Stress in polycrystalline GaN films prepared by r.f sputtering

Undoped, Be-doped and Si-doped polycrystalline GaN films were deposited by R.F. sputtering onto fused silica substrates. The films were deposited at various deposition temperatures ranging from 300 K to 623 K and characterized by optical measurements while the microstructural information was obtained from SEM and XRD studies. The compositional study for the GaN film was carried out using SIMS. Residual stresses in these films were evaluated from the band tail of the absorption spectra as well as from direct measurements of hardness by commercially available depth sensing indentometer. It was observed that undoped GaN films had the highest hardness followed by that for Be-doped and Si-doped films. The values of hardness obtained form the above optical measurement tallied quite well with those obtained from direct indentation measurement.     

Intracellular transport of single-headed molecular motors KIF1A

Motivated by experiments on single-headed kinesin KIF1A, we develop a model of intracellular transport by interacting molecular motors. It captures explicitly not only the effects of adenosine triphosphate hydrolysis, but also the ratchet mechanism which drives individual motors. Our model accounts for the experimentally observed single-molecule properties in the low-density limit and also predicts a phase diagram that shows the influence of hydrolysis and Langmuir kinetics on the collective spatiotemporal organization of the motors. Finally, we provide experimental evidence for the existence of domain walls in our in vitro experiment with fluorescently labeled KIF1A.     

Does Solvent Influence the Ground-state Tautomeric Population of Hypericin?¶

Nuclear magnetic resonance measurements indicate that hypericin exists in the same "normal" tautomeric form irrespective of whether the solvent is dimethyl sulfoxide or tetrahydrofuran. This result is discussed in the context of previous experimental and theoretical work. It is concluded that solvent perturbations cannot induce tautomerization in hypericin.     

Figure of merit for near-velocity-matched traveling-wave modulators

We derive a relationship between the bandwidth and active length and a figure of merit for velocity- and near-velocity-matched lithium niobate traveling-wave electro-optic modulators. The figure of merit is given by the bandwidth per unit drive voltage squared and is independent of the length of the device. Alternatively, this figure of merit can be described by its inverse, which is proportional to the device's switching energy.     

Calculation of CWKB envelope in boson and fermion productions

We present the calculation of envelope of boson and of both low-and high-mass fermion production at the end of inflation when the coherently oscillating inflatons decay into bosons and fermions. We consider three different models of inflation and use CWKB technique to calculate the envelope to understand the structure of resonance band formation. We observe that though low-mass fermion production is not effective in preheating because of Pauli blocking, it is quite probable for high-mass fermion to take part in pre-heating.      

Thin film stress measurement by instrumented optical fibre displacement sensor

Residual stress can adversely affect the mechanical, electronic, optical and magnetic properties of thin films. This work describes a simple stress measurement instrument based on the bending beam method together with a sensitive non-contact fibre optical displacement sensor. The fibre optical displacement sensor is interfaced to a computer and a Labview programme enables film stress to be determined from changes in the radius of curvature of the film-substrate system. The stress measurement instrument was tested for two different kinds of thin film, hard amorphous carbon nitride (CN) and soft copper (Cu) films on silicon substrates deposited by RF magnetron sputtering. Residual stress developed in 500 nm thick CN thin films deposited at substrate temperatures in the range 50-550 °C was examined and it was found that stress in CN films decreased from 0.83 to 0.44 GPa compressive with increase of substrate temperature. Residual stress was found to be tensile (121 MPa) for Cu films of thickness 1500 nm deposited at room temperature.     

Study of photophysical properties of capped CdS nanocrystals

Here, we have examined the role of capping agent on the optical properties of CdS nanoparticles by steady-state and time-resolved photoluminescence (PL) spectroscopy. The estimated particles sizes are 3.45, 2.5 and 2.39 nm for uncapped, capped with silica (SiO₂) and thiosalicylic acid (TSA), respectively. The absorption and emission spectra show a clear blue shift to shorter wavelengths in presence of TSA- and SiO₂-capped nanoparticles. It is found that the average decay time 〈τ〉 are 6.24, 4.54 and 2.84 ns for uncapped, capped with SiO₂ and TSA nanoparticles, respectively. Our analysis suggests that the hole or the electron is trapped on thiol molecule of TSA or hydroxyl group of SiO₂, then radiative recombination of the electron and hole is delayed, resulting in strong quenching of PL efficiency.     

Oxidation of Dimethyl Sulfide in Air Using Electron-Beam Irradiation,and Enhancement of its Oxidation Via an MnO<Subscript>2</Subscript> Catalyst

The decomposition of dimethyl sulfide (DMS) at initial concentrations of 4.5–18.0 ppmv in air was studied under electron-beam (EB) irradiation. Doses to decompose 90% of input DMS were 2.5 kGy for 4.5 ppmv, 3.4 kGy for 10.6 ppmv, and 3.9 kGy for 18.0 ppmv. HCOOH, (CH₃)₂SO, and trace CH₃OH and (CH₃)₂SO₂ were produced as irradiation products in addition to CO₂ and CO. Application of an O₃ decomposition catalyst to an irradiated sample gas led to an enhancement in the oxidation of DMS and its products into CO₂ and the decomposition of O₃. For 10.6 ppmv DMS/air, the mineralization ratio increased from 41% via only EB irradiation to 100% via the combination treatment at 6.3 kGy. The yield of CO₂ to CO_x increased from 5.3 to 87.6% by combination with catalytic oxidation. This combination treatment enables the irradiation energy used to deodorize gas streams containing DMS to be reduced.     

Assessment of the Nature of Depolarization Current in Thermally Treated Kapton Polyimide

Pyrolysis of normally insulating aromatic polyimide is known to impart electrical conductivity to the polymer due to the formation of carbonized regions in an insulating matrix with a concomitant change in the polymer’s structural arrangement. The wholly pyrolyzed polyimide is potentially useful for specific applications in certain types of semiconductor devices because of the polyimide’s insulator/conductor transition which creates a barrier type conduction. Pyrolysis, however, degrades the required mechanical integrity of the polyimide for construction of such devices. In order to evaluate the fundamental aspects of barrier conduction by high voltage electron transfer from metal contact that can still produce measurable current in thermally treated non-pyrolyzed polyimide, the nature of depolarization in Kapton was assessed by the thermally stimulated depolarization current (TSDC) technique. The results show that thermal treatment of polyimide without pyrolysis and therefore without loss of mechanical integrity offers a viable means of steady electron conduction for semiconductor operation. This revised version was published online in July 2006 with corrections to the Cover Date.