碳纳米管阵列、捆束的三步升温工艺制备及其形貌与结构

使用结构简单的单温炉设备，通过三步升温热解二茂铁、三聚氰氨混合物方法，在二氧化硅、多晶陶瓷基底上分别合成了碳纳米管阵列、碳纳米管捆束.使用扫描电子显微镜、透射电子显微镜、电子能量损失谱和x射线光电子能谱对合成样品进行了结构和成分分析.结果显示：两种基底上合成的纳米管均为多壁纯碳管；生长于光滑二氧化硅表面的碳纳米管具有高度取向性和一致的外径，长度为10—40μm.碳纳米管采取催化剂顶端生长模式并展示出类杯状形貌；生长于粗糙多晶陶瓷表面的碳纳米管捆束随机取向，碳纳米管直径为15—80nm，长度在几百微米，展示 关键词： 碳纳米管 热解法 三步升温工艺     

Yellow‐light‐emitting cyano‐substituted poly[(1,3‐phenylene vinylene)‐alt‐(1,4‐phenylene vinylene)] derivative: Its synthesis and optical properties

A soluble cyano‐substituted poly[(1,3‐phenylene vinylene)‐alt‐(1,4‐phenylene vinylene)] derivative ( 9 ) was synthesized and characterized. Comparison between 9 and its model compound ( 10 ) showed that the chromophore in 9 remained to be well defined as a result of a π‐conjugation interruption at adjacent m‐phenylene units. The attachment of a cyano substituent only at the β position of the vinylene allowed the maximum electronic impact of the cyano group on the optical properties of the poly(p‐phenylene vinylene) material. At a low temperature (?108 or ?198 °C), the vibronic structures of 9 and 10 were partially resolved. The absorption and emission spectra of a film of 9 were less temperature‐dependent than those of a film of 10 , indicating that the former had a lower tendency to aggregate. A light‐emitting diode (LED) based on 9 emitted yellow light (λ_max ≈ 578 nm) with an external quantum efficiency of 0.03%. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3149–3158, 2003     

电致发光色纯性增强的硅基有机微腔

报道了硅基有机微腔的电致发光（EL）.该微腔由上半透明金属膜、中心有源多层膜和多孔硅分布Bragg反射镜（PS DBR）组成.半透明金属膜由Ag（２０nm）构成，充当发光器件的负电极和微腔的上反射镜.有源多层膜由Al (1 nm) / LiF(05 nm) /Alq3/Alq3:DCJTB/NPB/CuPc/ITO/SiO2组成，其中的Al/LiF为电子注入层，ITO为正电极，SiO2为使正、负电极电隔离的介质层.该PS DBR是采用设备简单、成本低廉且非常省时的电化学腐蚀法用单晶Si来制备的；该PS 关键词： 电化学腐蚀 电致发光 窄峰发射 硅基有机微腔     

线性均衡约束最优化的一个广义投影强次可行方向法

本文讨论带线性均衡约束最优化问题,首先利用摄动技术和一个互补函数将问题等价转化为一般约束最优化问题,然后结合广义投影技术和强次可行方向法思想,建立了问题的一个新算法.算法在迭代过程中保证搜索方向不为零,从而使得每次迭代只需计算一次广义投影.在适当的条件下,证明了算法的全局收敛性,并对算法进行了初步的数值试验.     

新型菲涅尔线聚光太阳电池组件特性分析

以PMMA为材料,采用热压成型工艺加工线聚焦菲涅尔聚光棱镜,对在其聚光条件下不同入射角度情况下太阳电池的电流电压特性进行测试,结果表明:该菲涅尔线聚焦棱镜能有效提高太阳电池的单位输出功率,而且具有比较宽泛的集光角的特性,基本满足实际应用的要求.     

Transport properties of acetone aqueous solutions: molecular dynamics simulation and NMR studies

Two quantities η_rel and are applied to study the nonideal acetone–water association mixture. An all-atom acetone model and a TIP5P water model have been adopted for molecular dynamics simulation. We study the transport properties of the system comparing the 's of strong hydrogen bond and weak contact based on transport properties, MD simulations together with NMR experimental data and find good agreement of concentration dependence, which exhibits the cooperation effect.     

