Structure and mechanical properties of Al/AlN multilayer with different AlN layer thickness

Nanometer scale Al/AlN multilayers have been prepared by dc magnetron sputtering technique with a columnar target. A set of Al/AlN multilayers with the Al layer thickness of 2.9 nm and the AlN layer thickness variation from 1.13 to 6.81 nm were determined. Low angle X-ray diffraction (LAXRD) was used to analyze the layered structure of multilayers. The phase structure of the coatings was investigated with grazing angle XRD (GAXRD). Mechanical properties of these multilayers were thoroughly studied using a nanoindentation and ball-on-disk micro-tribometer. It was found that the multilayer hardness and reduced modulus showed no strong dependence on the AlN layer thickness. Al2.9 nm/AlN1.13 nm multilayer had more excellent tribological properties than single layers and other proportion multilayers with a lowest friction coefficient of 0.15. And the tribological properties of all the multilayers are superior to the AlN single layer.     

Study on anti-emission materials for non-emitting grid applications in microwave power tubes

Hafnium and platinum were deposited onto molybdenum grids by ion-beam assisted deposition method. Electron-emission characteristics from molybdenum grids with Hf and Pt films, which were contaminated by active electron-emission substances (Ba, BaO) of the cathode, were measured using analogous diode method. The surfaces of grids were analyzed by X-ray diffraction. The results revealed that the reaction between BaO and Hf formed BaHfO₃ compound, which greatly reduced the accumulation of BaO on the surface and accordingly decreased grid emission. In contrast, Ba were formed by the decomposition of BaO on the surface of Pt film under high temperature and re-evaporated from its surface, which reduced the active electron-emission substances on the surface of the grid and effectively restrained grid emission. Their mechanisms for grid-emission suppression are discussed and a good method to develop new grid-coating materials is suggested.     

Preparation and characterization of ZnO nanorods from NaOH solutions with assisted electrical field

ZnO naorods on ZnO-coated seed substrates were fabricated by solution chemical method from Zn(NO₃)₂/NaOH under assisted electrical field. The working mechanism of electrical field was analyzed and the factors affecting the rod growth such as potential, precursor concentration and growth temperature were elucidated. The structural and optical properties are characterized by SEM, TEM, XRD, HRTEM and UV-vis. The results indicated that the nanorods have wurtzite structure without electrical field and are primarily of zincite structure under electrical field; when the electrical field is 1.1-1.3 V, not only the elevation of ion diffusion and adsorption lower the crystallite/solution interfacial energy and then the crystal nucleation barrier by increasing charge intensity, but also the production of H⁺ through oxidation of OH⁻ increases properly the degree of solution supersaturation near the substrate, and thus lowers the activation energy. Both the two processes do favor to rod growth. With increasing precursor concentration in this system, the average diameter and length of ZnO nanorods increase, leading to decreasing of optical transmittance. The maximum rod growth rate at given concentration of Zn²⁺ occurs at a specific temperature.     

Twin Paradox and the Logical Foundation of Relativity Theory

We study the foundation of space-time theory in the framework of first-order logic (FOL). Since the foundation of mathematics has been successfully carried through (via set theory) in FOL, it is not entirely impossible to do the same for space-time theory (or relativity). First we recall a simple and streamlined FOL-axiomatization Specrel of special relativity from the literature. Specrel is complete with respect to questions about inertial motion. Then we ask ourselves whether we can prove the usual relativistic properties of accelerated motion (e.g., clocks in acceleration) in Specrel. As it turns out, this is practically equivalent to asking whether Specrel is strong enough to “handle” (or treat) accelerated observers. We show that there is a mathematical principle called induction (IND) coming from real analysis which needs to be added to Specrel in order to handle situations involving relativistic acceleration. We present an extended version AccRel of Specrel which is strong enough to handle accelerated motion, in particular, accelerated observers. Among others, we show that~the Twin Paradox becomes provable in AccRel, but it is not provable without IND.     

