Synthesis and transition temperatures of liquid crystals incorporating a 1,4-tetrafluorophenylene unit

Two homologous series of mesogenic materials which incorporate a 1,4-tetrafluorophenylene moiety and a terminal cyano- or nitro-substituent have been synthesized by using palladiumcatalysed coupling procedures. The compounds exhibit nematic and/or smectic A phases.     

狭义相对论效应──运动时钟变慢的计算机模拟演示实验

利用精炼的C语言进行程序设计，定量模拟狭义相结论的运动时钟变慢，并对处于两种不同时空观的时钟运行进行对比，使得时间膨胀效应变得直观。     

Synthesis and characterization of poly(arylene ether)s containing 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one or 6‐(4‐hydroxyphenyl)pyridazine moieties

A series of novel soluble pyridazinone‐ or pyridazine‐containing poly(arylene ether)s were prepared by a polycondensation reaction. The pyridazinone monomer, 6‐(4‐hydroxyphenyl)pyridazin‐3(2H)‐one ( 1 ), was synthesized from the corresponding acetophenone and glyoxylic acid in a simple one‐pot reaction. The pyridazinone monomer was successfully copolymerized with bisphenol A (BPA) or 1,2‐dihydro‐4‐(4‐hydroxyphenyl)phthalazin‐1(2H)‐one (DHPZ) and bis(4‐fluorophenyl)sulfone to form high‐molecular‐weight polymers. The copolymers had inherent viscosities of 0.5–0.9 dL/g. The glass‐transition temperatures (T_g's) of the copolymers synthesized with BPA increased with increasing content of the pyridazinone monomer. The T_g's of the copolymers synthesized from DHPZ with different pyridazinone contents were similar to those of the two homopolymers. The homopolymers showed T_g's from 202 to 291 °C by differential scanning calorimetry. The 5% weight loss temperatures in nitrogen measured by thermogravimetric analysis were in the range of 411–500 °C. 4‐(6‐Chloropyridazin‐3‐yl)phenol ( 2 ) was synthesized from 1 via a simple one‐pot reaction. 2 was copolymerized with 4,4′‐isopropylidenediphenol and bis(4‐fluorophenyl)sulfone to form high‐T_g polymers. The copolymers with less than 80 mol % pyridazinone or chloropyridazine monomers were soluble in chlorinated solvents such as chloroform. The copolymers with higher pyridazinone contents and homopolymers were not soluble in chlorinated solvents but were still soluble in dipolar aprotic solvents such as N‐methylpyrrolidinone. The soluble polymers could be cast into flexible films from solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3328–3335, 2006     

Synthesis and properties of noncoplanar rigid‐rod aromatic polyhydrazides and poly(1,3,4‐oxadiazole)s containing phenyl or naphthyl substituents

Two new phenyl‐ and naphthyl‐substituted rigid‐rod aromatic dicarboxylic acid monomers, 2,2′‐diphenylbiphenyl‐4,4′‐dicarboxylic acid ( 4 ) and 2,2′‐di(1‐naphthyl)biphenyl‐4,4′‐dicarboxylic acid ( 5 ), were synthesized by the Suzuki coupling reaction of 2,2′‐diiodobiphenyl‐4,4′‐dicarboxylic acid dimethyl ester with benzeneboronic acid and naphthaleneboronic acid, respectively, followed by alkaline hydrolysis of the ester groups. Four new polyhydrazides were prepared from the dicarboxylic acids 4 and 5 with terephthalic dihydrazide (TPH) and isophthalic dihydrazide (IPH), respectively, via the Yamazaki phosphorylation reaction. These polyhydrazides were amorphous and readily soluble in many organic solvents. Differential scanning calorimetry (DSC) indicated that these hydrazide polymers had glass transition temperatures in the range of 187–234 °C and could be thermally cyclodehydrated into the corresponding oxadiazole polymers in the range of 300–400 °C. The resulting poly(1,3,4‐oxadiazole)s exhibited T_g's in the range of 252–283 °C, 10% weight‐loss temperature in excess of 470 °C, and char yield at 800 °C in nitrogen higher than 54%. These organo‐soluble polyhydrazides and poly(1,3,4‐oxadiazole)s exhibited UV–Vis absorption maximum at 262–296 and 264–342 nm in NMP solution, and their photoluminescence spectra showed maximum bands around 414–445 and 404–453 nm, respectively, with quantum yield up to 38%. The electron‐transporting properties were examined by electrochemical methods. Cyclic voltammograms of the poly(1,3,4‐oxadiazole) films cast onto an indium‐tin oxide (ITO)‐coated glass substrate exhibited reversible reduction redox with E_onset at ?1.37 to ?1.57 V versus Ag/AgCl in dry N,N‐dimethylformamide solution. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6466–6483, 2006     

