CRITICAL CURRENT DENSITY AND FLUX PINNING CHARACTERISTICS IN MELT-TEXTURED Y0.6Er0.4Ba2Cu3Oy SUPERCONDUCTOR

We prepared highly textured YBa₂CuO_y and Y_0.6Er_0.4Ba₂Cu₃O_y bulk samples by a powder melting process method under the same conditions and studied the magnetic properties and flux pinning character istics. It is found that the J_c estimated by the Bean's model decreases with the magnetic field according to a power law J_c∝B^-n (n<0.55), suggesting that J_c values of these materials are controlled by the flux pinning rather than weak links. Also, J_c and flux pinning are improved by the Er addition. The reduction of the size of Y₂BaCuO₅ particles, magnetic pinning and stress-field pinning caused by the Er addition may be responsible for the enhancement of J_c and flux pinning.     

On Hardy-type integral inequalities

The Hardy integral inequality is one of the most important inequalities in analysis. The present paper establishes some new Copson-Pachpatte(C-P) type inequalities, which are the generalizations of the Hardy integral inequalities on binary functions.     

亚像元成像系统细胞神经网络插值方法研究

亚像元动态成像技术是实现卫星相机小型化及提高相机空间分辨率的有效方法。采用细胞神经网络(CNN)实现了对亚像元图像的实时插值,对插值的过程进行了详细的分析,并与基于亚像元图像的传统插值方法进行了对比。结果表明,亚像元成像系统细胞神经网络插值方法不仅可以节约系统资源,而且还可以提高系统的运行速度。通过仿真证明了该方法的正确性。     

快脉冲超导磁体用NbTi超导线材的制备研究北大核心CSCD

本研究以Cu10Ni合金作为基体材料,采用组装法制备了铜比1.8,Φ0.7 mm的快脉冲超导磁体用NbTi超导线材.研究了Cu10Ni合金、时效次数和最终应变、去应力退火对快脉冲超导磁体用NbTi/Cu超导线微观组织和临界电流密度的影响.实验结果表明:采用Cu10Ni合金作为基体,时效3次且最终应变在3.5-5.0之间时,线材最终应变增大,临界电流密度呈先增大而后降低,最终趋于稳定的变化规律;最终应变为4.37时,随着热处理次数的增加,临界电流密度呈先增大而后降低的趋势,断线次数也随之明显增多.损耗的测试结果表明:采用Cu10Ni合金为基体制备的超导线材的损耗要明显小于无氧铜基体的超导线材.经过3次时效热处理且最终应变为4.37时,Cu10Ni合金为基体制备的超导线材其临界电流密度最高为2308A/mm^2(4.2K,5T,判据0.1μV/cm),损耗为40.8mJ/cm^3,(±3T,4.2K).     

HCSB DEMO 中子通量谱分析及活化片法测量系统概念设计研究

利用蒙特卡罗粒子输运程序(MCNP)对氦冷固态增殖剂包层聚变示范堆(HCSB DEMO)做了中子通量谱分析。根据中子通量谱特点选出活化片材料,根据跑兔系统和活化片法测中子通量的原理设计出适用于测量HCSB DEMO 增殖包层中子的活化片法测量系统,并对其各组成部分及功能做了说明。计算了活化片在测量系统辐照端辐照时的活化反应率、活化片特征γ 射线发射率及特征γ 计数率,并得到一套合理的测量方案,用于HCSB DEMO 包层中子的测量。     

热处理温度对碳掺杂MgB_2/Nb/Cu超导线材性能的影响

采用Nb/Cu复合管作为外包套材料,通过原位法粉末装管工艺(PIT)制备了C掺杂MgB2/Nb/Cu线材.在高纯流动氩气保护条件下、650～950℃温度区间内烧结2h.微观结构分析显示,通过该工艺制备的MgB2/NbZr/Cu线材具有良好的晶粒连结性和较高的致密度.X射线衍射(XRD)分析表明在750℃左右可以生成纯度较高的MgB2相,在低温和高温下烧结后均有杂相峰出现,并且高温烧结后所生成的相结构较为复杂.采用四引线法超导临界电流的测试结果表明,低温烧结后的线材具有超导电流传输性能,而当热处理温度超过750℃时,样品中的电流传输状态表现为正常电阻态.实验结果证实采用Nb作为原位法MgB2超导线材的包套阻隔层时,成相热处理一般应该在低于750℃的温度下进行.     

实用化MgB2超导材料研究进展

本文综述了实用化MgB2超导材料的最新研究进展.最新的理论和实验结果表明通过元素替代和掺杂,有希望进一步提高MgB2超导线带材的临界电流密度和磁通钉扎特性,完全可以达到实用化要求.目前MgB2超导磁体的制备技术研究已经开始,极有可能开发出采用闭路循环制冷机制冷的核磁共振成像仪(MRI)取代现在医学上使用的基于低温超导的核磁共振成像系统.     

2T高温超导Bi-2223带材磁体

通过带材Ic及其弯曲性能测试,进行磁体设计,采用先处理后绕制(R&W)的工艺,制得中心磁场达2T的高温超导Bi-2223带材饼状线圈磁体.该磁体在液氮(77K)下通电流22.4A,中心磁场达0.25T;在液氦下可通电流170A,中心磁场达2.0T(4.2K),为液氮下的8倍,表明所采用的工艺,对制作中小规模高温超导Bi-2223带材饼状线圈磁体,是合适的.     

热处理和添加元素对MgB2晶畴尺寸和微观应变的影响

用X射线衍射仪和扫描电镜研究了热处理温度和添加元素(Ti, Zr)对单相MgB2粉末样品的晶畴尺寸和微观应变的影响.结果表明,无论是没添加的还是添加了合金元素的MgB2样品,随热处理温度的升高晶畴尺寸明显增大.在同样处理制度下,添加元素样品的晶畴尺寸明显小于不添加的样品.随热处理温度的升高,微观应变有降低的趋势.晶畴尺寸的测试结果与扫描电镜的观测结果表现出很好的一致性.实验说明,添加元素(Ti, Zr)MgB2样品临界电流密度的提高,与晶格畸变增加,晶畴尺寸变小,晶界增多,导致钉扎力增加有关.