Cems characterization of SnO2 films obtained by sputtering and sol-gel route

Conversion electron Mössbauer spectroscopy (CEMS) has been used to study tin oxide films prepared by sol-gel dipping and sputtering. The spectra of films prepared by sol-gel route result close to that of crystalline SnO₂ after heat treatment at a temperature as low as 150°C. The Mössbauer parameters of as sputter deposited films indicate that the structure of the deposited stannic oxide has an amorphous character more pronounced for thinner samples. The structure becomes predominantly that of crystalline SnO₂ by heating at 550°C for 30 min provided the film thickness is higher than 10 nm.     

Non-local approximation of the Mumford-Shah functional

The Mumford-Shah functional, introduced to study image segmentation problems, is approximated in the sense of -convergence by a sequence of non-local integral functionals. Received June 6, 1996 / Accepted July 11, 1996     

Production and characterization of refractive index gratings in high-birefringence fibre optics

In this work, we report production and modelling of both Bragg gratings and rocking filters in high birefringence fibre optics. Bragg gratings are produced by UV (257.0 nm) external interferometric exposition of a frequency-doubled Ar⁺ ion laser, whereas for rocking filters formation the visible Ar⁺ ion laser lines in 488.0 and 514.5 nm are used in an internal method. The spectral characteristics due to the birefringence properties are studied through numerical methods and experimental techniques. The spectral responsivity of the structures under temperature changes and stress application is presented.     

DRIFTS study of surface reactivity to NO2 by zinc nanoparticle aggregates and zinc hollow nanofibers

Zinc nanostructures synthesized with different morphologies from the same evaporation/condensation technique are studied with concern to surface reactivity to NO₂ by Diffuse Reflectance Infrared Fourier Transformed Spectroscopy (DRIFTS). Synthesis of nanopowders is obtained, according to previous work, by gas flow thermal evaporation at 540 °C of bulk Zn grains. Two types of Zn powders are obtained and studied in experiments. The first one is collected on the cold walls of the reactor as a deposit produced by thermophoretic effect. It is constituted by grains (∼10 μm) originated by the stratification of smaller aggregates (∼200 nm) and isolated primary particles (∼50 nm) born in the gas flow. The second type of powder is grown from the condensation of Zn chemical vapors within the expansion orifice of the quartz reactor after relatively long time (∼1 h) deposition process. It is constituted mainly by hollow Zn nanofibers with external and internal diameter about 100 and 60 nm. Preliminary characterization of the two types of powders is made by SEM, TEM, XRD. Thereafter, the two types of samples are studied by DRIFTS at variable temperature (VT). Comparison is made between the home-synthesized nanopowders with respect to commercial Zn standard dust. The Zn hollow nanofibers when exposed to NO₂ are found to exhibit dramatic reactivity, which is not observed at all either in the case of clustered aggregate zinc or of commercial Zn dust powders. Results indicate that, at increasing temperature from RT to 300 °C, the hollow nanofibers surface reacts distinctively with adsorbant gas NO₂, with contemporary formation of a progressively growing narrow absorption band at 2500 cm⁻¹ and contemporary depression of a doublet (∼1600-1628 cm⁻¹) band. In order to justify this striking spectral feature, we propose the occurring of a possible polymerization process at nanofibers surface where most probably as a consequence of pre-treatment and exposure to gas NO₂ a very thin film of ZnO is formed. The possible role of huge specific surface of hollow nanofibers as inferred by preliminary SEM, TEM, XRD studies is discussed.     

Modification of surface properties of electrospun polyamide nanofibers by means of a perfluorinated acridine

Polyamide 6 (PA6) nanofibers were prepared from formic acid solutions by using electrospinning technique. The fibers were smooth, defects free and with diameters smaller than 200 nm. Small amounts of a perfluorinated acridine were added as dopant to the feed solution to modify the wettability of the fibers. The effect of doping on the contact angle values is well apparent. The contact angle values go from 50° of pure PA6 to 120° when 6% of acridine is added. A comparison between fibers and films of pure and doped polyamide 6 was carried out in order to determine the effect of morphology on wettability. Thermal annealing near the T_g of the polymer promoted the segregation of the molecules to the surface, reaching contact angles of 131° with smaller amounts (4%) of acridine. The surface segregation was also promoted by time aging.