Crucial factors affecting the physicochemical properties of sol–gel produced Fe3O4@SiO2–NH2 core–shell nanomaterials

Multifunctional nanomaterials with task-specific physicochemical properties, especially core?Cshell nanostructures with Fe₃O₄ core and NH₂-functional shells (Fe₃O₄@SiO₂?CNH₂), have been extensively investigated as high-performance adsorbents, catalysts and catalyst supports; and in most cases the controllable sol?Cgel technique is the choice for fabrication of this kind of widely applied materials. Herein, we demonstrated that mono-dispersed and spherical Fe₃O₄@SiO₂?CNH₂ nanomaterials with magnetic response core, NH₂-functional shell structure can be facilely prepared by co-condensation of TEOS with APTMS using a versatile sol?Cgel process. It was shown that the proper usage of APTMS and appropriate pre-hydrolysis time of TEOS were crucial and key steps for formation of highly uniform and desirable amino loading Fe₃O₄@SiO₂?CNH₂ materials. The TEOS pre-hydrolysis and the critical time (around 90?min) before the addition of APTMS prove to be vital for uniform structure evolution, while the appropriate concentration of APTMS (~2.28?mmol?L^?1 in our system) leads to well-dispersed materials with relatively high loading of amino functionality. The as-prepared Fe₃O₄@SiO₂?CNH₂ magnetic nanoparticles prepared under optimum conditions possessing superparamagnetic behavior, uniform core?Cshell structure (~200?nm in diameter), relatively large BET surface area (~138?m²/g) and high incorporation of amino-functionality (~2.90?wt?%).     

A 2-dimensional gradual period photonic heterostructure possessing omnidirectional band gap in visible range made by holography

A 2-dimensional gradual period photonic heterostructure was made with holography by use of non-uniform swelling effect of dichromated gelatin during processing. In this structure, the symmetric point group of triangle lattice was debased to C_2V from C_6V. Theoretical analysis and experimental results show that omnidirectional band gap in visible range can be achieved with this kind of heterostructure made by low refractive index materials.