FTIR spectroscopy study of CO adsorption on Pt-Na-mordenite

Different carbonyls are formed after CO adsorption at ambient temperature on a Pt-Na-mordenite (Pt-Na-MOR) sample. Pt(3+)(CO)(2) dicarbonyls (nu(s) at 2205 cm(-1) and nu(as) at 2167 cm(-1)) are decomposed without formation of monocarbonyls. The respective mixed-ligand species, Pt(3+)((12)CO)((13)CO), formed after (12)CO-(13)CO coadsorption, display bands at 2192 and 2131 cm(-1), in excellent agreement with the theoretically calculated values. Pt(2+)-CO species absorb at 2145 cm(-1) and are not able to accept a second CO molecule. Pt(+)-CO carbonyls are characterized by a band at 2111 cm(-1). Under CO equilibrium pressure, these species are converted into dicarbonyls (nu(s) at 2135 cm(-1) and nu(as) at 2101 cm(-1)). The respective mixed-ligand species, Pt(+)((12)CO)((13)CO), manifest bands at 2123 and 2069 cm(-1), in good agreement again with the theory. Different carbonyls of metallic platinum are observed below 2100 cm(-)(1). In addition, weakly adsorbed CO was registered as Na(+)-CO complexes (2177 and 2165 cm(-1)) and Na(+)-OC-Na(+) species (2138 cm(-1)). It was found that during desorption of CO platinum was reduced, ultimately to metal. However, heating in a NO + O(2) mixture leads to reoxidation of the metal particles and restoration of the initial state of the sample.     

Thermal analysis of polyaniline poly(N-vinylpyrrolidone)-stabilized dispersions

The polyaniline dispersions stabilized with poly(N-vinylpyrrolidone) (PANI/PVP) were synthesized by oxidative polymerization with different mass ratios of PANI and PVP and different molar concentrations of the components in the polymerization mixture. The composite powders prepared from colloidal PANI/PVP dispersions were characterized by thermogravimetry and differential thermal analysis. The change in the ratio of PANI and PVP as well as the starting molar concentrations of aniline hydrochloride and oxidant has influence on the resulting properties of the dispersions. Concerning the doping, the results show that PANI/PVP powders are stable up to approximately 160 °C. Degradation of polymer chains starts at temperatures above 250 °C. The PANI/PVP composite powders with lower content of PANI exhibit slightly higher thermal stability. Further, colloidal PANI/PVP dispersions were screen-printed on aluminum foil for infrared spectroscopic characterization and on poly(ethylene terephthalate) foil for electrical measurements. The sheet resistance of printed layers measured by two-point probe was of the order of tens to thousands of kΩ sq^?1. The influence of both the change in the composition and the drying temperature is discussed.     

Thermodynamic Properties of Polymorphs of Fluorosulfate Based Cathode Materials with Exchangeable Potassium Ions

FeSO₄F‐based frameworks have recently emerged as attractive candidates for alkali insertion electrodes. Mainly owing to their rich crystal chemistry, they offer a variety of new host structures with different electrochemical performances and physical properties. In this paper we report the thermodynamic stability of two such K‐based “FeSO₄F” host structures based on direct solution calorimetric measurements. KFeSO₄F has been reported to crystallize in two different polymorphic modifications—monoclinic and orthorhombic. The obtained enthalpies of formation from binary components (KF plus FeSO₄) are negative for both polymorphs, indicating that they are thermodynamically stable at room temperature, which is very promising for the future exploration of sulfate based cathode materials. Our measurements show that the low‐temperature monoclinic polymorph is enthalpically more stable than the orthorhombic phase by ≈10 kJ mol^?1, which is consistent with the preferential formation of monoclinic KFeSO₄F at low temperature. Furthermore, observed phase transformations and difficulties in the synthesis process can be explained based on the obtained calorimetric results. The KMnSO₄F orthorhombic phase is more stable than both polymorphs of KFeSO₄F.     

Alkoxyallene‐ynes: Selective Preparation of Bicyclo[5.3.0] Ring Systems Including a δ‐Alkoxy Cyclopentadienone

The development of an intramolecular rhodium(I)‐catalyzed Pauson–Khand reaction of alkoxyallene‐ynes with a proximal alkoxy group is reported. This reaction, in the presence of a [Rh(cycloocta‐1,5‐diene)Cl]₂/propane‐1,3‐diylbis(diphenylphosphane) system under a CO atmosphere, constitutes a powerful tool for selectively accessing carbo‐ and heterobicyclo[5.3.0] frameworks featuring an enol ether moiety. Through this procedure, a straightforward access to guaiane skeletons with a tertiary hydroxy group at the C10 position was achieved.