Interference of circularly polarized light: contrast and application in fabrication of three-dimensional periodic microstructures

The contrast of interference pattern formed by two circularly polarized waves and by a linearly polarized wave and a circularly polarized one is discussed. The results are compared with that by two linear beams. It shows that the use of circular light in holographic fabrication of three-dimensional periodic microstructures may remove the necessity of beam ratio and polarization optimization needed in the interference of three linear noncoplanar beams and improve the uniform contrast of resultant pattern simultaneously.     

Optical spectroscopy of Yb/Er codoped NaY(WO4)2 crystal

Erbium and ytterbium codoped double tungstates NaY(WO₄)₂ crystals were prepared by using Czochralski (CZ) pulling method. The absorption spectra in the region 290-2000 nm have been recorded at room temperature. The Judd-Ofelt theory was applied to the measured values of absorption line strengths to evaluate the spontaneous emission probabilities and stimulated emission cross sections of Er³⁺ ions in NaY(WO₄)₂ crystals. Intensive green and red lights were measured when the sample were pumped by a 974 nm laser diode (LD), especially, the intensities of green upconversion luminescence are very strong. The mechanism of energy transfer from Yb³⁺ to Er³⁺ ions was analyzed. Energy transfer and nonradiative relaxation played an important role in the upconversion process. Photoexcited luminescence experiments are also fulfilled to help analyzing the transit processes of the energy levels.     

Simulation of Birefringence and Absorption in InGaAs-GaAs Multiple Quantum Well Acoustooptic Modulators Operating Near 980 nm

This paper presents the simulation of surface acoustic wave (SAW)-induced absorption coefficient and refractive index change in InGaAs-GaAs multiple quantum well (MQW) structures operating near 980 nm. The exciton problem is solved in two dimensional momentum space to include the non-axial effect due to strain induced valance band mixing and nonparabolicity. The optical absorption coefficient and refractive index changes near the band gap in the MQWs are calculated as a function of SAW power.     

Bulk Sn1−xMnxO2 magnetic semiconductors without room-temperature ferromagnetism

Polycrystalline Sn_1−xMn_xO₂ (0≤x≤0.05) diluted magnetic semiconductors were prepared by solid-state reaction method and their structural and magnetic properties had been investigated systematically. The three Mn-doped samples (x=0.01, 0.03, 0.05) undergo paramagnetic to ferromagnetic phase transitions upon cooling, but their Curie temperatures are far lower than room temperature. The magnetization cannot be attributed to any identified impurity phase. It is also found that the magnetization increases with increasing Mn doping, while the ratio of the Mn ions contributing to ferromagnetic ordering to the total Mn ions decreases.     

Initial study on the structure and photoluminescence properties of SiC films doped with Al

SiC films doped with aluminum (Al) were prepared by the rf-magnetron sputtering technique on p-Si substrates with a composite target of a single crystalline SiC containing several Al pieces on the surface. The as-deposited films were annealed in the temperature range of 400-800 °C under nitrogen ambient. The thin films have been characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results show that the introduction of Al into films hinders crystalline formation process. And with the increase of annealing temperature, more Si particles are formed in the films, which strongly affect the optical absorption properties. The photoluminescence (PL) spectra of the samples show two peaks at 370 nm and 412 nm. The intensities of the PL peaks are evidently improved after Al doped. We attribute the origin of the two PL peaks to a kind of Si-related defect centres. The obtained results are expected to have important applications in modern optoelectronic devices.     

Superlattice CoCrPt/Ru/CoFe structure fabricated by pulsed laser deposition

The synthetic antiferromagnets (SAF) have been used in spin-valve sensor in data storage industry [1]. We report a new hard/Ru/soft sandwich structure (SHBL) fabricated by pulsed lased deposition to replace current single layer structure for information recording application. SHBL consists of two magnetic layers separated by thin nonmagnetic layers, typically with Ru layers of 0.7-1.2 nm, through which antiferromagnetic coupling is induced. Varying the relative thickness of the magnetic layers, the spacer layers, and the type of magnetic materials can alter magnetic properties of CoCrPt/Ru/CoFe superlattice. The coercivity H_c and grain size of magnetic layer is also dependent on the laser fluence. High laser fluence results in both small grain size and high H_c. The observed phenomena are related to high quenching and deposition rates during PLD at high fluence, resulting in more pronounced phase segregation.