Heteroatom-doped peri-acenes (PAs) have recently attracted considerable attention considering their fascinating physical properties and chemical stability. However, the precise sole addition of boron atoms along the zigzag edges of PAs remains challenging, primarily due to the limited synthetic approach. Herein, we present a novel one-pot modular synthetic strategy toward unprecedented boron-doped PAs (B-PAs), including B-[4,2]PA ( 1 a-2 ), B-[4,3]PA ( 1 b-2 ) and B-[7,2]PA ( 1 c-3 ) derivatives, through efficient intramolecular electrophilic borylation. Their chemical structures are unequivocally confirmed with a combination of mass spectrometry, NMR, and single-crystal X-ray diffraction analysis. Notably, 1 b-2 exhibits an almost planar geometry, whereas 1 a-2 displays a distinctive bowl-like distortion. Furthermore, the optoelectronic properties of this series of B-PAs are thoroughly investigated by UV/Vis absorption and fluorescence spectroscopy combined with DFT calculation. Compared with their parent all-carbon analogs, the obtained B-PAs exhibit high stability, wide energy gaps, and high photoluminescence quantum yields of up to 84 %. This study reveals the exceptional ability of boron doping to finely tune the physicochemical properties of PAs, showcasing their potential applications in optoelectronics.     

Flame surface modification of polyethylene sheets

High density polyethylene sheets 2 mm thick were flame treated to modify the surface properties. Sheets treated using a flame with air to gas (methane) ratio ∼ 10:1 at different distances between the inner cone tip of the flame and the polymer surface were investigated. Grafting of selected monomers as maleic anhydride, acrylamide and glycidyl methacrylate was attempted by flame treatment of sheets covered with a monomer layer. Good grafting results were obtained with acrylamide and maleic anhydride. The surface temperature-time dependence during the flame treatment was measured with a high resolution thermocouple. Scanning Electron Microscopy (SEM) allowed evidencing a modified thickness of about 120 μ. The chemical surface modification was studied by X ray Photoelectron Spectroscopy (XPS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFT). The hydroxyl, carbonyl and carboxyl content was measured after derivatization with reagents containing an elemental tag to facilitate XPS analysis of surface functional groups. In comparison to the untreated polyethylene, wetting tension and contact angle of the flamed materials showed a strong variation. This variation was almost independent of the distance between the flame and the polymer surface. Adhesion between treated polyethylene and a polyurethane adhesive was determined using T-peel test measurements. High adhesion levels were found with flame treated polyethylene at 5 mm distance. XPS results indicate that when adhesion is high, the hydroxyl is in excess compared to the other measured functions, i.e. carbonyl and carboxyl species.