制备了适于配制紫外光固化涂料的环氧丙烯酸酯，研究了反应温度、阻聚剂、催化剂等因素对环氧树脂与丙烯酸反应的影响；讨论了反应机理和动力学；并利用红外光谱观察了产物的紫外光固化行为。季铵盐能有效地催化环氧树脂和丙烯酸的反应，当其用量为０．６％～１．２％时，在９０～１１０℃反应４．５～８小时后，环氧基转化率大于９７％。由此配制的光固化涂料经紫外光辐照能快速固化。     

Hydrogen bonded layer-by-layer assembly of poly(2-vinylpyridine) and poly(acrylic acid): Influence of molecular weight on the formation of microporous film by post-base treatment

This article describes the buildup of hydrogen bonded multilayer film of poly(2-vinylpyridine) (P2VP) and poly(acrylic acid) (PAA), and the influence of polymer molecular weight on the formation of microporous film by post-base treatment. The formation of a microporous film involved a two-step mechanism: the release of PAA from P2VP/PAA multilayer, and the reorganization of the remaining P2VP on the substrate. Fourier transform infrared spectroscopy (FT-IR) indicated that the release of PAA from hydrogen bonded multilayer was a rapid process, which was almost independent of the molecular weight of PAA. Furthermore, the molecular weight of P2VP had a great effect on micropore formation by immersing the P2VP/PAA multilayer in basic solution. The rate of micropore formation increased with increasing molecular weight. We anticipate that a comparative study on P2VP/PAA films containing high or low molecular weight polymer provides a way to control the surface morphology, and will be helpful and constructive for the forthcoming discussion about the formation of the microporous film.     

The Mechanism on Cyclization, Debenzylation and Oxidation of 1-[1-（Benzyloxy）-3-methylnaphthalen-4-yloxy]propan-2-one

Mansonone compounds represent a series of naturally occurring o-quinones mainly isolated from the heartwood of Mansonia Altissima1 and Ulmus Glabra2. Mansonone F contained oxaphenalene skeleton which was a relatively novel structure and rarely existed in …     

4,5,6-三取代-2H-吡喃-2-酮的简便合成法

2H-吡喃-2-酮及其衍生物是有机合成的蓬要中间体。对于它们的合成已有许多报道,例如利用烯醇醚或烯醇砖醚与丁酰氯反应;羰基化合物与甲氧亚甲螭丙二酸二甲酯反应;α-苯基丙醛酸酯与丙酮的成环缩合2,6-二氯-3-三氯甲基吡啶与亚甲基丁二酸酯的反应,邻氰基苯乙炔、二苯乙二酮和丙酮的反应。但上述方法往往原料较难得到,产率较低或操作麻烦。     

A new isocoumarin from bark of Pellodendron chinense

A new isocoumarin, 3-acetyl-3,4-dihydro-5,6-dimethoxy-1H-2-benzopyran-1-one, was isolated from the cortex of Phellodendron chinense schneid. The structure was determined on the basis of spectroscopic evidences.     

纳米CoHCF修饰电极的制备及其对血红蛋白的电化学测定研究

A cobalt hexacyanoferrate （CoHCF） nanoparticle （size ca. 60 nm） chemically modified electrode （CME） was fabricated and the electrochemical behavior of hemoglobin （Hb） at this nanosized CoHCF CME was studied. In comparison with a bare glassy carbon electrode （GCE） and a general CoHCF CME electrodeposited in a traditional manner, the present nanosized CoHCF CME performed efficiently electrocatalytic reduction for Hb with relatively high sensitivity, stability, and longlife, Combined with liquid chromatography （LC）, the nanosized CoHCF CME was used as the electrochemical detector of Hb in the established flow injection analysis-electrochemical determination （FIA-ECD） system. The peak current was a linear function of concentrations in the range from 2.5×10^-8 to 5.0×10^-6mol/L for Hb, with detection limit of 1.4×10^-8 mol/L. The FIA-ECD system has been successfully applied to assess the Hb content of clinic blood samples with advantages of sensitiveness, speediness, easy control and small sample-consumption.     

在丙烯酰胺聚合反应中聚苯乙烯磺酸效应的研究

<正> 在聚合体系中添加具有一定结构的高分子化合物作模板,并利用此模板高分子与单体分子间存在的某种相互作用使单体分子按一定的排列进行聚合,这是所谓“模板聚合”的最初尝试,近年来,模板聚合已成为一类新的聚合方法,利用模板大分子对其周围单体分子反应过程和生成物结构、分子量的影响,有些研究者已由此成功地实现了对新生成物分子量和空间构型的控制,从而为实现高分子设计开创了新的途径。     

超支化双亲水性嵌段共聚物对CaCO3结晶影响的研究

采用合成的聚乙二醇-超支化聚酯(PEG-hb-DMPA)的线性-超支化杂化二嵌段共聚物, 探讨了羧端基树状功能化的杂化嵌段共聚物对CaCO₃结晶的影响，并用FTIR、XRD、SEM等对产物进行了表征。结果表明，羧端基的双亲水性嵌段共聚物对CaCO₃结晶形貌乃至晶型均具有显著调控作用，比较高的浓度(1.67 g·L^-1, >10 min)或较低浓度作用较长时间(0.33 g·L^-1, 24 h)均得到了呈较均匀球粒形态的球霰石CaCO₃结晶。     

Two Novel Alkaloids from Zanthoxylum nitidum

Two novel alkaloids, 4,5‐dihydroxy‐1‐methyl‐3‐oxo‐2‐(trichloromethyl)‐3H‐indolium chloride ( 1 ) and 4‐(2‐methoxyethyl)‐N,N‐dimethylbenzenamine ( 2 ), were isolated from the EtOH extract of the roots of Zanthoxylum nitidum. Their structures were identified on the basis of spectroscopic and mass‐spectrometric analyses.