含氧膦结构的可溶性感光聚酰亚胺合成与表征

聚酰亚胺(PI)是一类综合性能优异的功能性材料,广泛应用于航天、航空及电子工业等领域[1].感光聚酰亚胺可以采用光刻工艺,大大简化了其应用加工程序[2,3],因而备受人们所青睐.含查尔酮结构的聚合物对UV辐射敏感度高和化学稳定性好,最近被广泛的研究和应用[4～7].主链含查尔酮结     

N-丙基-N-[2-(2,4,6-三氯苯氧基)乙基]-1H-咪唑-1-甲酰胺的合成

以2，4，6-三氯苯酚和1，2-二氯乙烷为初始原料，在相转移催化剂十六烷基三甲基溴化胺和弱碱性助剂三乙胺存在下合成了N-丙基-N-[2-(2，4，6-三氯苯氧基)乙基]-1H-咪唑-1-甲酰胺，其结构经元素分析,IR，^1H NMR分析证实。并对该合成路线的反应机理进行了讨论。     

高分子化学课程中若干论题的进展

高分子化学课程中下列五个论题被加以修正和补充:(1)1,2-二取代乙烯单体的聚合;(2)乙烯基单体聚合时的键连方式;(3)自由基聚合的自动加速;(4)引发转移和引发转移终止剂;(5)氢转移聚合和基因转移聚合。     

Y2O3, La2O3, Sm2O3对氧化铝瓷烧结及力学性能的影响

研究了3种稀土氧化物对氧化铝陶瓷烧结性能和力学性能的影响.结果表明 含Y2O3,La2O3,Sm2O3的添加剂促进了氧化铝瓷的烧结,提高了氧化铝瓷的力学性能.Y2O3和Sm2O3掺量为0.50%,La2O3掺量为0.75%时氧化铝瓷在1600或1620 ℃保温2 h烧结,相对密度达98.9%以上,强度超过439 MPa,断裂韧性达5.15 MPa·m1/2以上.微观结构分析表明,Y2O3,La2O3,Sm2O3抑止氧化铝晶粒生长,细化晶粒,使晶粒尺寸较均匀形成致密化结构.     

Luminescence of Eu~(2 ) in Strontium Aluminum Oxide System with Long Decay Property

Luminescentmaterialshavinglongdecayperi0dhaveat-IIactedmuchinterestduetotheirpotentialwidespreadaPplicati0ns.Recently,alongdecayluminescentp0wderhavingthecomPositionofSrAl2O4activatedwithEu' wasreportedandregardedasthebestcandidateforpracticalaPPlicationbecauseofitsuniqueadVantages0veritsprecursors.l'2Inthispaper,wereportthesynthesisofthelongdecayluminescentpowderandtheinnuence0fthemolarratioofAlt0sr0ntheethessioncolor.Toproducethelundnescentp0wder,amixtureofSrCO3,Al2O3,Eu2O3andsomesol…     

萘降解菌LHJ38生物合成靛蓝的研究

萘降解菌LHJ38在金属盐培养基中加入水杨酸钠诱导培养后能提高其生物合成靛蓝的能力,在LB培养基中加入水杨酸钠反而抑制了其生物合成靛蓝的能力.与LHJ38最适生长pH值不同,LHJ38生物合成靛蓝的最佳pH值范围是8.45—9.45,在pH为8.95的情况下生物合成靛蓝能力是其在pH值为6.95的情况下的两倍.     

PHOTOSENSITIVITY OF Ce (Ⅳ) INITIATED METHYL ACRYLATE POLYMERIZATION

The influences of UV light irradiation (313 nm) and diffused daylight on the polymerization of methyl acrylate initiated by the ceric ammonium nitrate without any reducing agent have been studied both in aqueous nitric acid and in pure water. The rate of polymerization was found to be accelerated and the overall activation energy and the induction time were found to be decreased sharply by the UV light irradiation. Under UV light, the rate of polymerization is 8 times as high as the rate in dark. The rate of polymerization was found to attain a maximum with the increase of nitric acid concentration and the rate of polymerization became less sensitive to UV light in the presence of nitric acid whereas the induction period reduced outstandingly. Based on the experimental results, the mechanism is proposed.     

氯代甲苯异构体双电荷离子电子捕获诱导解离谱研究

研究了４种Ｃ７Ｈ７Ｃｌ异构体在７０ｅＶ电子轰击下产生的［Ｃ７Ｈ７Ｃｌ］＾２＋、［Ｃ７Ｈ６Ｃｌ］＾２＋．和［Ｃ７Ｈ５Ｃｌ］＾２＋ ３种双电荷离子的电子捕获诱导解离（ＥＣＩＤ）反应。分子离子的ＥＣＩＤ反应明显的邻位效应，表明其结构仍保持中性分子的结构特征；而由各异构体产生的［Ｃ７Ｈ６Ｃｌ］＾２＋．和［Ｃ７Ｈ５Ｃｌ］＾２＋离子异构化成同一结构。３种双电荷离子ＥＣＩＤ反应的产物与离子所带电子的奇偶性有关，     

铈离子与氨基甲酸酯类化合物引发丙烯酰胺聚合的研究

本文对铈离子与苯基氨基甲酸酯类化合物在H_2O-CH_3CN(3∶1,V/V)及H_2O-HCONH_2(1∶2,V/V)两种介质中引发丙烯酰胺的聚合进行了研究。考察了不同结构的苯基氨基甲酸酯对聚合的影响。苯基氨基甲酸酯类化合物对铈离子引发聚合均有促进作用,其中对-甲苯基氨基甲酸酯的促进作用最为显著。测定了聚合反应表现活化能及聚合动力学方程,并提出了聚合反应机理。     

低能离子散射谱分析中的荷电效应及中和作用

用低能离子散射谱（ISS）对比分析了与样品托有良好电接触的和与样品托绝比的金属银片，观察到荷电效应对ISS分析有严重影响。实验还表明在ISS分析时使用低能电子中和枪可以有效地消除荷电效应，还发现电子中和枪的使用对于惰性气体离子的中和作用无明显影响。