Preparation of Sr2CeO4:Eu3+,Dy3+ white luminescence phosphor particles and thin films by using an emulsion liquid membrane system

Sr(2)CeO(4) and Sr(2)CeO(4):Eu(3+),Dy(3+) phosphor particles and thin films were prepared by using an emulsion liquid membrane (ELM, water-in-oil-in-water (W/O/W) emulsion) system, containing VA-10 (2-methyl-2-ethylheptanoic acid) as extractant (cation carrier). A two-step extraction enabled efficient extraction for Sr(3+) and rare earth ions, and the resulting precursor metal oxalate particles produced in the internal water phase of the ELM system were about 60 nm in diameter. Calcination of the oxalate particles in air gave submicrometer-sized Sr(2)CeO(4) and Sr(2)CeO(4):Eu(3+),Dy(3+) particles, which showed blue and white luminescence, respectively, by UV excitation. Blue and white luminescence phosphor thin films were also prepared by soaking alumina substrates into the W/O emulsion containing precursor oxalate particles, followed by calcination in air.     

Electron spin resonance study of polymerization of butadiene with tris(acetylacetonato)titanium and triethylaluminum

ESR spectra of homogeneous catalyst derived from tris(acetylacetonato)titanium(III) and triethylaluminum were observed at several temperatures from ?78°C, to +25°C, at molar ratios of aluminum to titanium of 1–108. At ?78°C, this catalyst yields a violet complex which shows an ESR signal with a g value of 1.959 and is associated with the first intermediate. At ?40°C to ?30°C, this signal decreases, and two signals with g values of 1.947 and 1.960 are observed. The latter two signals diminish at ?5°C to +10°C, while two kinds of new signals with g values of 1.965 and 1.969 appear overlapping each other. The structures of the species corresponding to these five signals are discussed on the basis of the ESR spectra, the intensity change, and the unpaired spin distribution. A new signal with a g value of 1.978 is found in the presence of butadiene at 25°C at Al/Ti > 8 and is assigned to a growing end of polybutadiene with this catalyst. The polymer yield increases remarkedly at Al/Ti molar ratios greater than 10. The microstructure of the resulting polymer consists almost completely of 1,2 units. The structure of the growing end is proposed to be a titanium (III) species containing two 1-substituted allyl groups, by comparison with the structure ascribed to the growing end of polybutadiene with n-butyl titanate-triethylaluminum catalyst.     

Preparation and photochromism of diarylethene covalently bonded onto layered sodium-magadiite surfaces

Diarylethene derivatives (DE) covalently bonded to silanol oxygens of layered silicate surfaces, i.e., magadiite (Mag), were synthesized and investigated for their photochromic behavior. The DE-Mag layered hybrids were found to undergo reversible color change by alternating UV and visible light irradiation. A more highly efficient, reproducible photochromic behavior was realized with DE-Mag than with a corresponding DE-Si possessing silyl substituents on DE in place of the Mag surface. Moreover, the present covalently bonded DE exhibited an improvement over DE hybrids incorporated in layered double hydroxide (LDH) clays, in which the repetitive photochromic behavior decreased during alternating irradiation, due to the accumulation of the photochemically inert parallel isomers of DE.     

Electron spin resonance study on polymerization of alkyl acrylates with n-butyl titanate(IV)–triethylaluminum catalyst

n-Butyl titanate(IV)–triethylaluminum catalyst at Al/Ti molar ratios greater than 6 polymerizes methyl and n-butyl acrylates at ?78°C. The polymerization system which includes methyl acrylate at ?78°C, gives two ESR signals with g factors of 1.958 and 1.961 that overlap each other. The absorption intensity of the latter signal is approximately proportional to the polymer chain concentration calculated from polymer yield and the molecular weight. The polymerization system at Al/Ti ratios smaller than 3 has no catalytic activity on the polymerization and shows only the ESR signal with the g factor of 1.958. On the basis of these facts the ESR signal with the g factor of 1.961 is attributed to the active growing end of poly(methyl acrylate) with this catalyst. The character of this active growing end is discussed.     

Photoinduced face-inversion of conjugated tetraene ligands on a Pd-Pd-Pd moiety

The linear sandwich tripalladium complexes [Pd3{Ar(CH=CH)4Ar}2[BArf]2 (Ar = Ph, p-t-Bu-C6H4, p-styryl-C6H4) undergo photoinduced isomerization involving face-inversion of the tetraene ligands. Irradiation of these complexes with visible light (>510 nm) resulted in rac (staggered sandwich) to meso (eclipsed sandwich) isomerization. The structures of rac and meso isomers are determined by X-ray crystallographic analyses.     

Polyiodide composition in poly(vinyl acetate)-iodine-iodide complex

Polyiodide formed by complexation of poly(vinyl acetate) (PVAc) with iodine in the presence of iodide has been investigated by chemical analysis and resonance Raman spectrophotometry. When PVAc films were immersed in iodide-iodine aqueous solutions which had different ratios of iodide to iodine concentration [I^?]/[I₂], the complex films exhibited tremendous variations of swelling degree, despite the relatively small change in the amount of bound iodine. From a quantitative chemical analysis, the composition of polyiodide bound to PVAc was found to be 1.01 ± 0.035 in the molar ratio of iodide to iodine irrespective of the composition of the iodide-iodine aqueous solution ([I^?]/[I₂] = 2–500). The polyiodide formed in PVAc-iodine-iodide complex was therefore inferred to be (I₃^?)_n. Resonance Raman spectra obtained on PVAc-iodine-iodide complexes were also identical to those of the benzamide-iodine complex, in which the polyiodide consists of (I₃^?)_n, consistent with the result from chemical analysis.     

