Preparation and Properties of Aramid-Silica Hybrids with Inter-Phase Bonding Through (3-glycidoxypropyl)-trimethoxysilane

Nano-composites from aramid-silica system have been prepared via sol-gel process. Poly (phenyleneterephthalamide) copolymer chains were prepared by reacting a mixture of p- and m-phenylenediamines with terephthaloyl chloride in dimethylacetamide used as solvent. The sol-gel process in the polymer matrix was carried out through hydrolysis and condensation of a mixture of tetraethoxysilane and (3-glycidoxypropyl) trimethoxysilane. The latter was used to develop linkage, on one hand with silica network structure using alkoxy groups and on the other hand with aramid chains at its secondary amine groups through glycidal groups of silane. Mutual interaction between the two disparate phases aramid and silica network was thus created. Thin films of the composites containing different proportions of silica ranging from 5.0 to 25.0-wt% were cast by the solvent elution technique. The α-relaxation temperature associated with the glass transition was measured by the dynamic mechanical thermal analysis. The results showed an increase in the glass transition temperature from 328°C for the pure aramid to 352°C for the hybrid materials containing 25-wt% silica, an indicative of the increased interfacial interaction between the two phases. Films having relatively low silica content were flexible and transparent, but those with high silica content were opaque and brittle. These films were tested for their tensile strength, modulus and toughness. The mechanical strength of the composites as compared to the pure aramid increased initially but with further addition of silica the strength decreased. The initial increase can be explained due to increased interfacial interaction between the two phases, however agglomeration of silica particles was responsible for decreasing strength at higher silica contents.     

Synergistic effect of aluminum trihydrate and zirconium hydroxide nanoparticles on mechanical properties,flammability, and thermal degradation of polyester/jute fiber composite

Cellulose - This study focuses on the synergistic effects of hydroxide based nanoparticles namely aluminum trihydrate (ATH) and zirconium hydroxide (ZHO) on the mechanical characteristics, thermal...     

Lyciumaside and Lyciumate: A New Diacylglycoside and Sesquiterpene Lactone from Lycium shawii

One new diacylglycoside named lyciumaside ( 1 ) and a new sesquiterpene lactone named lyciumate ( 2 ) were isolated from Lycium shawii Roem . & Schult . The structures of the two new compounds were elucidated based on 1D‐ (¹H‐ and ¹³C‐NMR and NOE) and 2D‐NMR (COSY, HSQC, and HMBC) spectroscopic techniques, and mass spectrometry (ESI‐MS). Preliminary evaluations demonstrated lyciumaside ( 1 ) possesses strong antioxidant activity with an IC₅₀ = 30 μg/ml (80% inhibition) while it was inactive in α‐glucosidase and urease enzymes assays.     

Determination of bromide by low power surfatron microwave induced plasma after bromine continuous generation

A simple continuous flow generation of volatile bromine is described for the determination of low concentrations of the elements by atmospheric-pressure argon microwave induced plasma (MIP) surfatron. Bromine is continuously generated by mixing the bromide with sulphuric acid and hypochlorite solutions. The bromine vapor is separated from the aqueous phase by a gas-liquid separator and is desiccated by passing it through concentrated sulphuric acid. The detection limit attained was 2 microg/l. and the precision was +/-0.7% (at the 80 microg/l. level). The proposed determination is very selective if oxidizing/reducing agents are absent. The procedure has been tested for bromide determination in two drug preparations. Good agreement between the experimental results and the certified values has been obtained.     

One-pot synthesis of CoO–ZnO/rGO supported on Ni foam for high-performance hybrid supercapacitor with greatly enhanced cycling stability

The high specific capacitance along with good cycling stability are crucial for practical applications of supercapacitors,which always demands high-performance and stable electrode materials.In this work,we report a series of ternary composites of CoO-ZnO with different fractions of reduced graphene oxide(rGO) synthesized by in-situ growth on nickel foam,named as CZG-1,2 and 3,respectively.This sort of binder-free electrodes presents excellent electrochemical properties as well as large capacitance due to their low electrical resistance and high oxygen vacancies.Particularly,the sample of CZG-2(CoO-ZnO/rGO 20 mg) in a nanoreticular structure shows the best electrochemical performance with a maximum specific capacitance of 1951.8 F/g(216.9 mAh/g) at a current intensity of 1 A/g.The CZG-2-based hybrid supercapacitor delivers a high energy density up to 45.9 Wh/kg at a high power density of 800 W/kg,and kept the capacitance retention of 90.1% over 5000 charge-discharge cycles.     

Numerical study of forced convection heat transfer across a cylinder with various cross sections

Journal of Thermal Analysis and Calorimetry - The thermal performance of an isothermal horizontal cylinder with different selected cross sections in cross-flow was investigated numerically. These...     

