Study of the THGEM detector with a reflective CsI photocathode

The THGEM detector without and with a CsI has been tested successfully. The optimal parameters of THGEM have been determined from eight samples. The UV photoelectric effect of the CsI photocathode is observed. The changing tendency related to the extraction efficiency (ε_extr) versus the extraction electric field is measured, and several electric fields influencing the anode current are adjusted to adapt to the THGEM detector with a reflective CsI photocathode.     

离子液体中电沉积制备钴纳米线阵列

Porous anodic alumina (PAA) was used as a template to prepare Co nanowires array from 1-ethyl-3-methylimidazolium chloride ionic liquid by direct current method. The surface morphology of porous anodic alumina template was observed by field emission-scanning tunneling microscopy (FE-SEM) before and after the electrodeposition of Co nanowires. The electrodeposition of Co nanowires was characterized by transmission electron microscopy (TEM) and X-ray powder diffraction (XRD). TEM results indicate that the Co nanowire surface is coarse and porous when aqueous solution was used as electrolyte， and the Co nanowire deposited from the ionic liquid is uniform and smooth. XRD results show that the electrodeposition of Co is a mixture of crystal and microcrystal phase.     

模板法室温合成CdS纳米棒

模板法室温合成CdS纳米棒;模板法;硫化镉;一维CdS纳米材料     

水相法制备CdS纳米棒

水相法制备CdS纳米棒;cds纳米棒;水相溶液;晶体生长;乙二胺     

超薄金壳包覆NaYF4:Yb,Er@SiO2纳米结构的可控合成与表面增强上转换荧光

利用原位还原法成功制备了尺寸均一、超薄完整金壳包覆的NaYF₄:Yb,Er@SiO₂@Au（NSA）纳米结构,其XRD、TEM、EDX、HRTEM-HAADF、Mapping及吸收光谱表征结果表明,SiO₂壳及纳米金壳的平均厚度分别约为5 nm和2 nm。在980 nm连续激光激发下,系统研究了核壳结构的上转换荧光强度与氯金酸浓度的依赖关系。稳态光谱结果显示,NSA与仅SiO₂包覆样品（NS）相比Er³⁺的红绿荧光强度均增强了~2.8倍。通过分析上转换荧光动力学过程及利用FDTD方法模拟,讨论了表面等离激元增强上转换荧光的机制。     

水+3-甲基吡啶+溴化钠三元溶液临界跨接现象

采用折射率法在较宽温度范围内研究了溴化钠、3-甲基吡啶和水的临界质量分数分别为0.240、0.192和0.568体系的临界性质, 发现在近临界点临界指数为0.365, 与Fishe重整化值一致. 有效临界指数随着温度逐渐远离临界点, 从0.365下降到0.20左右, 但当排除了“正规项”的影响后, 展现出向平均场理论值0.5单调跨接的行为.     

郁金药材中姜黄素类成分含量测定方法研究

开展了郁金药材中姜黄素类成分的含量测定的研究,确立了姜黄素的优化提取条件,建立了姜黄素的高效液相色谱含量测定方法。通过筛选,发现以60％乙醇回流,15倍药材溶剂量,提取时间1h,提取次数1次对姜黄素的提取较完全。姜黄素在0．0265～0．2648μg范围内线性关系良好。精密度、稳定性和重复性的RSD均小于2％,平均加标回收率为99。73％,RSD为1．41％。     

对叔丁基杯[n]芳烃酰胺衍生物的合成及其对某些金属离子的萃取性能

对叔丁基杯[n]芳烃酰胺衍生物的合成及其对某些金属离子的萃取性能;杯芳烃; 酰胺衍生物; 金属离子; 萃取; 离子识别     

强流脉冲电子束应力诱发的微观结构

利用强流脉冲电子束装置在各种工艺条件下对奥氏体不锈钢、单晶铝及多晶铝等面心立方金属进行辐照处理.利用扫描电子显微镜和透射电子显微镜等详细分析了辐照样品的变形组织与结构.通过分析，在一定程度上建立起强流脉冲电子束诱发的应力特征与变形结构之间的关系，并对目前现有的几种应力波数值模拟结果进行了分析.实验结果表明，强流脉冲电子束能够在材料内部诱发10²—10³MPa的应力，其传播方式与材料的 晶体结构关系密切.这一应力是导致材料深层性能与微观组织结构发生变化的根源所在. 关键词： 强流脉冲电子束 应力 微观结构 变形