Hybrid Electrodes Used in Polymer Electro-Optic Modulator with Ultra-Broadband

Hybrid electrode combined coplanar waveguide (CPW) and microstrip lines in ultra-broadband electro-optic modulators. The characteristics of the modulators with hybrid electrode is like that of the modulator with the microstrip lines, in which the microstrip electrode is loaded above only one arm of Mach-Zehnder (M-Z) optical waveguide, besides the problem of microstrip line to coaxial transition and corona polarization in polymer modulators have been best solved at the same time. By using finite element method (FEM), the characteristic parameters such as half-wave voltage, modulation bandwidth characteristic impedance, effective microwave refractive index of polymer modulators with microstrip line and hybrid electrode are analysed and compared in this paper. The results present that velocity match, impendence match and lower microwave propagating loss is easily realized in modulators with hybrid electrode.     

A stable dual-wavelength fiber laser with tunable wavelength spacing using a polarization-maintaining linear cavity

We propose and experimentally demonstrate a stable dual-wavelength erbium-doped polarization-maintaining (PM) fiber laser with tunable wavelength spacing using an all-PM linear cavity that makes use of two reflection peaks from the PM fiber Bragg grating (PM-FBG). Experimental results show stable dual lasing lines with a wavelength separation of ∼0.22 nm and a large optical signal-to-noise ratio (OSNR) of over 40 dB under room temperature. By applying axial strain to the PM-FBG, the center wavelengths of the two lasing lines can be tuned over several nanometers and the wavelength separation between the lasing lines can also be tuned to as small as 0.05 nm, which, to our knowledge, is the smallest wavelength spacing ever obtained from a stable room-temperature dual-wavelength fiber laser. The proposed laser configuration has the advantages of simple structure, low loss, stable dual-wavelength operation and a very small lasing linewidth of ∼5 kHz . PACS 42.55.Wd; 42.81.-i; 42.81.Gs     

Single to 16-Channel Wavelength Conversion at 10 Gb/s Based on Cross-Gain Modulation of ASE Spectrum in SOA

A simple scheme for single to multi-channel wavelength conversion based on cross-gain modulation of amplified spontaneous emission (ASE) spectrum in semiconductor optical amplifier (SOA) is described. Single to 16-channel wavelength conversion at 10 Gb/s is first demonstrated without any additional probe lights, the modulation information carried by input signal could be converted into arbitrary many channels if only the demultiplexer with enough channels is exploited. Output performance and pattern effects are investigated experimentally.     

Cu~+、Ag~+、Au~+与乙硫醇的气相化学反应

利用激光溅射 分子束的技术 ,结合反射飞行时间质谱计 ,研究了Cu+、Ag+、Au+与乙硫醇的气相化学反应。结果显示这三种金属离子与 (CH3 CH2 SH) n 反应形成一系列团簇离子M+(CH3 CH2 SH) n,且团簇离子尺寸不一样。Ag+、Au+与乙硫醇的反应还生成了 (CH3 CH2 SH) +n ,由此推测Cu+、Ag+、Au+与乙硫醇团簇的反应存在两种通道 ,一种通道是生成M+(CH3 CH2 SH) n,另一种是生成 (CH3 CH2 SH) +n 。Cu+、Au+与乙硫醇的反应还生成了M+(H2 S) (M =Cu、Au) ,但是实验中没有观察到Ag+(H2 S) ,理论计算表明Ag+(H2 S)很不稳定。另外 ,分析产物离子M+(CH3 CH2 SH) n 的强度发现 ,n =1～ 2之间存在明显的强度突变现象     

碳纳米管阵列、捆束的三步升温工艺制备及其形貌与结构

使用结构简单的单温炉设备，通过三步升温热解二茂铁、三聚氰氨混合物方法，在二氧化硅、多晶陶瓷基底上分别合成了碳纳米管阵列、碳纳米管捆束.使用扫描电子显微镜、透射电子显微镜、电子能量损失谱和x射线光电子能谱对合成样品进行了结构和成分分析.结果显示：两种基底上合成的纳米管均为多壁纯碳管；生长于光滑二氧化硅表面的碳纳米管具有高度取向性和一致的外径，长度为10—40μm.碳纳米管采取催化剂顶端生长模式并展示出类杯状形貌；生长于粗糙多晶陶瓷表面的碳纳米管捆束随机取向，碳纳米管直径为15—80nm，长度在几百微米，展示 关键词： 碳纳米管 热解法 三步升温工艺     

A method to collect an infrared spectrum in solution.

Herein we report a new method to collect a qualified infrared spectrum of a solute in solution by two solvent cells with different thickness during background single-beam spectrum scanning. By collecting the background spectrum with two cells (two stages), we successfully achieved accurate solvent compensation between a sample and a reference, namely, the solvent amounts in the sample and background measurements could become congruent. Therefore, the solvent bands were thoroughly suppressed in the infrared spectrum and a qualified spectrum of the solute was obtained.     

Mono-dispersed cross-linked polystyrene micro-spheres prepared by seed swelling polymerization method

A two-step swelling procedure was adopted to synthesize mono-dispersed and highly cross-linked poly (St-divinylbenzene) particles with PSt micro-spheres (1.80 μm in diameter). The PSt micro-spheres were prepared by a dispersion polymerization method and used as seeds. The effects of monomer concentration, ratio of ethanol to water, swelling reagents, crosslinking reagents, swelling temperature and agitation speed on particle size were investigated in detail. The morphologies and size distributions of these micro-spheres were examined by SEM and particle size analysis (PSA). The T _g of the micro-spheres was measured by DSC. The results indicate that the particles (6.20 μm in diameter) exhibit excellent mono dispersed property and high crosslinking degree when the concentration of the swelling reagent was 25%, the concentration of the crosslinking reagents was 23%, the swelling temperature was 30°C and the stirring speed was 150 r/min. __________ Translated from Chinese Journal of Applied Chemistry, 2007, 24(11): 1289–1294     

Buckling of a stiff thin film on a compliant substrate in large deformation

A finite-deformation theory is developed to study the mechanics of thin buckled films on compliant substrates. Perturbation analysis is performed for this highly nonlinear system to obtain the analytical solution. The results agree well with experiments and finite element analysis in wavelength and amplitude. In particular, it is found that the wavelength depends on the strain. Based on the accurate wavelength and amplitude, the membrane and peak strains in thin films, and stretchability and compressibility of the system are also obtained analytically.