Measurement of speed of sound in poly(lactic acid)-clay composite

We measured longitudinal speed of sound for matrix[poly(lactic acid)]-additive(clay particles) composite rectangular-solid specimen prepared by injection molding. It was found that the speed of sound measured in the direction along the longer side of the specimen was the highest at the middle of the specimen. This trend corresponded with that for crystallinity determined through differential scanning calorimetry (DSC). A cross section view of the specimen parallel to its longer side showed that there was a transverse flow trace of resin in the vicinity of the injection gate while the flow trace along the direction of the longer side spread wider as getting far from the gate toward the middle of the specimen. The high crystallinity appeared in the middle of the specimen was inferred to come from the promotion of crystallization by molecular orientation induced with the above flow trace parallel to the direction along the longer side of the specimen.     

Multiple Melting Behavior of High-Speed Melt Spun Polylactide Fibers

High-speed melt spinning of polylactide (PLA) was conducted and the structure and multiple melting behavior of the as-spun fibers were investigated. In the analysis of temperature modulated differential scanning calorimetry (TMDSC) thermograms for the as-spun PLA fibers taken-up at 1 and 6 km/min, the peaks around the melting temperature region in the reversing heat flow (RHF) and nonreversing heat flow (NRHF) curves were mainly separated into (1) a pair of an endothermic peak (Peak L) in RHF and an exothermic peak (Peak R) in NRHF in a low temperature region, (2) an endothermic peak (Peak M) both in RHF and NRHF (only in RHF for PLA fiber spun at the low-speed) in an intermediate temperature region, and (3) an endothermic peak (Peak H) both in RHF and NRHF in a higher temperature region. Wide-angle X-ray diffraction (WAXD) measurements were conducted during the heating process of the as-spun fibers cut into powders. In the case of fibers obtained at 1 km/min, disordered crystals, i.e. α′-form crystals, were formed through cold crystallization followed by a disorder-to-order phase transition, i.e. α′ to α crystalline modification, with partial melting of the α′ crystals around 148.5°C in the temperature range of Peaks R and L. Finally, the α form crystals melted above 169.4°C, in the temperature range of Peak H. On the other hand, the PLA crystals generated by the orientation-induced crystallization during the spinning process at a spinning velocity of 6 km/min did not show a WAXD profile of perfect α form crystals but showed an intermediate structure having lattice spacings between the α′ and α forms. Such intermediate crystals did not transformed into α form crystals during the heating process.     

Aerobic oxidation of thiols to disulfides catalyzed by diaryl tellurides under photosensitized conditions

Aerobic oxidation of thiols is efficiently catalyzed by diaryl tellurides such as bis(4-methoxyphenyl) telluride under photosensitized conditions to give the corresponding disulfides in good to excellent yields. In this catalytic system, the tellurone oligomer, produced by the reaction of a telluride with singlet oxygen, is assumed to be the active species and is capable of oxidizing 4 equiv of a thiol.     

Palladium doping of magic gold cluster Au38(SC2H4Ph)24: formation of Pd2Au36(SC2H4Ph)24 with higher stability than Au38(SC2H4Ph)24

A phenylethanethiolate-protected Pd(2)Au(36)(SC(2)H(4)Ph)(24) cluster, which is a two-Pd atom-doped cluster of the well studied magic gold cluster Au(38)(SC(2)H(4)Ph)(24), was synthesized in high purity and its stability was investigated. The results demonstrate that Pd(2)Au(36)(SC(2)H(4)Ph)(24) is more stable than Au(38)(SC(2)H(4)Ph)(24) against degradation in solution and core etching by thiols.