碳纳米管上原位沉积钯-钴-镍纳米颗粒及其对乙醇氧化的电活性

以水合肼为还原剂,在水和乙醇的混合溶液中制备多壁碳纳米管(MWCNT)负载的纳米镍(Ni/MWCNT)和纳米镍钴(Ni-Co/MWCNT)颗粒,然后将它们分别与氯化钯溶液反应,形成的钯纳米颗粒原位沉积在MWCNT表面,从而得到MWCNT负载的Pd-Ni/MWCNT和Pd-Ni-Co/MWCNT催化剂。SEM和TEM图像显示,MWCNT上的催化剂颗粒是由5~10 nm的小颗粒团聚而成的30~100 nm的大颗粒,三金属催化剂的粒径比双金属的粒径小,在MWCNT上的分散度更高。ICP和EDS分析显示,Pd直接还原并包覆在纳米镍和纳米镍钴表面;采用循环伏安和计时电流技术,研究了催化剂在碱性溶液中对乙醇氧化的电催化活性,结果表明,Pd-Ni-Co/MWCNT催化剂对乙醇氧化具有强的电催化活性,乙醇氧化对应的峰电流密度达101.8 mA·cm^-2,并且催化剂催化活性稳定。     

高分散在氮掺杂碳纳米管表面铂纳米粒子的高效甲醇电氧化性能

以氮掺杂碳纳米管（NCNT）为载体,利用掺杂氮原子的锚定作用,通过微波辅助乙二醇还原法方便地将Pt纳米粒子高分散地固载于NCNT表面,制得了Pt/NCNT系列催化剂,对催化剂制备规律、电催化甲醇氧化反应（MOR）性能及构效关系开展了系统深入的研究。结果表明,随Pt负载量在18.2%~58.7%（w/w,下同）范围增加,Pt纳米粒子的粒径在2.2~3.7 nm范围相应地逐渐增大。单位质量催化剂的MOR催化活性先增加后急剧减小,在负载量为47.8%时达到最大。Pt的质量比活性在中等负载量（27.6%~47.8%）区间出现高值平台。该变化规律源于Pt纳米粒子的MOR催化活性在3 nm前后的明显差异,即<3 nm时活性差,>3 nm时活性优异。高负载量（58.7%）时活性的急剧下降源于Pt纳米粒子因团聚引起的Pt利用率的降低。     

2-亚胺吡啶镍配合物的合成、晶体结构及催化乙烯聚合

经过一系列化学反应,在吡啶环上引入特丁基及甲醛基,再与2,6-二异丙基苯胺反应生成2-（N-2,6-二异丙基苯亚氨基）亚甲基-6-特丁基吡啶（g）配体,并合成了相应的配合物[NiBr₂（g）]（h）。配合物h的单晶结构表明其为单配体单金属结构,属于正交晶系,a=1.52776（14）nm,b=1.60846（15）nm,c=1.83777（17）nm,晶胞体积4.5160（7）nm³,Z=8。在助催化剂MAO的作用下,考察了催化乙烯聚合特性,在0℃时,所得聚合产物中包括支化聚合物和齐聚物,其中支化聚合物的分子量M_w=1.09×10⁴,其支链大部分为甲基、丁基和长支链,支链密度为58.5。     

表面官能团化增强碳纳米笼超级电容器性能

以具有多级孔结构、高比表面积、良好导电性等特征的碳纳米笼（CNCs）为前体,采用硝酸氧化法在CNCs表面引入含氧官能团。以CNCs为超级电容器电极材料,在相同电流密度下,官能团化样品的比电容显著高于纯CNCs;在1A·g^-1下比电容最高可达到255F·g^-1,比纯CNCs的188F·g^-1增加了34%,这表明表面含氧官能团化能够显著提高CNCs的超级电容器比电容。在100A·g^-1的大电流密度下,硝酸氧化后CNCs的比电容保持在111~167F·g^-1,表明具有良好的耐大电流充放电性能。在10A·g^-1的电流密度下循环10000圈后,CNC-6M样品的比电容由196F·g^-1下降到176F·g^-1,样品的比电容仍保留90%,具有良好的循环稳定性。表面含氧官能团化CNCs所表现出的这种优异的超级电容器性能归因于CNCs的多尺度分级孔结构、高比表面积、良好的导电性、表面亲水性含氧官能团化带来的浸润性提高和引入的赝电容。     