Self-assembly patterning of colloidal crystals constructed from opal structure or NaCl structure

We developed a novel self-assembly process to fabricate an orderly array of particle wires constructed from a close-packed colloidal crystal without preparation of patterned templates. A substrate was immersed vertically into a SiO2 colloidal solution, and the liquid surface moved downward upon evaporation of solution. Particles formed a mono-/multiparticle layer, which was cut by the periodic drop-off of solution. The orderly array of particle wires was successfully fabricated, showing the suitability of the self-assembly process for the fabrication of nano-/microstructures constructed from nano-/microparticles or blocks. The mechanism of the assembly process and control of thickness, width, and interval of particle wires were further discussed. Moreover, an array of particle wires constructed not from close-packed face-centered cubic (or hexagonal close packed) structure but from two kinds of particles was realized to fabricate an array of particle wires with NaCl structure by this self-assembly process.     

Development of direct fluorination technology for application to materials for lithium battery

Direct fluorination of 1,3-dioxolan-2-one with elemental fluorine was successfully carried out to provide 4-fluoro-1,3-dioxolan-2-one, which was expected as an additive for lithium ion secondary battery. 4-Fluoro-1,3-dioxolan-2-one was also further fluorinated with elemental fluorine to give three isomers of difluoro derivatives by the same methodology. Another topic is the preparation of trifluoromethanesulfonyl fluoride, an intermediate of lithium battery electrolyte, by the reaction of methanesulfonyl fluoride with elemental fluorine. The use of perfluoro-2-methylpentane as a solvent gave satisfactory selectivity of trifluoromethanesulfonyl fluoride.     

The hydrophilization of polystyrene substrates by 172-nm vacuum ultraviolet light

This paper describes the photochemical surface modification of polystyrene (PS) substrates using vacuum ultraviolet (VUV) light 172 nm in wavelength. We have particularly focused on the effects of atmospheric pressure during VUV irradiation on the obtained surface's wettability and the stability of the wettability, in addition to its chemical structure, morphology, and photooxidation rate. Samples were photoirradiated with VUV light under pressures of 10, 10(3), or 10(5) Pa. Although, in each case, the originally hydrophobic PS surface became highly hydrophilic, the final water-contact angle and photooxidation rate depended on the atmospheric pressure. The samples treated at 10 Pa were less wettable than those prepared at 10(3) and 10(5) Pa due to the shortage of oxygen molecules in the atmosphere. The minimum water-contact angles of the samples treated at 10, 10(3), and 10(5) Pa were about 8 degrees, 0 degrees, and 0 degrees, respectively. With the samples prepared at 10 and 10(3) Pa, photooxidation reactions proceeded in the topmost region closest to the surface, while at 10(5) Pa photooxidation was found to be greatly enhanced in the deeper regions, as evidenced by angle-resolved X-ray photoelectron spectroscopy. Photoetching rates were determined through atomic force microscope observation of microstructured PS samples prepared by a simple mesh-contact method. As estimated from AFM images of the latticed microstructures obtained, the rates of samples prepared at 10(3) and 10(5) Pa were about 1.5 and 1.3 nm/min, respectively. However, no photoetched features were observable on the sample surface prepared at 10 Pa. Hydrophilic stability also varied greatly depending on atmospheric pressure. The hydrophilicity of samples treated at 10 and 10(3) Pa gradually decreased as they were exposed to air. On the other hand, the sample surface prepared at 10(5) Pa showed excellent hydrophilicity even after being left in air for 30 days.     

Reversible color changes in lamella hybrids of poly(diacetylenecarboxylates) incorporated in layered double hydroxide nanosheets

The present study is an investigation of a reversible thermal color change induced in lamella hybrids of poly(diacetylenecarboxylates) incorporated in layered double hydroxide (LDH) nanosheets. These poly-[m,n]/LDH hybrids prepared by the photo- or gamma-ray-induced polymerization of diacetylenecarboxylates, i.e., CH(3)(CH(2))(m)()(-)(1)CC-CC(CH(2))(n)()(-)(1)CO(2)(-) (mono-[m,n]), and intercalated in LDH lamella sheets, were observed to develop colors ranging from yellow to blue. The change in color was found to depend greatly on the alkyl carbon numbers of the mono-[m,n] (m,n = 10,11; 5,11; 10,5; 16,1) values. Moreover, the conformational alignment of the mono-[m,n] within the LDH was observed to be a crucial factor in color development, which was greatly affected by the intercalation degrees and extent of poly(ene-yne) linkage elongation of the polymers. For the poly-[m,n]/LDH hybrids investigated, a reversible color change was found to occur repeatedly and remarkably for the poly-[10,11]/LDH hybrid. This color change occurred at temperatures between ca. 20 and 80 degrees C back and forth from purple red to bright orange, in stark contrast to the irreversible color change for poly-[10,11] without LDH. Moreover, DSC and Raman spectroscopic studies of the LDH hybrids showed that the thermochromic temperature corresponded to the phase transition temperature of 80 degrees C. XRD analysis also indicated that the poly-[m,n]/LDH hybrid could retain its lamella structure during such thermochromic color changes, enabling conformational recovery in the polymer chains by a cooling down of the hybrids to temperatures lower than the transition temperature, while the nonhybrid poly-[10,11] powders exhibited an irreversible color change at 60 degrees C, above which the polymer powder turned amorphous.