Temperature dependence of surface and structure properties of ZnCdO film

Zn1-xCdx O films are grown on c-sapphire substrates by laser molecular beam epitaxy(LMBE) at different temperatures. Their crystallographic structures, compositions, surface electronic structures are investigated. The a-axis lattice constant of Zn0.95Cd0.05 O is 3.20. Moreover, the epitaxial relationship shows a 30°-in-plane rotation of the film with respect to the c-sapphire substrate. When the substrate temperatures arrives at 500℃, the in situ reflection high-energy electron diffraction(RHEED) pattern of Zn Cd O film shows sharp streaky pattern. The maximum Cd content of Zn Cd O film grown at low substrate temperatures increases up to about 29.6 at.%, which is close to that of the ceramic target. In situ ultraviolet photoelectron spectroscopy(UPS) measurements demonstrate that Zn Cd O film exhibits intense peaks at 4.7 e V and 10.7 e V below the Fermi level, which are assigned to the O 2p and Zn 3p states. Energetic distance between Zn 3d and Cd 4d is 0.60 e V. Above 470 nm, the thin film shows excellent optical transmission.     

潜空战术导弹纵向特性分析及控制系统设计

对潜空战术导弹的水下和空中运动分别建立了纵向质心运动方程,分析了出水前后的弹体纵向特性并完成了经典方法的控制系统设计,最后分别给出了Simulink质心弹道和六自由度弹道对比仿真验证;结果表明,潜空导弹质心运动方程可简捷有效地设计期望弹道和分析弹体特性,据此设计出的控制系统可以顺利实现对潜空导弹的全程控制,提供了一套完整的潜空战术导弹纵向特性分析方法和控制系统设计方法。     

磺硝酚偶氮若丹宁固相萃取光度法测定生物样品中的汞

在 p H2 .0的氯乙酸 -氢氧化钠缓冲介质与吐温 - 80存在下 ,磺硝酚偶氮若丹宁 (NSPAR)与汞反应生成 2∶ 1稳定络合物 ,可被 Waters Sep- Pak C18小柱固相萃取 ,氮 -氮二甲基甲酰氨 (DMF)洗脱后光度法测定 ,λmax=5 5 0 nm,体系摩尔吸光系数ε=8.12× 10 4L· mol-1· cm-1。汞含量在 0 .0 5— 4 .0μg/m L内符合比耳定律 ,用于生物样品中汞含量的测定 ,结果令人满意     

The quantum Weyl group and the universal quantumR-matrix for affine lie algebraA1(1)

The universal quantumR-matrix is obtained in the case of the affine Kac-Moody Lie algebra sl(2).     

HL—1装置汤姆逊散射测量空间两点电子温度

本文叙述用激光汤姆逊散射方法测量HL-1装置在不同放电条件下空间两点的电子温度。简要介绍了测量条件,空间两点测量的实验安排及数据获取系统等。对实验结果进行了初步分析。在适当改变等离子体边缘径向电场分布时,电子温度有明显增加。     

Growth and optical property of ZnWO4: Er crystal

Good quality crystals ZnWO₄ activated with Er³⁺ have been grown by means of Czochralski method and characterized using optical spectroscopy techniques. XRD, absorption spectra, fluorescence spectrum are presented and the Judd-Ofelt intensity parameters Ω₂, Ω₄, and Ω₆ are obtained to be 6.76×10^-20, 0.37×10^-20, and 0.50×10^-20 cm², respectively. Along crystallographic axes, refractive indices are presented. The fluorescence decay time of the ⁴I_13/2 level has also been investigated and shows an exponential behavior with a lifetime value of 5.52 ms. The crystal is potentially used for green and infrared eye-safe lasers.     

掺CdSxSe1-x玻璃波导分布反馈光学双稳器件

本文给出了掺CdS_xSe_1-x玻璃平面波导分布反馈(DFB)光学双稳器件的设计和制备方法,实现了低功耗、快速的本征光学双稳。     

Time-resolved measurement of atomic emission enhancement by fs--ns dual-pulsed laser-induced breakdown spectroscopy

Time-resolved measurement of atomic emission enhancement is performed by using a 500-fs KrF laser pulse incident upon a high density supersonic O_{2} gas jet, synchronized with an orthogonal ns frequency-doubled Nd:YAG laser pulse. The ultra-short pulse serves as an igniter of the gas jet, and the subsequent ns-laser pulse significantly enhances the atomic emission. Analysis shows that the contributions to the enhancement effect are made mainly by the bremsstrahlung radiation and cascade ionization.     

水体中溶解氧对声致发光的影响

采用声源频率为1.1 MHz的超声波, 在温度为283～313 K的范围内引发水中的声致发光, 发现声致发光强度的对数lnI和水中的溶解(DO)的浓度之间呈线性关系。同时模拟了水中含有5种阴离子: Cl-, SO-₄, F-, NO-₃, HCO-₃时阴离子的存在对声致发光的影响, 发现上述5种阴离子对声致发光强度没有影响。     

Corrosion resistance and lubricated sliding wear behaviour of novel Ni-P graded alloys as an alternative to hard Cr deposits

Alternative process to hexavalent chromium, substitute materials and new designs are urgently needed owing to the requirement of “clean” manufacture. This comparative study was conducted to systematically investigate the corrosion resistance and lubricated sliding wear behavior of graded Ni-P alloy deposits produced from a single plating bath by electrodeposition and hard Cr deposits, using potentiodynamic polarization and reciprocating ball-on-disc tribometer. Results showed that Ni-P deposits heat-treated at 400 °C with maximum hardness exhibited more than two orders of magnitude higher corrosion resistance than hard Cr deposits in 10 wt.% HCl solution. The Stribeck curves for the heat-treated Ni-P gradient deposits and hard Cr under lubrication conditions were obtained with accurate control of normal load and sliding speed during the wear process, three main different regimes corresponding to different lubrication mechanism were identified. Heat-treated Ni-P gradient deposits showed relatively poor wear resistance than hard Cr deposits under the lubrication conditions, which may be attributed to superior oil-retaining surface structure and the unique “nodular” effect of hard Cr in wear process.