A New Series of C‐6 Unsubstituted Tetrahydropyrimidines: Convenient One‐Pot Chemoselective Synthesis,Aggregation‐Induced and Size‐Independent Emission Characteristics

A new series of C‐6 unsubstituted tetrahydropyrimidines 6 have been directly synthesized via a convenient urea‐catalyzed chemoselective five‐component reaction (5CR) under mild conditions. Compounds 6 show typical aggregation‐induced emission enhancement (AIEE) characteristics because they are practically no emissive in solution but emit blue or green fluorescence in aggregates with fluorescence yield up to 93 %. One of the 5CR products, 6 aa , exhibits blue‐ and green‐fluorescence aggregates (bf‐ and gf‐aggregates). The bf‐ and gf‐aggregates are prepared under different conditions and proved to result from different J‐aggregations by single‐crystal X‐ray analysis. In addition, the bf‐ and gf‐aggregates of 6 aa show unusual size‐independent emission (SIE) characteristics because their maximum emission wavelengths in different sizes (suspension particles, film, powder and crystals) are the same, 434 and 484 nm, respectively. Based on the obtained experimental results, the 5CR mechanism, the origins of AIEE and SIE characteristics are discussed.     

Underpotential Deposition‐Induced Synthesis of Composition‐Tunable Pt?Cu Nanocrystals and Their Catalytic Properties

Pt? Cu alloy octahedral nanocrystals (NCs) have been synthesized successfully by using N,N‐dimethylformamide as both the solvent and the reducing agent in the presence of cetyltrimethylammonium chloride. Cu underpotential deposition (UPD) is found to play a key role in the formation of the Pt? Cu alloy NCs. The composition in the Pt? Cu alloy can be tuned by adjusting the ratio of metal precursors in solution. However, the Cu content in the Pt? Cu alloy NCs cannot exceed 50 %. Due to the fact that Cu precursor cannot be reduced to metallic copper and the Cu content cannot exceed 50 %, we achieved the formation of the Pt? Cu alloy by using Cu UPD on the Pt surface. In addition, the catalytic activities of Pt? Cu alloy NCs with different composition were investigated in electrocatalytic oxidation of formic acid. The results reveal that the catalytic performance is strongly dependent on Pt? Cu alloy composition. The sample of Pt₅₀Cu₅₀ exhibits excellent activity in electrocatalytic oxidation of formic acid.     

DFT Study on Homolytic Dissociation Enthalpies of C-I Bonds

The C-I bond dissociation enthalpies （BDE） of various organic iodides were calculated using high-level theoretical methods including MP2 and CCSD（T） with extrapolated basis set as well as a number of density functional theory methods. After systematic evaluation of the theoretical results against available experimental C-I BDEs, it was found that the MPW LYPIM method gave the lowest root mean square error. We, therefore, used this method to examine the substituent effects on different categories of C（sp3）-I and C（sp2）-I bonds. Fur thermore, the remote substituent effects on the C-I BDEs of substituted iodobenzenes and substituted （iodomethyl）benzenes were also investigated at the same level. The C-I BDEs of typical heteroaromatic iodides including five-membered and six-membered heterocyclic iodides were also examined.     

Copper-and Silver-Mediated Cyanation of Aryl Iodides Using DDQ as Cyanide Source

A new copper and silver‐mediated cyanation of aryl iodides with DDQ as a cyanide source is achieved, providing nitriles with good yields. This new approach represents a safe method leading to aryl nitriles.     

交联聚乙烯基吡咯烷酮快速前处理方法结合液相色谱-串联质谱分析红葡萄酒中酪蛋白过敏原

建立了红葡萄酒酪蛋白过敏原的质谱分析方法。选择专一性SRM离子对,建立3种亚型酪蛋白α-S1,α-S2,β的质谱定性与定量方法;利用交联聚乙烯基吡咯烷酮(PVPP)处理红葡萄酒有效提取蛋白,并直接快速酶解,使前处理缩短到2 h以内。结果表明,酪蛋白的回收率提高到80%以上,检出限达10μg/L。