Phase transformation of Ni-B, Ni-P diffusion barrier deposited electrolessly on Cu interconnect

In this paper, we report that the phase transformation of Ni-B, Ni-P diffusion barriers deposited electrolessly on Cu, for the reason that the Ni-P layer is a more effective diffusion barrier than the Ni-B layer. The Ni₃B crystallized was decomposed to Ni and B₂O₃ above 400 °C and the Ni₃P crystallized was decomposed to Ni and P₂O₅ above 600 °C respectively in Ar atmosphere. Also, the Ni₃B was decomposed to Ni and free B above 400 °C and the Ni₃P was decomposed to Ni and free P above 600 °C respectively in H₂ atmosphere. The decomposed Ni formed a solid solution with Cu. The Cu diffusion occurred above 400 °C for Ni-B layer and above 600 °C for Ni-P layer, respectively. Because the decomposition temperature of Ni-P layer is about 200 °C higher than that of Ni-B layer, the Ni-P layer is a more effective barrier for Cu than the Ni-B layer.     

Synthesis of a Novel Aromatic Diamino-bridged Bis（β-cyclodextrin） and its Inclusion Complexation with Dyes Molecules

Bridged bis(β-cyclodextrin)s (CDs), as a very important family of CD derivatives, have been known that they can significantly alter the molecular binding ability and selectivity toward a variety of guests in comparison with parent cyclodextrin. Their two…     

Two New Eremophilenolides from Ligularia muliensis

Many Ligularia species have long been used as traditional folk medicine for theirantibiotic, antiphlogistic and antitussive activities1, and were found to be an importantsource of eremophilane. In the course of our search for bioactive sesquiterpenoids, w…     

一些特殊图类乘积的离散度

连通图的离散度是用s(G)来表示的,s(G)=max{ω(G-S)-|S|:ω(G-S)>1,SV(G)}.给出了两个完全图乘积的和一个完全图与路的乘积的离散度.还给出了两个完全图乘积的坚韧度.     

Paper-like Microfibrous Nickel Catalyst for Hydrogen Production via NH3 Decomposition in Fuel Cell Applications

Recently, miniature H2 generator to power fuel cells for portable/micro electronic devices and passenger propulsion has been the focus of intense research activities1-3. One of the strategies is to find simple CO-free H2 production with novel microreactor…     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Property changes of electroplated Cu/Co alloys and multilayers by organic additives

We investigated the change of magnetic properties of the electroplated Cu/Co alloys and multilayers caused by organic additives and high temperature annealing. When plated with a pure Cu/Co electrolyte, the alloy contained ∼25% of Cu and ∼75% of Co. The alloy was made of hcp-Co, fcc-Co and Cu(1 1 1) and was super-paramagnetic at room temperature. As we add a few organic additives in the plating electrolyte, the hcp-Co of the films disappeared. The organic additives contained in the electrolytes changed paramagnetic Cu/Co multilayers to ferromagnets. High-temperature thermal annealing increased coercivity due to the growth of the Co grains.     

Ruthenium-catalyzed regioselective synthesis of 2-substituted indoles via ring-opening of epoxides by anilines

Anilines react with epoxides in dioxane at 180°C in the presence of a catalytic amount of a ruthenium catalyst along with tin(II) chloride to afford 2-substituted indoles in moderate to good yields.     

Synthesis and electrical characteristics of polyaniline nanoparticles and their polymeric composite

Monodisperse polyaniline nanoparticles (PAPSSA) were synthesized from an oxidative dispersion polymerization using poly(sodium 4-styrenesulfonate) (PSSA) as both a polymeric stabilizer and a dopant agent due to its acidity. The nanoparticles were being stabilized with two different molecular weight of PSSA. Size effect of PAPSSA particles were examined by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and dynamic light scattering (DLS). The d.c. electrical conductivity of composite films on the glass substrate was measured by a four-probe method. It was found that the electrical properties of the composite films are affected by the content of nano-sized polyaniline and different molecular weights of stabilizer in the poly(vinyl alcohol) (PVA) matrix.