-DTA-MS联用技术研究了草酸铜对高氯酸铵的催化过程。研究发现,草酸铜分解生成的氧化铜对高氯酸铵有较强的催化作用,添加2%的草酸铜使高氯酸铵的高温分解温度提前112℃。分解的气相产物主要有H2O,NH3,O2,HCl,Cl2,HNO,NO,N2O和NO2。在草酸铜原位分解生成的CuO表面吸附生成氧的过氧化离子(O2-)和氧离子(O-,O2-)是加速AP热分解反应的主要原因。     

SiO2/Co3O4核壳催化剂对AP热分解的催化性能研究

采用改良的Stöber法制备粒径约为200 nm的单分散球形SiO₂颗粒,以此为内核,分别通过液相沉淀法和尿素均匀沉淀法制备包覆形式不同的新型SiO₂/Co₃O₄核壳式纳米催化剂。采用X-射线衍射分析(XRD)、透射电子显微镜(TEM)、红外光谱分析(IR)、拉曼光谱分析(Raman)、BET比表面积测试等手段对产物进行表征,利用差式扫描量热仪(DSC)考察SiO₂/Co₃O₄复合物对高氯酸铵(AP)热分解反应的催化作用,探讨不同包覆形式对其催化活性的影响。结果表明,两种方法制备得到的SiO₂/Co₃O₄复合物分别为层包覆和粒子包覆,比表面积大,具有明显的核壳结构,且粒子包覆形式的SiO₂/Co₃O₄对AP热分解反应的催化效果最好,使AP的高温分解温度降低了110 ℃,放热量增加了662 J·g^-1。     

紫外-可见漫反射光谱研究Pt-Sn/Al_2O_3体系催化剂的制备过程

以紫外-可见漫反射光谱为主要手段研究了Pt-Sn/Al_2O_3体系催化剂的浸渍、热处理过程。探讨了制备过程中铂的价态和配位环境的变化以及载体所起的作用。     

一维链状锰配位聚合物[Mn(1,5-nds)(Him)_4]_n的合成、晶体结构及热稳定性研究(英文)

The synthesis,structural characterization and thermal behavior of a novel one-dimensional manganese (Ⅱ) complex of formula [Mn(1,5-nds)(Him)4]n [1,5-nds=naphthalene-1,5-disulfonate,Him=imidazole] is reported.The complex crystallizes in the triclinic system,space group P1,with a=0.835 42(13) nm,b=0.983 45(18) nm,c= 0.987 42(19) nm,α=60.523 0(10)°,β=97.748(2)°,γ=87.189(2)° and Z=2.The 1,5-nds ligand assumes the μ2 coordination mode and interlinks Mn(Ⅱ) ions into infinite one-dimensional chain structure along [111] direction,with the adjacent Mn…Mn distance being 1.144 99(12) nm.The chains are assembled into a three-dimensional supramolecular architecture via hydrogen bonds and C-H…π interactions.IR spectra and thermal analysis data are in agreement with the crystal structure.     

巯基修饰单链DNA在纳米金薄膜电极上自组装、杂交和取向的电化学交流阻抗谱

利用电化学交流阻抗技术对SH-ssDNA在纳米金薄膜电极表面的自组装、杂交和取向进行了系统表征。 探讨了SH-ssDNA的组装时间、浓度和链长对其自组装的影响,自组装15 h时电荷传递电阻Rct最大,表面覆盖率最高;研究了SH-ssDNA的浓度、链长以及与互补DNA的杂交方式对杂交反应的影响。 结果发现,随着单链浓度的增加,杂交后R_ct的变化值逐渐降低,当SH-ssDNA为5 μmol/L时Rct值比杂交前增加了16%。 通过对阻抗谱数据模拟和分析,表明SH-ssDNA以垂直竖立取向在金电极表面形成均匀致密单分子层,杂交效率与SH-ssDNA的覆盖率密切相关。     

红辉沸石合成A型分子筛的红外光谱研究

以天然红辉沸石合成了A型分子筛，通过XRD、IR光谱研究了其晶化过程。发现在1000-950cm^-1、750一600cm^-1、560cm^-1、460cm^-1处的红外吸收峰随结晶度有规律的变化，初步探讨其反应机理。     

含水玻璃夹层状硅酸盐的合成与XRD表征

120℃时膨润土、高岭土分别用水玻璃固化，固化物晶形仍以蒙脱石、高岭石结构为主，且蒙脱石可包含更多的水玻璃成分，其固化机理为水玻璃加强了这些硅酸盐的层间作用力，讨论了新型夹层物质形成的可能。     

盐酸氯丙嗪1H NMR、 13C NMR谱的归属及结构表征

通过运用¹H-¹H COSY(¹H-¹H COrrelation SpectroscopY)、TOCSY(TOtal Correlation SpectroscopY)、HSQC(Heteronuclear Single Quantum Correlation)、HMBC (Heteronuclear Multiple Bond Correlation)、NOESY(Nuclear Overhauser Enhancement SpectroscopY)等多种二维核磁技术,对盐酸氯丙嗪（Chlorpromazine hydrochloride CPZ· HCl）在CDCl₃、CD₃COCD₃和D₂O三种溶剂中的¹H、¹³C NMR谱进行了准确归属（重点集中于谱峰重叠程度较高的芳香族区域）．实验表明：杂环上N与苯环存在部分共轭;在CDCl₃、CD₃COCD₃中,侧链卷曲至芳环上方处于屏蔽区,且侧链上N为较稳定的四面体构型;比较了CPZ· HCl在不同溶剂与浓度下的¹H NMR谱的变化,对文献中其核磁共振谱（特别是芳香区的谱峰）归属的争议作了解释．量子化学计算结果与实验结果相吻合．