碳纳米管阵列、捆束的三步升温工艺制备及其形貌与结构

使用结构简单的单温炉设备，通过三步升温热解二茂铁、三聚氰氨混合物方法，在二氧化硅、多晶陶瓷基底上分别合成了碳纳米管阵列、碳纳米管捆束.使用扫描电子显微镜、透射电子显微镜、电子能量损失谱和x射线光电子能谱对合成样品进行了结构和成分分析.结果显示：两种基底上合成的纳米管均为多壁纯碳管；生长于光滑二氧化硅表面的碳纳米管具有高度取向性和一致的外径，长度为10—40μm.碳纳米管采取催化剂顶端生长模式并展示出类杯状形貌；生长于粗糙多晶陶瓷表面的碳纳米管捆束随机取向，碳纳米管直径为15—80nm，长度在几百微米，展示 关键词： 碳纳米管 热解法 三步升温工艺     

Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955 Pb（Zn1/3Nb2/3）O3-0.045PbTiO3 Single Crystals

We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955 Pb（Zn1/3Nb2/3） O3-0.045 PbTiO3 （PZN-4.5%PT） single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200℃ to room temperature. Critical electric field of 0.061 k V/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30OC increases abruptly from 14μC/cm^2 for a poling field of O.06kV/cm to 29.5μC/cm^2 for a poling field of 0.061 kV/cm, and afterwards, increases slowly and saturates to 31 μC/cm^2 for poling fields beyond 0.55 kV/cm.     

A Quantum Chemical Study on Recognition of Nitro-phenols by Calix[n]arenes

A PM3 calculation in vacuum of the inclusion complexation ofo-, m-, p-nitro-phenol with calix[n]arenes is performedsuccessfully. The pathways for inclusion process are describedand the most probable structures of the 1:1 complex are soughtthrough a potential energy scan. The energy differences betweenthe inclusion complexes and the hosts, by calculation, show thatthe most stable complexation is calix[4]-p-nitro phenol andcalix[6]-m-nitro phenol.     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

光纤光栅选频掺Yb3+双包层光纤激光器

利用相位掩模法 ,在D形内包层掺Yb3 双包层光纤一端直接写制出Bragg光栅 ,用作双包层光纤激光器的输出腔镜 .试验得到了线宽为 0 196nm ,波长为 10 5 8 2nm ,最高输出功率为 5 70mW的稳定激光输出 ,解决了激光器中模式竞争造成的输出不稳定现象 .从速率方程出发 ,对激光器的输出功率与抽运功率、光栅反射率的关系以及最佳光纤长度进行了理论分析 ,结果与实验符合很好     

Zn(BTZ)2白色有机电致发光材料的合成及其器件制备

以PCl₃为脱水剂,将邻氨基硫酚与水杨酸脱水环化合成出2-(2-羟基苯基)苯并噻唑,并进一步将所得产物与乙酸锌反应合成出2-(2-羟基苯基)苯并噻唑螯合锌(Zn(BTZ)₂)材料。以该配合物作为发光层制备出结构为ITO/PVK:TPD/Zn(BTZ)₂/Al近白色电致发光器件,其色坐标位于白场之内(x=0.242,y=0.359),在驱动电压为16V时,亮度达3200cdm²,对应的量子效率为0.32%。进一步在Zn(BTZ)₂中掺入橙红色染料Rubrene,制成ITO/PVK:TPD/Zn(BTZ)₂:Rubrene/Al结构器件,实现了纯白色发光(色坐标值:x=0.324,y=0.343),非常接近于白色等能点,且量子效率达0.47%。最后对上述器件的发光和电学性能进行了深入的研究和探讨。     

稀土粉末Eu∶Y_2O_3的自由感应衰减量子拍

稀土固体是重要的激光和光电子材料。目前 ,由于以宽带信号和太赫兹比特数据传输率为特征的信息技术的发展 ,稀土固体材料的相干瞬态动力学过程成为宽带与高速信息光子学的基本物理问题之一。研究了室温下稀土粉末样品Eu3+ ∶Y2 O3自由感应衰减的相干瞬态光谱 ,这有助于理解有效的光吸收动力学、激发态弛豫、相干能量传递和超短光脉冲在稀土固体中的传播。用一对紫外飞秒相干光脉冲作用于稀土粉末样品Eu3+ ∶Y2 O3,然后监测物质激发态的布居数随两个激发脉冲之间的延时的变化 ,测量到其自由感应衰减量子拍 (FID) ,从拍频周期分析确定了其能级精细结构 ,能级的退相时间长达皮秒量级。理论分析和实验结果符合得很好。对稀土离子的量子干涉的研究 ,表明其在受激受控光放大方面具有潜在的应用前景     

A New Triterpene from the Orchid Pholidota yunnanensis

A new triterpene, 25-methylenecyclopholidonyl p-hydroxy-trans-cinnamate, was isolated from a orchid Pholidota yunnanensis. The structure elucidation and ^1H, ^13C-NMR assignments were achieved by spectral and chemical method.     

一种可实时化的多光谱图像融合系统

在多光谱摄影和光电成像技术基础上，本文提出了一种可实时化的多光谱图像融合系统。与多光谱摄影相比，不仅可实现多光谱实时化摄像，而且光谱响应进一步向近红外延伸，并引入图像处理技术。实验表明：这种技术对于增加系统的识别能力具有明显的作用，可进一步构成不同用途的新型多光谱图像融合系统。     

Study on the in—plane electrical resistivity and thermoelectric power in single crystals of La2—xBaxCuO4

The in-plane electrical resistivity and thermoelectric power have been measured on single crystals of La_2-xBa_xCuO₄ at around x=0.125. The room temperature resistivity and thermopower have their maximum values at x=0.125, indicating that the carrier concentration is the minimum and the carriers are most strongly localized at x=0.125. The observed semiconductor-like behaviour can be well described by the weak-localized quasi-two-dimensional state. The steep rise in electric resistivity of the sample at x=0.125 below 70K is attributed to the formation of static stripe-order of holes and spins, which are pinned by the low-temperature tetragonal (LTT) structure, as discovered in La_1.48Nd_0.4Sr_0.12CuO₄. The temperature dependence of electric resistivity below 70K is still well described by the formula ρ∝ lnT. A definite change in the slope of thermopower is observed at the low-temperature orthorhombic-LTT structural phase transition temperature. The origin of the 1/8 anomaly is discussed in the text.