Biomedical Applications of Scutellaria edelbergii Rech. f.: In Vitro and In Vivo Approach

In the current study, in vitro antimicrobial and antioxidant activities and in vivo anti-inflammatory and analgesic activities of Scutellaria edelbergii Rech. f. (crude extract and subfractions, i.e., n-hexane, ethyl acetate (EtOAc), chloroform, n-butanol (n-BuOH) and aqueous) were explored. Initially, extraction and fractionation of the selected medicinal plant were carried out, followed by phytochemical qualitative tests, which were mostly positive for all the extracts. EtOAc fraction possessed a significant amount of phenolic (79.2 ± 0.30 mg GAE/g) and flavonoid (84.0 ± 0.39 mg QE/g) content. The EtOAc fraction of S. edelbergii exhibited appreciable antibacterial activity against Gram-negative (Escherichia coli and Klebsiella pneumoniae) strains and significant zones of inhibition were observed against Gram-positive bacterial strains (Bacillus subtilis and Staphylococcus aureus). However, it was found inactive against Candida Albicans and Fusarium oxysporum fungal strains. The chloroform fraction was the most effective with an IC₅₀ value of 172 and 74 µg/mL against DPPH (1,1-Diphenyl-2-picryl-hydrazyl) and ABTS assays, in comparison with standard ascorbic acid 59 and 63 µg/mL, respectively. Moreover, the EtOAc fraction displayed significant in vivo anti-inflammatory activity (54%) using carrageenan-induced assay and significant (55%) in vivo analgesic activity using acetic acid-induced writing assay. In addition, nine known compounds, ursolic acid (UA), ovaul (OV), oleanolic acid (OA), β-sitosterol (BS), micromeric acid (MA), taraxasterol acetate (TA), 5,3′,4′-trihydroxy-7-methoxy flavone (FL-1), 5,7,4′-trihydroxy-6,3′-dimiethoxyflavone (FL-2) and 7-methoxy catechin (FL-3), were isolated from methanolic extract of S. edelbergii. These constituents have never been obtained from this source. The structures of all the isolated constituents were elucidated by spectroscopic means. In conclusion, the EtOAc fraction and all other fractions of S. edelbergii, in general, displayed a significant role as antibacterial, free radical scavenger, anti-inflammatory and analgesic agents which may be due to the presence of these constituents and other flavonoids.     

Tuning the properties of a black TiO2-Ag visible light photocatalyst produced by a rapid one-pot chemical reduction

A highly efficient black TiO₂-Ag photocatalytic nanocomposite, active under both UV and visible light illumination, was synthesized by decorating the surface of 25 nm TiO₂ particles with Ag nanoparticles. The material was obtained via a rapid, one-pot, simple (surfactant and complexing agent free) chemical reduction method using silver nitrate and formaldehyde as a metal salt and reducing agent, respectively. The nanocomposite shows an increase of over 800% in the rate of photocatalytic methylene blue dye degradation, compared to commercial unmodified TiO_2, under UV-VIS illumination. Unlike pure TiO₂, the nanocomposite exhibits visible light activation, with a corresponding drop in optical reflectance from 100% to less than 10%. The photocatalytic properties were shown to be strongly enhanced by post-reduction annealing heat treatments in air, which were observed to decrease, rather than coarsen, silver particle size, and increase particle distribution. This, accompanied by a variation in the silver surface oxidation states, appear to dramatically affect the photocatalytic efficiency under both UV and visible light. This highly active photocatalyst could have wide ranging applications in water and air pollution remediation and solar fuel production.     

Electronic and optical properties of quaternary selenides for optoelectronic applications: Insights from DFT+U-computations

The optical properties, electronic charge density, electronic structure of the new layered selenides materials, BaGdCuSe₃, CsUCuSe₃, CsZrCuSe₃, and CsGdZnSe₃ compounds have been calculated by using the full potential and linear augmented plane wave (FP-LAPW) methods as applied in the WIEN2k package, which is based on the density functional theory. The ALnMSe3 compound's structure of these was (A = Cs, Ba; Ln = Zr, Gd, U; M = Cu, Zn) is composed of (n = 1, 2) layers, which might be separated by A atoms. It is to be observed that there is strong hybridization between the s, p, and d states of Zr, Gd, and Cu atoms. Around the gadolinium atom, the charge density contours are completely circular, but the Gadolinium “Gd” atom shows an ionic nature. To calculate the refractive index, we used Kramer's Kronig correlations with the imaginary part dielectric function. The decrease in the refractive index is due to the lack of probability for direct excitation of the electrons, resulting in a loss of energy. The value of the static refractive index for all reference compounds is about 1.75–2.25, which is indication that the material used in optoelectronic devices.