溶胶-凝胶制备技术与新型催化材料Ⅲ.溶胶粒子表面修饰方法制备催化膜

提出用溶胶粒子表面修饰方法，结合溶胶凝胶技术制备无机催化膜．该方法的基本原理是利用合适的金属配合物在胶粒表面的吸附作用，经溶胶凝胶过程，将活性组分结合到无机膜中．实验测定结果表明：（ＮｉＥＤＴＡ）２－，ＶＯ－３，ＭｏＯ２－４，（Ｐｄ（ＮＨ３）４）２＋，ＰｄＣｌ２－４，ＰｔＣｌ２－６和ＲｈＣｌ３－６可用来修饰ＡｌＯＯＨ溶胶．以Ｐｄ／γＡｌ２Ｏ３催化膜的制备为例，经三次溶胶凝胶过程，可制得无裂缺的厚度为９μｍ的Ｐｄ／γＡｌ２Ｏ３催化膜，膜材料的平均孔直径为６ｎｍ，Ｐｄ被均匀地分布在膜的顶层，其平均粒径为２３ｎｍ．     

Structural hierarchy of rock masses and the mechanisms of its formation

The formation mechanisms for the structural hierarchy in geological media are discussed. It is shown that the formation of such a hierarchy is caused by certain external and internal circumstances. The first ones consist in the fact that, because of external actions, the Earth’s poles continuously execute the translational and rotational motions responsible for a regular structure of rock fracture and for the appearance of the scale factor √2. The second ones consist in the fact that, under the action of many random factors and because of external actions, during the formation of geological media there appear dissipative structures and, hence, some self-similar fractal structures are formed.     

Reply to Nathan: How to reconstruct the causal argument

Nicholas Nathan tries to resist the current version of the causal argument for sense-data in two ways. First he suggests that, on what he considers to be the correct re-construction of the argument, it equivocates on the sense of proximate cause. Second he defends a form of disjunctivism, by claiming that there might be an extra mechanism involved in producing veridical hallucination, that is not present in perception. I argue that Nathan’s reconstruction of the argument is not the appropriate one, and that, properly interpreted, the argument does not equivocate on proximate cause. Furthermore, I claim that his postulation of a modified mechanism for hallucinations is implausibly ad hoc.     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004