Effect of excess halide on the palladium‐catalyzed insertion‐triggered radical copolymerization of methyl acrylate and 1‐hexene

[Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) is a very efficient initiator of the radical polymerization of methyl acrylate, but it is not active in the polymerization of methyl methacrylate or in the copolymerization with 1‐hexene. The addition of an excess of NBu₄Cl to solutions of [Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) provides an initiator system that copolymerizes methyl acrylate and 1‐hexene by an insertion‐triggered radical mechanism. Random copolymers are obtained with 11% incorporation of 1‐hexene in moderate yields (about 35%). Studies of the decomposition products obtained after the first insertion of methyl acrylate in the Pd? C₆F₅ bond of 1 show that the addition of excess halide in the presence of monomer favors the homolytic cleavage of the Pd? C bond, and the generation of the radicals that are active species in the polymerization, versus alternative evolution pathways. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5682–5691, 2006     

Single electron transfer–degenerative chain transfer living radical polymerization of N‐butyl acrylate catalyzed by Na2S2O4 in water media

Living radical polymerization of n‐butyl acrylate was achieved by single electron transfer/degenerative‐chain transfer mediated living radical polymerization in water catalyzed by sodium dithionate. The plots of number–average molecular weight versus conversion and ln[M]₀/[M] versus time are linear, indicating a controlled polymerization. This methodology leads to the preparation of α,ω‐di(iodo) poly (butyl acrylate) (α,ω‐di(iodo)PBA) macroinitiators. The influence of polymerization degree ([monomer]/[initiator]), amount of catalyst, concentration of suspending agents and temperature were studied. The molecular weight distributions were determined using a combination of three detectors (TriSEC): right‐angle light scattering (RALLS), a differential viscometer (DV), and refractive index (RI). The methodology studied in this work represents a possible route to prepare well‐tailored macromolecules made of butyl acrylate in an environmental friendly reaction medium. Moreover, such materials can be subsequently functionalized leading to the formation of different block copolymers of composition ABA. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2809–2825, 2006     

Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF‐TrFE) were exposed to vacuum UV (115–300 nm VUV) and γ‐radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after γ‐irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV‐irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV‐irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d₃₃ piezoelectric coefficients and D‐E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D‐E loops after exposure to either γ‐ or VUV‐radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV‐irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV‐radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3253–3264, 2006     

Grafting of silica during the processing of silica‐filled SBR: Comparison between length and content of the silane

The treatment of nanoscopic silica grafted in the blend during the processing of silica‐filled styrene butadiene rubber was performed with silane, introduced at different concentrations, or at a constant concentration with a given length of alkyl chain. From swelling measurements in water and in solvent, the maximum silane content that can be grafted has been calculated as a function of the length of the silane alkyl chains as well as their efficiency to cover the silica surface. The found values are close to the values found in the literature for grafting in solution. Moreover, a direct correspondence between the length of the silane alkyl chains and their concentration has been deduced. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 143–152, 2006     

Encapsulation of ZnS:Mn2+ nanocrystals with diblock copolymers

The encapsulation of the nanocrystalline manganese‐doped zinc sulfide (ZnS:Mn) in poly(styrene‐b‐2vinylpyridine) (PS‐PVP) diblock copolymers is reported. Below the critical micelle concentration in the absence of nanocrystals (NCs), inverse micelles of PS‐PVP were induced by adding ZnS:Mn NCs, the presence of which was confirmed by scanning force microscope and dynamic light scattering. In toluene, a PS‐selective solvent, the less‐soluble PVP blocks preferentially surround the ligand‐coated ZnS:Mn NCs. For PS‐PVP encapsulated ZnS:Mn NCs, the ratio of blue emission to orange emission of ZnS:Mn NCs is dependent on both the concentration of PS‐PVP and the solvent quality. The pyridine of PVP blocks form complexes with the Zn atoms via the nitrogen lone pair and thus the sulfur vacancies are passivated. As a result, the defect‐related blue emission is selectively quenched even when the micelles are not formed. As the concentration of PS‐PVP encapsulating the ZnS:Mn NCs increases, the intensity of blue emission decreases. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3227–3233, 2006     

Acrylic acid level and adhesive performance and peel master‐curves of acrylic pressure‐sensitive adhesives

