Nylon‐6/glass‐fiber (GF)/liquid‐crystalline‐polymer (LCP) ternary blends with different viscosity ratios were prepared with three kinds of nylon‐6 with different viscosities as matrices. The rheological behaviors of these blends were characterized with capillary rheometry. The morphology was observed with scanning electron microscopy and polarizing optical microscopy. This study showed that although LCP did not fibrillate in binary nylon‐6/LCP blends, LCP fibrillated to a large aspect ratio in some ternary blends after GF was added. The addition of 5 wt % LCP significantly reduced the melt viscosity of nylon‐6/GF blends to such an extent that some nylon‐6/GF/LCP blends had quite low viscosities, not only lower than those of neat resins and nylon‐6/GF blends but also lower than those of corresponding nylon‐6/LCP blends. The mutual influence of the morphology and rheological properties was examined. The great reduction of the melt viscosity was considered the result of LCP fibrillation. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1619–1627, 2004     

Permeability of N2, Ar,He, O2, and CO2 through as‐extruded amorphous and biaxially oriented polyester films: Dependence on chain mobility

For as‐extruded amorphous and biaxially orientated polyester films based on poly(ethylene terephthalate), poly(ethylene naphthalate), and copolymers containing poly(ethylene terephthalate) and poly(ethylene naphthalate) moieties, permeability, diffusion, and solubility coefficients are interpreted in terms of chain mobility. The influence of polymer morphology is determined by comparison of the data for as‐extruded amorphous sheets and materials produced with different biaxial draw ratios. The crystallinities of the samples were assessed using differential scanning calorimetry and density measurements. Changes in mobility at a molecular level were investigated using dielectric spectroscopy and dynamic mechanical thermal analysis. The study, in conjunction with our earlier work, leads to the conclusion that the key to understanding differences in gas transport is the difference in local chain motions rather than in free volume. This was illustrated by the permeability results for He, Ar, N₂, and O₂ in the range of polyesters. However, the permeability of CO₂ was found to require alternative explanations because of polymer–penetrant interactions. For biaxially oriented samples, the differences in diffusivity are not only due to differences in local chain motions, but also additional constraints resulting from the increased crystallinity and chain rigidity—which also act to hinder segmental mobility. The effectiveness of the reduction in permeability in the biaxially oriented films is consequently determined by the ability of the polymer chains to effectively align and form crystalline structures. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2916–2929, 2004     

Segmental and secondary dynamics in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) blends

Broadband dielectric spectroscopy was used to study the segmental (α) and secondary (β) relaxations in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) (PVPh/PMMA) blends with PVPh concentrations of 20–80% and at temperatures from ?30 to approximately glass‐transition temperature (T_g) + 80 °C. Miscible blends were obtained by solution casting from methyl ethyl ketone solution, as confirmed by single differential scanning calorimetry T_g and single segmental relaxation process for each blend. The β relaxation of PMMA maintains similar characteristics in blends with PVPh, compared with neat PMMA. Its relaxation time and activation energy are nearly the same in all blends. Furthermore, the dielectric relaxation strength of PMMA β process in the blends is proportional to the concentration of PMMA, suggesting that blending and intermolecular hydrogen bonding do not modify the local intramolecular motion. The α process, however, represents the segmental motions of both components and becomes slower with increasing PVPh concentration because of the higher T_g. This leads to well‐defined α and β relaxations in the blends above the corresponding T_g, which cannot be reliably resolved in neat PMMA without ambiguous curve deconvolution. The PMMA β process still follows an Arrhenius temperature dependence above T_g, but with an activation energy larger than that observed below T_g because of increased relaxation amplitude. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3405–3415, 2004     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

Viscosity,particle size distribution,and structural investigation of tetramethyloxysilane/2‐hydroxyethyl methacrylate sols during the sol–gel process with acid and base catalysts

