Preparation of nanometer FeCuP alloy and its application in decomposition of PH3

A new ternary Fe-based alloy catalyst FeCuP applied to decompose PH_3 was prepared with low-cost material by chemical reduction deposition method.The properties of it were characterized by XRD,ICP and SEM.Its catalytic activity on the decomposition of PH_3 and the decomposition conditions were studied.FeCuP alloy exhibits high thermal stabilities and high catalytic activity.Using it as catalyst,the decomposition temperature of phosphine decreases from over 800℃to 400-500℃.The decomposition rate of phosphine achieved 100%.     

室温以上磁制冷材料La(Fe1-xCox)11.7Al1.3化合物的研究

通过X射线衍射分析和超导量子干涉磁强计（SQUID）磁性测量,研究了Co替代Fe含量对居里温度在室温以上的磁制冷材料La（Fe1-xCox）11.7Al1.3（x=0.072,0.081）磁结构和磁性能的影响。La（Fe1-xCox）11.7Al1.3材料的居里温度随Co的含量增加而增加,La（Fe0.919Co0.081）11.7Al1.3的居里温度为311 K。当外场变化为1.9 T时磁熵变达到3.6 J·kg^-1·K^-1,RCP值为168.6 J·kg^-1,虽然它的磁熵变小于具有巨磁熵变的磁制冷材料,但是它在磁场为1.9 T时的制冷能力与这些材料相当。     

利用高炉水淬渣制备(Ca/Y)-α-Sialon陶瓷的组织与性能

以高炉水淬渣合成的Ca-α-Sialon粉体为原料采用无压烧结技术制备了（Ca/Y）-α-Sialon陶瓷。通过用排水法、三点弯曲实验法、金相显微镜法、XRD法等手段研究了（Ca/Y）-α-Sialon陶瓷的烧结致密化过程、材料的力学性能、显微组织、相组成和材料的断裂特征。结果表明,适量的Y2O3促进材料的烧结致密化和提高材料的力学性能,但Y2O3过量（大于10%）时对材料的烧结和力学性能不利。掺杂Y^3＋的（Ca/Y）-α-Sialon呈柱状晶,随着Y2O3含量的增加和烧结温度的提高,（Ca/Y）-α-Sialon呈柱状晶出现粗化和等轴化。含10%Y2O3的材料在1700℃烧结时可获得较高的力学性能。     

Dy(ClO_4)_3·3H_2O-18C6-CH_3CN体系的相平衡及其固体配合物的合成

近年来稀土冠醚配合物的研究受到广泛重视,但稀土高氯酸盐冠醚配合物的研究报道较少。高氯酸镝与冠醚18C6的配合物尚未见报道。我们利用半微量相平衡方法研究了Dy(ClO_4)_3·3H_2O-18C6-CH_3CN三元体系在15℃时的溶解度。同时制得了固态配合物,用化学分析及物理化学方法研究了配合物的组成和性质。     

THE REACTION OF AROMATIC ALDEHYDES WITH p-NITROBENZYLLIBUTYLTELLURONIUM BROMIDE BY PHASE TRANSFER CATALYSIS

Under the condition of solid-liquid phase transfer catalysis,olefins were obtained by the reaction of p-nitrobenzyldibutyltelluroniumbromide with aromatic aldehyde.Under the condition of liquid-liquid phasetransfer catalysis,however,different products were obtained due to thereactivity of different bases or aldehydes.     

稀土离子在多孔阳离子交换剂内的扩散动力学

研究了稀土离子在Amberlyst15、D001、XN1010多孔树脂内的自扩散。结果表明,扩散过程遵循二级分散扩散机制。用粒内扩散方程求算了有效粒内扩散系数e,将e分解为树脂孔道扩散系数p及树脂固相扩散系数s,p与该离子在外部溶液中的自扩散系数相近,而s接近于与实验用的多孔树脂交联度相同的凝胶树脂内的自扩散系数值。     

A Systematic Evaluation of Polyurethane as a Conformal Coating for the Inhibition of Corrosion on Electronic Components

The corrosion of printed circuit boards can be effectively prevented with a polyurethane conformal coating. In this study, the protective performance of PU coating was investigated systematically through electrochemical measurements and simulated exposure/immersion tests. Some fungi tests were also included. All experimental results show that a polyurethane coating effectively inhibits corrosion on printed circuit boards. The optimal thickness of the coating film should be about 60 μm. Long-term exposure tests showed that this coating material could preserve the reliability of the investigated printed circuit boards for more than 400 days in a 90% relative humidity environment at 25°C.     

Oscillator Strength Calculations with the Compromised Orbitals

The oscillator strength has been calculated from a common set of compromised orbitals, instead of sets of the two separately optimized non-orthogonal orbitals for the two states involved in the transition. Inaccuracies of two types arose from the calculations were assessed by investigating simple atomic and molecular systems.