Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

Viscosity,particle size distribution,and structural investigation of tetramethyloxysilane/2‐hydroxyethyl methacrylate sols during the sol–gel process with acid and base catalysts

The tetramethoxysilane (TMOS)/2‐hydroxylethyl methacrylate (HEMA) hybrid gels were synthesized with acid and base catalysts, via the in situ polymerization of HEMA, with and without the cosolvent methanol. With methanol in the TMOS/HEMA sol, the enhanced esterification and depolymerization reactions of the silanols resulted in a slower growth of silica particles. The silica particles that were synthesized with an acid catalyst were less than 40 nm. The thermal resistance of the poly(2‐hydroxyethyl methacrylate) (PHEMA) chains was enhanced by the addition of colloidal silica. The Fourier transform infrared characterizations and the exothermal peaks on the differential scanning calorimetry traces of these hybrid gels indicated chemical hybridization occurring as a result of condensation of the colloid silica and PHEMA at higher temperatures. Hence, the residual weight content of the hybrid gel after its synthesis with the base catalyst was even higher than the content of TMOS in the hybrid sol. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3476–3486, 2004     

Novel fixed‐site–carrier polyvinylamine membrane for carbon dioxide capture

Fixed‐site–carrier membranes were prepared for the facilitated transport of CO₂ by casting polyvinylamine (PVAm) on various supports, such as poly(ether sulfone) (PES), polyacrylonitrile (PAN), cellulose acetate (CA), and polysulfone (PSO). The cast PVAm on the support was crosslinked by various methods with glutaraldehyde, hydrochloric acid, sulfuric acid, and ammonium fluoride. Among the membranes tested, the PVAm cast on polysulfone and crosslinked by ammonium fluoride showed the highest selectivity of CO₂ over CH₄ (>1000). The permeance of CO₂ was then measured to be 0.014 m³ (STP)/(m² bar h) for a 20 μm thick membrane. The effect of the molecular weight of PVAm and feed pressure on the permeance was also investigated. The selectivity increased remarkably with increasing molecular weight and decreased slightly with increased pressure in the range of 1 to 4 bar. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4326–4336, 2004     

Pressure and temperature dependence of the gas‐transport properties of dense poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] membranes

The gas‐transport properties of poly[2,6‐toluene‐2,2‐bis(3,4‐dicarboxylphenyl)hexafluoropropane diimide] (6FDA‐2,6‐DAT) have been investigated. The sorption behavior of dense 6FDA‐2,6‐DAT membranes is well described by the dual‐mode sorption model and has certain relationships with the critical temperatures of the penetrants. The solubility coefficient decreases with an increase in either the pressure or temperature. The temperature dependence of the diffusivity coefficient increases with an increase in the penetrant size, as the order of the activation energy for the diffusion jump is CH₄ > N₂ > O₂ > CO₂. Also, the average diffusion coefficient increases with increasing pressure for all the gases tested. As a combined contribution from sorption and diffusion, permeability decreases with increases in the pressure and the kinetic diameter of the penetrant molecules. Even up to 32.7 atm, no plasticization phenomenon can be observed on flat dense 6FDA‐2,6‐DAT membranes from their permeability–pressure curves. However, just as for other gases, the absolute value of the heat of sorption of CO₂ decreases with increasing pressure at a low‐pressure range, but the trend changes when the feed pressure is greater than 10 atm. This implies that CO₂‐induced plasticization may occur and reduce the positive enthalpy required to create a site into which a penetrant can be sorbed. Therefore, a better diagnosis of the inherent threshold pressure for the plasticization of a glassy polymer membrane may involve examining the absolute value of the heat of sorption as a function of pressure and identifying the turning point at which the gradient of the absolute value of the heat of sorption against pressure turns from a negative value to a positive one. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 354–364, 2004     

Relationship between the dynamic softening transition and wet sliding friction of elastomer compounds

For properly chosen elastomer compounds, thermorheological characterization is combined with an examination of the variation of the wet sliding friction with temperature. A conceptual argument leads to the assumption that the wet sliding friction should maximize at the energy dissipation peak associated with the dynamic softening transition at a characteristic frequency determined by the sliding speed and the effective smallest surface asperity scale. The dynamic softening transition is characterized with the peak in tan δ/G′ⁿ, where tan δ is the loss tangent, G′ is the elastic modulus, and n is a constant between 0 and 1. The William–Landel–Ferry transform is uncritically applied for extrapolating the position of the peak in tan δ/G′ⁿ at high frequencies. Even based on the criterion of tan δ, the results obtained on a concrete surface indicate that the effective smallest asperity scale is of order of 100 μm. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2467–2478, 2004     