Synthesis and structural characterization of novel,fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties

The synthesis and structural characterization of a series of novel, fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties are described. The monomers, 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a – 2d ), were conveniently and efficiently synthesized from phenols and phthalic anhydride in two steps via 2‐(4′‐hydroxybenzoyl)benzoic acids, which were first obtained by the Friedel–Crafts reaction in good yields and with high stereoselectivity and were then converted into 2a – 2d by fusion with hydrazine. All the polymers were prepared by nucleophilic aromatic substitution (S_NAr) polycondensation between the compounds perfluorobiphenyl and 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a ‐ 2d ). The resulting fluorinated polymers were readily soluble in common organic solvents (e.g., CHCl₃, tetrahydrofuran, dimethylformamide, dimethyl sulfoxide, N‐methylpyrrolidone, etc.) at room temperature. Their weight‐average molecular weights and the polydispersities ranged from (7.96–18.25) × 10³ to 1.31–2.71, respectively. Their glass‐transition temperatures varied from 213 to 263 °C. They were all stable up to 390 °C both in air and in argon. The 5% weight‐loss temperatures of these polymers in air and argon ranged from 393–487 to 437–509 °C, respectively. Wide‐angle X‐ray diffraction studies indicated they were all amorphous and could be attributed to the presence of kink nonplanar moiety, phenyl phthalazinone along the polymer backbone. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 925–932, 2004     

Atom transfer radical polymerization of methyl methacrylate by copper(I)‐pyridine‐2‐carboximidate catalysts

Pyridine‐2‐carboximidates [methyl ( 1a ), ethyl ( 1b ), isopropyl ( 1c ), cyclopentyl ( 1d ), cyclohexyl ( 1e ), n‐octyl ( 1f ), and benzyl ( 1g )] were prepared from the reaction of 2‐cyanopyridine with the corresponding alcohols. Cyclopentyl‐substituted 1d was found to be a highly effective ligand for copper‐catalyzed atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA). For example, the observed rate constant for a CuBr/ 1d catalytic system was found to be nearly twice as high as the cyclohexyl‐substituted CuBr/ 1e catalytic system [k_obs = (1.19 vs 0.56) × 10^?4 s^?1). The effects of the solvents, temperature, catalyst/initiator, and solvent/monomer ratio on the ATRP of MMA were studied systematically for the CuBr/ 1d catalytic system. The optimum condition for the ATRP of MMA was found to be a 1:2:1:400 [CuBr]_o/[ 1d ]_o/[ethyl 2‐bromoisobutyrate]_o/[MMA]_o ratio at 60 °C in veratrole solution, which yielded well‐defined poly(MMA) with a narrow molecular weight distribution of 1.14. The catalytically active copper complex 2d was isolated from the reaction of CuBr with 1d . Narrow molecular weight distributions as low as 1.06 were achieved for the CuBr/ 1d catalytic system by employing 10% of the deactivator CuBr₂. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2747–2755, 2004     

Reversible nonlinear conduction in high‐density polyethylene/acetylene carbon black composites at various ambient temperatures

The reversible nonlinear conduction (RNC) in of high‐density polyethylene/acetylene carbon black composites with different degrees of crosslinking was studied above room temperature and below the melting point of high‐density polyethylene (HDPE). The experimental current density‐electric field strength curves can be overlapped onto a master curve, suggesting that the microscopic mechanisms for the appearance of RNC exist regardless of the ambient temperature and the crosslinking degree of the HDPE matrix. The relationship between the crossover current density and the linear conductivity can be explained in the framework of the dynamic random‐resistor‐network model. According to these results, two electron‐tunneling models are suggested to interpret the microscopic conduction behavior. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1212–1217, 2004     

密封容器中后处理制备Tl2Ba2CaCu2Oy高温超导薄膜及其性能研究

以铝酸镧（001）单晶为基片，采用两步法制备Tl2Ba2CaCu2Oy（Tl 2212）高 温超导薄膜.首先，利用脉冲激光沉积（PLD）工艺沉积Ba2CaCu2Ox非晶前驱体薄膜；然后，前驱体薄膜在高温（720—850℃）下密封钢容器里铊化结晶形成Tl 2212薄膜.XRD结果表明Tl2212 薄膜是沿c轴方向生长的，其相组成为Tl 2212，摇摆曲线（0012）的半高宽为0.72° ，SEM图像显示其表面光滑平整，其零电阻温度为106.2K. 关键词： Tl 2212超导薄膜 脉冲激光沉积