Synthesis of TiO2–SiO2/polymer core–shell microspheres with a microphase‐inversion method

A novel microphase‐inversion method was proposed for the preparation of TiO₂–SiO₂/poly(methyl methacrylate) core–shell nanocomposite particles. The inorganic–polymer nanocomposites were first synthesized via a free‐radical copolymerization in a tetrahydrofuran solution, and the poor solvent was added slowly to induce the microphase separation of the nanocomposite and result in the formation of nanoparticles. The average particle sizes of the microspheres ranged from 70 to 1000 nm, depending on the reaction conditions. Transmission electron microscopy and scanning electron microscopy indicated a core–shell morphology for the obtained microspheres. Thermogravimetric analysis and X‐ray photoelectron spectroscopy measurements confirmed that the surface of the nanocomposite microspheres was polymer‐rich, and this was consistent with the core–shell morphology. The influence of the synthetic conditions, such as the inorganic composition and the content of the crosslinking monomer, on the particle properties was studied in detail. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3911–3920, 2006     

Preparation and characterization of optically active polystyrene via a chiral nitroxide‐mediated polymerization

2,2,6,6‐Tetramethyl‐4‐[d‐(+)‐10‐camphorsulfonyl]‐1‐piperidinyloxy was synthesized and used as a chiral nitroxide for the bulk polymerizations of styrene initiated with benzoyl peroxide (BPO), tetraethylthiuram disulfide (TETD), and thermal initiation. The results showed that the polymerizations proceeded in a controlled/living way; that is, the kinetics presented approximately first‐order plots, and the number‐average molecular weights of the polymers with narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight) increased with the monomer conversion linearly. The molecular weight distributions in the case of thermal initiation were narrower than those in the case of BPO and TETD, whereas the polymerization rate with BPO or TETD as an initiator was obviously faster than that with thermal initiation. In addition, successful chain‐extension reactions were carried out, and the structures of the obtained polymers were characterized by gel permeation chromatography and ¹H NMR. The specific rotations of the polymers were also measured by polarimetric analysis. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1522–1528, 2006     

Electrical properties of polypyrrole/p‐InP structure

The polypyrrole/p‐InP structure has been fabricated by the electrochemical polymerization of the organic polypyrrole onto the p‐InP substrate. The current–voltage (I–V), capacitance–voltage (C–V), and capacitance–frequency (C–f) characteristics of the PPy/p‐InP structure have been determined at room temperature. The structure showed nonideal I–V behavior with the ideality factor and the barrier height 1.48 and 0.69 eV respectively. C–f measurements of the structure have been carried out using the Schottky capacitance spectroscopy technique and it has been seen that there is a good agreement between the experimental and theoretical values. Also, it has been seen that capacitance almost show a plateau up to a certain value of frequency, after which, the capacitance decreases. The higher values of capacitance at low frequencies were attributed to the excess capacitance resulting from the interface states in equilibrium with the p‐InP that can follow the a.c. signal. The interface state density N_ss and relaxation time τ of the structure were determined from C–f characteristics. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1572–1579, 2006     

Surface characterization of fluorinated polymers (PTFE, PVDF, PFA) for use in ultratrace analysis

Surface characterization of new unused PTFE, PFA and PVDF labware has been carried out by light microscopy, scanning electron microscopy, profilometry and atomic force microscopy. It has been found that in spite of higher micro-roughness, PFA exhibits the lowest nano-roughness and hence seems best suited as vessel material for relatively mild pressureless chemical operations for sample preparation of ultrapure substances, as container material for storage of ultrapure liquids, and for transport of such liquids, e.g., from the producer in the chemical to the end user in the microelectronics industry. This suitability refers only to the surface quality of the investigated materials. PTFE-surfaces, due to the sintering process of production, exhibit the most unfavourable surface quality of the investigated fluorinated polymers.     

合成丙交酯中微量水分分析

合成丙交酯中微量水分分析徐溢，柳胜春（重庆大学化工学院分析教研室６３００４４）关键词丙交酯，微量水，定量分析丙交酯是人工合成骨材料聚乳酸的合成中间体，其性能决定着合成产品的品质，要获得高质量的合成材料，对中间体的分析和监测十分重要。一般要求丙交酯中间...     

反气相色谱法研究聚丙烯结晶动力学及对熔点和结晶度的测定

<正> 研究聚合物的结晶动力学,过去大多采用膨胀计法和解偏振光法。曾有文献报道采用反气相色谱法测得聚乙烯等温结晶线。通过实验可知,测定聚丙烯结晶度时,试样热历史和测定前陈化温度的选择均影响测定结果。此外在测定聚丙烯试样的熔点时,保留图中出现了两个转折,经反复实验证实:此两转折对应于聚丙烯中不同晶形(α-、β-形)的熔点。