Thermoactivated creep and stress relaxation in Cd + 0·08 at% Sn single crystals

The activation area of plastically deformed Cd + 0·08 at% Sn single crystals was determined from differential creep test and stress relaxation at temperatures 78 K, 200 K and 295 K. The activation areaA depends on the resolved shear stress, ,A ^{* –r} wherer is dependent on temperature and the testing method used. For temperatures above 0·3T _m recovery during stress relaxation should be considered.     

Transient absorption and laser output of YAG : Nd

YAG : Nd grown under 98% Ar 2% H₂ protective atmosphere free of nitrogen or hydrocarbons showed after UV irradiation broad absorption peaked at 1·9×10⁴ cm^–1 which disappeared relatively slowly at room temperature. It was more intensive in oxygen treated samples than in those annealed in hydrogsn. Transient absorption suppresses laser output by the increase of absorption at 0·94×10⁴ cm^–1 (1064 nm) and, particularly in CW mode, by the anomalous rod deformation. YAG : Nd containing Fe ions (2·10^–4 wt%) showed no transient absorption.     

Laser properties of YAG : Nd grown from the melt contained in molybdenum crucibles

YAG:Nd grown from the melt using resitance furnace and molybdenum crucibles were compared with those grown by conventional method using r.f. heating and iridium crucibles. The former were succesfully grown in 98% Ar + 2% H₂ protective a mosphere using an excess of Y₂O₃ in the melt and after it annealed in an oxidizing atmosphere followed by treatment in hydrogen to reach the material with minimum losses. Laser rods machined from such crystals, showed nearly the same properties as those prepared by conventional method.     

Eine kennzeichnende Eigenschaft der Zykel der Galileischen Ebene

Ohne Zusammenfassung     

Influence of the overall pressure on electrical conductivity of the amorphous semiconductor Ge15Te81S2As2

The experimental results obtained with the chalcogenide glass Ge₁₅Te₈₁S₂As₂ with imposed overall pressure up to 700 MPa are presented. The material exhibits the switching effect and the memory effect. It is shown that the overall pressure changes remarkably d.c. electrical conductivity of the amorphous semiconductor. It is assumed that the changes in conductivity are caused by changes in activation energy. The changes in activation energy within the range of considered pressures are, as follows from our measurements, E/p–10·95×10^–5 eV/MPa +p × 10·41 W 10^–7 eV/MPa². The assumption of the activation energy dependence on pressurep are confirmed also by measurements of dependence In vs. 1/T at various pressures.     

Non-destructive measurement of the mobility in semiconductors by means of the microwave Faraday effect

The paper describes the measurement of the electron mobility in semiconducting plates placed between two cylindrical antennas with diameterd–0·75 ₀ by means of the microwave Faraday effect. This system enables (i) to measure the Faraday rotation in semiconducting plates of arbitrary transverse dimensions, greater or at least equal to the diameter of dielectric antennas, (ii) to evaluate the unknown value of the charge carrier mobility from the measured rotation in an unbounded solid state plasma slab approximation. The measurement of the Faraday rotation in n-type Ge plates are reported. The comparison of the experimental data with the theory shows good agreement.     

Effect of the size of experimental channels of the lead slowing-down spectrometer SVZ-100 (Institute for Nuclear Research, Moscow) on the moderation constant

Lead slowing-down (LSD) spectrometers have a low energy resolution (about 30%), but their luminosity is 10³ to 10⁴ times higher than that of time-of-flight (TOF) spectrometers. A high luminosity of LSD spectrometers makes it possible to use them to measure neutron cross section for samples of mass about several micrograms. These features specify a niche for the application of LSD spectrometers in measuring neutron cross sections for elements hardly available in macroscopic amounts—in particular, for actinides. A mathematical simulation of the parameters of SVZ-100 LSD spectrometer of the Institute for Nuclear Research (INR, Moscow) is performed in the present study on the basis of the MCNPX code. It is found that the moderation constant, which is the main parameter of LSD spectrometers, is highly sensitive to the size and shape of detecting volumes in calculations and, hence, to the real size of experimental channels of the LSD spectrometer.     

Effectiveness and design of surface texturing for different lubrication regimes

The aim of the present research work was to investigate the possibilities of designing surface texturing for different lubrication regimes and to evaluate its effectiveness, especially under starved, boundary and mixed lubrication regimes. This was achieved by combining an experimental tribological investigation with a surface-roughness analysis, a 2D FEM simulation and fluid dynamic modelling. The tribological investigation under unidirectional and reciprocating sliding was focused on the effect of the laser-texturing parameters—including the dimple depth and size, the dimple area density and the contact size—on the coefficient of friction under different lubrication regimes, achieved by varying the sliding speed, the normal load and the lubricant viscosity.     

Oxygen incorporation in polyethylene implanted with 150 keV Sb+ ions

Samples of polyethylene (PE) loaded with carbon black up to 8 wt.% and implanted with 150 keV Sb⁺ ions to the doses from 2×10¹³–2×10¹⁵ cm^–2 were studied using standard Rutherford Back Scattering (RBS) technique. On the PE samples implanted to the doses above 2×10¹⁴ cm^–2, a considerable surface carbonization is observed. The measured parameters of the Sb depth profile are compared with theoretical TRIM estimations. The projected range is by 25% lower than the theoretical one and the range straggling is about twice of that predicted. The differences are explained by stepwise polymer degradation during the ion bombardment. Strong oxidation of the ion implanted polymers is also observed. The oxygen depth profiles from the sample surface up to the depth comparable with Sb⁺ ion range evolve from nearly uniform one for low ion doses to highly non-uniform one for doses above 1×10¹⁵ cm^–2. The total oxygen content in the sample surface layer 300 nm thick reaches a maximum for the doses of (1–2)×10¹⁴ cm^–2.On leave from Belorussian State University, 220050 Minsk, Belarus.The authors thank the member of electrostatic accelerator group at INP for help during RBS measurements. The work was partly (V.H. and J.K.) supported by the Internal Grant Agency of the Academy of Sciences of Czech Republic under the grant No. 14805 and by the Internal Grant Agency of the Ministry of Education of Czech Republic under the grant No. 1002 (V.., V.R., V.H. and J.K.). In the final stage, the work was also supported by the Grant Agency of Czech Republic under the grant No. 202/93/0121.