Differential scanning calorimetry and thermogravimetric analysis investigation of the thermal properties and degradation of some radiation‐grafted films and membranes

The influence of irradiation and grafting on the crystallinity of three base polymers has been investigated with differential scanning calorimetry. Grafting has the largest effect on the base polymer crystallinity and results in a reduction of the crystallinity. The thermal degradation of the base polymers and grafted films has been investigated with thermogravimetric analysis. The extent of the fluorination of the base polymer, the irradiation method, and the graft level all influence the thermal degradation and its activation energy. It is proposed that the variation of the chain lengths of the grafted polystyrene chains is actually a primary underlying factor responsible for the influence of these various parameters on the degradation process. The first results of a comparative thermal analysis of some fuel‐cell membranes are also presented, and the promise and shortcomings of this method are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2612–2624, 2004     

Estimation of kinetics parameters for the adsorption of human serum albumin onto hydroxyapatite-modified silver electrodes by piezoelectric quartz crystal impedance analysis.

The adsorption of human serum albumin onto hydroxyapatite-modified silver electrodes has been in situ investigated by utilizing the piezoelectric quartz crystal impedance technique. The changes of equivalent circuit parameters were used to interpret the adsorption process. A kinetic model of two consecutive steps was derived to describe the process and compared with a first-order kinetic model by using residual analysis. The experimental data of frequency shift fitted to the model and kinetics parameters, k1, k2, psi1, psi2 and qr, were obtained. All fitted results were in reasonable agreement with the corresponding experimental results. Two adsorption constants (7.19 kJ mol(-1) and 22.89 kJ mol(-1)) were calculated according to the Arrhenius formula.     

Nowhere zero 4‐flow in regular matroids

Jensen and Toft 8 conjectured that every 2‐edge‐connected graph without a K₅‐minor has a nowhere zero 4‐flow. Walton and Welsh 19 proved that if a coloopless regular matroid M does not have a minor in {M(K_3,3), M*(K₅)}, then M admits a nowhere zero 4‐flow. In this note, we prove that if a coloopless regular matroid M does not have a minor in {M(K₅), M*(K₅)}, then M admits a nowhere zero 4‐flow. Our result implies the Jensen and Toft conjecture. © 2005 Wiley Periodicals, Inc. J Graph Theory     

Efficient synthesis of an aldehyde‐capped polythiophene containing fluorinated electron‐withdrawing groups

To incorporate an acceptor type polythiophene segment onto a supramolecular block copolymer for potential light harvesting applications, effective synthetic routes for the end‐functionalized and acceptor‐substituted polythiophenes are critical. The Ullmann coupling reaction can be utilized to obtain electron‐deficient polythiophenes and to attach terminal thiophene units that carry functional groups. In this article, the reactions involving a 2,5‐dibromothiophene monomer containing an electron‐withdrawing fluorinated ester and 5‐bromo‐2‐thiophenecarboxaldehyde (the end‐capper) were studied in detail. It was found that the Ullmann coupling reaction of the dibromide is very fast (completed in a few minutes) and the terminal bromine group does not survive long under the reaction condition. These findings lead to the development of an effective procedure for aldehyde end‐capping of electron‐deficient polythiophenes. Polymers with molecular weights around 4000 Da are routinely obtained. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 41–47, 2007     

Stability control of the electrooptic effect with new maleimide copolymers containing photoreactive tricyanopyrrolidene‐based chromophores

New photocrosslinkable maleimide copolymers have been synthesized by the attachment of a tricyanopyrrolidene‐based chromophore. The 2‐(3‐cyano‐4‐(2‐{4‐[hexyl‐(6‐hydroxy‐hexyl)‐amino]‐phenyl}‐vinyl)‐5‐oxo‐1‐{4‐[4‐(3‐oxo‐3‐phenyl‐propenyl)‐ phenoxy]‐butyl}‐1,5‐dihydro‐pyrrol‐2‐ylidene)‐malononitrile chromophore exhibits nonlinear optical activity and contains a chalcone moiety that is sensitive to UV light (λ = 330–360 nm) for crosslink formation. The maleimide monomers have also been functionalized with chalcone moieties. The resultant copolymers exhibit great processability, and one of them shows a maximum electrooptic coefficient of 90 pm/V at 1300 nm. We could control the thermal stability of the electrooptic coefficient with the newly synthesized photoreactive copolymers successfully. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 531–542, 2007