Fatigue life enhancement by irradiation of 12Cr1MoV steel with a Zr<Superscript>+</Superscript> ion beam. Mesoscale deformation and fracture

The structure and properties of 12Cr1MoV steel irradiated with a zirconium ion beam were studied by optical microscopy, scanning electron microscopy, and micro- and nanoindentation. It is shown that the modification covers the entire cross-section of the irradiated specimens to a depth of 1 mm. The data on irradiation-induced structural changes are used to interpret the changes in mechanical properties of the irradiated specimens under static and cyclic loading. Particular attention is given to analysis of strain estimation by the digital image correlation method.     

Synthesis of a disaccharide of phenolic glycolipid from Mycobacterium leprae (PGL-I) and its conjugates with bovine serum albumin

Russian Chemical Bulletin - Terminal disaccharide fragment of phenolic glycolipid from Mycobacterium leprae (PGL-I) was synthesized as a glycoside with 4-(2-aminoethoxy)phenyl aglycon. The obtained...     

Fluorescent Properties of Polymer Systems with Negative Photochromism Based on Complexes of Spiropyran with Metal Ions

Russian Journal of Applied Chemistry - A spectral-kinetic investigation was carried out to study the fluorescent properties of complexes of molecules of photochromic nitro-substituted spiropyran...     

Investigation of the Effect of Artificial Internal Defects on the Tensile Behavior of Laser Powder Bed Fusion 17–4 Stainless Steel Samples: Simultaneous Tensile Testing and X-Ray Computed Tomography

Experimental Mechanics - Insufficient data are available to fully understand the effects of metal additive manufacturing (AM) defects for widespread adoption of the emerging technology....     

A model for crack formation during active solid pyrolysis of a char-forming solid: crack patterns; surface area generation; volatile mass efflux

A model is developed for the formation and propagation of cracks in a material sample that is heated at its top surface, pyrolyses, and then thermally degrades to form char. In this work the sample is heated uniformly over its entire top surface by a hypothetical flame (a heat source). The pyrolysis mechanism is described by a one-step overall reaction that is dependent nonlinearly on the temperature (Arrhenius form). Stresses develop in response to the thermal degradation of the material by means of a shrinkage strain caused by local mass loss during pyrolysis. When the principal stress exceeds a prescribed threshold value, the material forms a local crack. Cracks are found to generally originate at the surface in response to heating, but occasionally they form in the bulk, away from ever-changing material boundaries. The resulting cracks evolve and form patterns whose characteristics are described. Quantities examined in detail are: the crack spacing in the pyrolysis zone; the crack length evolution; the formation and nature of crack loops which are defined as individual cracks that have joined to form loops that are disconnected from the remaining material; the formation of enhanced pyrolysis area; and the impact of all of the former quantities on mass flux. It is determined that the mass flux from the sample can be greatly enhanced over its nominal (non-cracking) counterpart. The mass efflux profile qualitatively resembles those observed in Cone Calorimeter tests.