Three series of pressure‐sensitive adhesives were prepared with constant glass‐transition temperature, using emulsion polymerization. The monomers chosen were butyl acrylate, 2‐ethylhexyl acrylate (EHA), methyl methacrylate (MMA), and acrylic acid (AA). Within each polymer series, the proportion of AA monomer was held constant for each polymer preparation but acrylic ester monomer levels were varied. Adhesion performance was assessed by measurement of loop tack, static shear resistance, and through the construction of peel master‐curves. Peel master‐curves were generated through peel tests conducted over a range of temperatures and peel rates and through application of the time–temperature superposition principle. Bulk effects dominated by polymer zero shear viscosity change as AA and EHA levels were varied were attributed to the observed effect on static shear resistance and the horizontal displacements of peel master‐curves. Static shear resistance was found to strongly correlate with log(a_C), a parameter introduced to horizontally shift peel master‐curves to form a superposed, “super master‐curve”. An interfacial interaction was proposed to account for deviations observed when loop tack was correlated with log(a_C). Surface rearrangements via hydrogen bonding with the test substrate were suggested as responsible for the interfacial interaction. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1237–1252, 2006     

Metallocene copolymers of propene and 1‐hexene: The influence of the comonomer content and thermal history on the structure and mechanical properties

The relationships between the structure and properties have been established for copolymers of propylene and 1‐hexene synthesized with an isotactic metallocene catalyst system. The most important factor affecting the structure and properties of these copolymers is the comonomer content. The thermal treatment, that is, the rate of cooling from the melt, is also important. These factors affect the thermal properties, the degree of crystallinity, and therefore the structural parameters and the viscoelastic behavior. A slow cooling from the melt favors the formation of the γ phase instead of the α modification. Regarding the viscoelastic behavior, the β relaxation, associated with the glass‐transition temperature, is shifted to lower temperatures and its intensity is increased as the 1‐hexene content raises. The microhardness values are correlated with those of the storage modulus deduced from dynamic mechanical thermal analysis curves, and good linear relations have been obtained between these parameters. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1253–1267, 2006     

Determination of streptomycin in a pharmaceutical sample based on its degradation by hydrogen peroxide in the presence of copper(II).

The kinetics of streptomycin degradation by hydrogen peroxide at pH 7.4 was investigated. The reaction was catalyzed by traces of Cu(II) ions, and it was followed spectrophotometrically at 322 nm by applying the initial-rate method. The kinetic parameters of the reaction are reported, and a rate equation is suggested. From the dependence of the relative rate constants on the temperature, the activation energy was calculated to be 57.5 kJ/mol. Based on this reaction, a kinetic method for streptomycin determination is proposed. The calibration graph is linear in the ranges 1.94 - 15.48 microg/cm(3) and 0.15 - 1.94 microg/cm(3). The influence of foreign ions and molecules on the accuracy of the determinations was investigated. The proposed kinetic method has high selectivity and good sensitivity, and enabled to determine streptomycin in pharmaceutical samples.     

Minicolumn field sampling--preconcentration of trace zinc from seawater and its laboratory detection by flow injection flame atomic absorption spectrometry.

A simple field sampling-preconcentration method for zinc determination in seawater is described. Seawater was collected in situ by pumping it through a minicolumn packed with a chelating resin (Chelite P) connected to a field flow preconcentration system (FFPS). These packed minicolumns retain the dissolved zinc, and once are loaded with the analyte, they are returned to the laboratory where they are sequentially inserted into a flow injection system for on-line zinc elution with diluted hydrochloric acid and flame atomic absorption spectrometric detection. A factorial design has been used to optimize the FFPS and the flow injection elution process. The proposed method has a linear calibration range from 0.07 to at least 9.4 microg L(-1) of zinc, with a detection limit of 0.02 microg L(-1) and a throughput of 26 samples h(-1). Validation was carried out against certified reference water samples. This procedure has been successfully applied to the determination of Zn in seawater samples from Galicia (Spain).     

Solid-phase extraction on alkyl-bonded silica gels in inorganic analysis.

Solid-phase extraction (SPE) is an effective tool for the preconcentration of trace elements and their separation from various sample constituents. Octadecyl and other alkyl-bonded silica gels are most widely used for these purposes. The fundamentals of the SPE of inorganic ions are reviewed and compared with those of related techniques (liquid-liquid extraction and reversed-phase liquid chromatography). The extraction of ions in the form of chelate compounds, inorganic salts solvated by neutral reagents, and ion-pair compounds is considered. Numerous applications of SPE to the separation and preconcentration of different elements and their species, including on-line combinations with instrumental determination techniques, are described and tabulated.