The tetramethoxysilane (TMOS)/2‐hydroxylethyl methacrylate (HEMA) hybrid gels were synthesized with acid and base catalysts, via the in situ polymerization of HEMA, with and without the cosolvent methanol. With methanol in the TMOS/HEMA sol, the enhanced esterification and depolymerization reactions of the silanols resulted in a slower growth of silica particles. The silica particles that were synthesized with an acid catalyst were less than 40 nm. The thermal resistance of the poly(2‐hydroxyethyl methacrylate) (PHEMA) chains was enhanced by the addition of colloidal silica. The Fourier transform infrared characterizations and the exothermal peaks on the differential scanning calorimetry traces of these hybrid gels indicated chemical hybridization occurring as a result of condensation of the colloid silica and PHEMA at higher temperatures. Hence, the residual weight content of the hybrid gel after its synthesis with the base catalyst was even higher than the content of TMOS in the hybrid sol. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3476–3486, 2004     

Time-resolved chemiluminescence technique for the microdetermination of proteins based on their complexation with copper(II).

Based on the complexation between proteins and Cu(II) coupled with the time-resolved chemiluminescence (CL) technique, a highly sensitive and quantitative assay for measuring proteins in solution is described. The complexes of proteins with Cu(II) have a strongly catalytic effect on the luminol-H2O2 CL reaction. Because the CL emission produced by the complexes is much more long-lived than that by Cu(II), the CL signals originating from proteins can be easily identified and measured with a time-resolved technique. On this basis, bovine albumin fraction V (BAF V) can be quantitatively determined in the range of 0.01 - 5.0 microg/ml with a detection limit of 5.8 ng/ml. The results show that the proposed assay exhibits a small variation in the response values for the same amount of different proteins, as compared to the Lowry as well as Bradford assays. The CL assay has also been studied for the detection of immobilized proteins.     

DNA-conjugated polymers for self-assembled DNA chip fabrication.

We developed two DNA-conjugated polymers, one based on polyallylamine and the other on polyacrylic acid, for use in DNA chips. A 30-mer single-stranded DNA probe and thioctic acid were covalently attached to polyallylamine as sidechains. The same single-stranded DNA and 3-(pyridyldithio)propionyl hydrazide were covalently attached to polyacrylic acid as sidechains. Both DNA-conjugated polymers could be specifically immobilized onto a gold sensor substrate by a self-assembly technique. The interactions between fully matched DNA and each DNA-conjugated polymer were investigated by surface plasmon resonance. A gold surface modified with either DNA-conjugated polymer recognized fully matched DNA much better than unmatched DNA. The hybridization selectivity and efficiency of DNA-conjugated polyallylamine was optimized by adjusting the pH so as to reduce the effects of cationic polymer sidechains. The hybridization selectivity and efficiency of DNA-conjugated polymers were higher than those of a conventional immobilized thiol-based DNA. The coating of DNA-conjugated polymers reduced nonspecific adsorption of DNA by the gold substrate. DNA-conjugated polyacrylic acid was more selective toward fully matched DNA than was DNA-conjugated polyallylamine. Therefore, DNA-conjugated polymers show promise for application in novel DNA chips.     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Behavior of cellulose in NaOH/Urea aqueous solution characterized by light scattering and viscometry

Cellulose was dissolved in 6 wt % NaOH/4 wt % urea aqueous solution, which was proven by a ¹³C NMR spectrum to be a direct solvent of cellulose rather than a derivative aqueous solution system. Dilute solution behavior of cellulose in a NaOH/urea aqueous solution system was examined by laser light scattering and viscometry. The Mark–Houwink equation for cellulose in 6 wt % NaOH/4 wt % urea aqueous solution at 25 °C was [η] = 2.45 × 10^?2 weight‐average molecular weight (M_w)^0.815 (mL g^?1) in the M_w region from 3.2 × 10⁴ to 12.9 × 10⁴. The persistence length (q), molar mass per unit contour length (M_L), and characteristic ratio (C_∞) of cellulose in the dilute solution were 6.0 nm, 350 nm^?1, and 20.9, respectively, which agreed with the Yamakawa–Fujii theory of the wormlike chain. The results indicated that the cellulose molecules exist as semiflexible chains in the aqueous solution and were more extended than in cadoxen. This work provided a novel, simple, and nonpollution solvent system that can be used to investigate the dilute solution properties and molecular weight of cellulose. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 347–353, 2004