Single- and multi-shot laser-induced damages of Ta_2O_5/SiO_2 dielectric mirrors at 1064 nm

Ta2O5/SiO2 dielectric mirrors deposited by ion beam sputtering (IBS) are studied. The multi-shot laserinduced damage threshold (LIDT) and its dependence on the number of shots are investigated, after which we find that the multi-shot LIDT is lower than that of single-shot. The accumulation effects of defects play an important role in the multi-shot laser damage. A simple model, which includes the conduction band electron production vsa multiphoton and impact ionizations, is presented to explain the experimental phenomena.     

Effect of surface nanocrystallization induced by fast multiple rotation rolling on hardness and corrosion behavior of 316L stainless steel

A nanostructured layer was fabricated by using fast multiple rotation rolling (FMRR) on the surface of 316L stainless steel. The microstructure in the surface was characterized by transmission electron microscopy and X-ray diffraction. The effects of FMRR on the microhardness, surface roughness and corrosion behavior of the stainless steel were investigated by microhardness measurements, surface roughness measurements, potentiodynamic polarization curves and pitting corrosion tests. The surface morphologies of pitting corrosion specimens were characterized by scanning electron microscopy. The results show that FMRR can cause surface nanocrystallization with the grain size ranges from 6 to 24 nm in the top surface layer of the sample. The microhardness of FMRR specimen in the top surface layer remarkably increases from 190 to 530 HV. However, the surface roughness slightly rises after FMRR treatment. The potentiodynamic polarization curves and pitting corrosion tests indicated that the FMRR treated 316L stainless steel with a surface nanocrystallized layer reduced the corrosion resistance in a 3.5% NaCl solution and enhanced the pitting corrosion rate in a FeCl₃ solution. Possible reasons leading to the decrease in corrosion resistance were discussed.     

Ultrawidely tunable single-mode fiber acousto-optic filter

A single-mode fiber (SMF) acousto-optic tunable filter (AOTF) with a tuning range of more than 300 nm is demonstrated. The SMF used in the experiment has a ring of symmetric holes within the cladding, which causes a larger mode-index difference between the first and the second higher-order antisymmetric modes than those of a conventional SMF. As a result, the difference in beatlengths between the core mode and the higher-order modes is highly increased, which makes it possible for the SMF AOTF to exhibit a single resonance peak in the transmission spectrum over the wavelength range of 1.3-1.6 μm for given acoustic frequencies of 3.1-3.8 MHz.     

Experimental realization of an approximate partial transpose for photonic two-qubit systems

We report the first experimental realization of an approximate partial transpose for photonic two-qubit systems. The proposed scheme is based on the local operation on single copies of quantum states and classical communication, and therefore can be easily applied for other quantum information tasks within current technologies. Direct detection of entanglement, i.e., without performing quantum state tomography, using the partial transpose operation, is also demonstrated.     

Radiation-induced changes in electrical conductivity and structure of BaPbO3 after γ-irradiation

Several barium plumbate (BaPbO₃) solid samples, made from PbO and BaCO₃ powder by chemistry liquid-phase coprecipitation, were investigated before and after γ-irradiation. The solid samples were irradiated by a ⁶⁰Co γ-irradiation source whose dose rate is about 0.7?kGy per hour. The irradiation times were 0, 72, 144, 216, 288 and 360?h. Then, the four-probe method, X-ray diffraction (XRD), scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) were used to indicate the changes in electrical conductivity and microstructure of BaPbO₃ after γ-irradiation. The XRD results indicated that the content of PbO was reduced as the irradiation dose was increased and eventually vanished from the surface of samples. However, there was no new obvious substance phase found from the XRD atlas. It seems that the PbO transformed into nearly amorphous Pb₅O₈. The conjecture could be proved by the results of annealing experiment and SEM. The XPS results seem to show that the microstructure of BaPbO₃ was slightly changed.     

Microstructural and mechanical analysis of Cu and Au interconnect on various bond pads

Effects of High Temperature Storage (HTS) and bonding toward microstructure change of intermetallic compound (IMC) at the wire bonding interface of 3 types of bond pad (Al, AlSiCu and NiPdAu) were presented in this paper. Optical and electron microscope analyses revealed that the IMC growth rate of samples under 175 and 200 °C HTS increased in the order of Al > AlSiCu > NiPdAu. Besides, higher HTS and bonding temperatures also promoted higher IMC thickness. The compositional study showed that higher HTS and bonding temperature developed rapid interdiffusion in bonding interface. In the mechanical ball shear test, a decrease of the shear force of Al and AlSiCu bond pads after 500 h HTS was believed due to poorly developed IMC at bonding interface. On the other hand, shear force degradation at 1000 h was due to excessive growth of IMC that in turn causes the formation of defects. For NiPdAu bond pad, increasing trend of shear force with HTS duration at 175 °C implied a good reliability of the Cu wire bonding. The rapid microscopic inspection on Cu wired Al bond pad under HTS 175 °C showed the IMC development from the periphery to the center of the ball bond. However, after 500 h voids started to develop until the crack was observed at 1000 h.     

Plasmonic effects in composite metal nanostructures for sensing applications

We have investigated numerically the plasmonic effect on a two-dimensional periodic array of metallic nanostructures. The unit cell of the array has an Ag nanosphere and nanorod pair formed in a single structure. Three-dimensional finite element method is used for the study on the sensing performance within the optical spectra. The study takes into account the influences of the structural and material parameters, the rotational angle of the metal nanostructure, the number of metal nanostructure per unit cell, and the localized surface plasmon resonances. The proposed nanostructures function as a refractive index sensor with a sensitivity of 400 nm/RIU (RIU is the refractive index unit), showing the characteristics of low transmittance (T?=?3.90%), high absorptance (A?=?94.5%), and near-zero reflectance (R?=?0.15%), could be achieved by a triangular arrangement of nanostructures within a unit cell. We also show how the tailoring of the structural parameters relates to the specific sensing schematics of the sensor.

Open image in new window

Graphical abstract x-y sectional plane of electric field intensity, electric force lines (pink lines), energy flows (green arrows) and surface charge density of type 2, corresponding to the surrounding testing medium of (a) n=1.00 and (b) n=1.33 around the PMNSs.

     

Slow electron acoustic double layer (SEADL) structures in bi-ion plasma with trapped electrons

The properties of ion acoustic double layer (IADL) structures in bi-ion plasma with electron trapping are investigated by using the quasi-potential analysis. The κ-distributed trapped electrons number density expression is truncated to some finite order of the electrostatic potential. By utilizing the reductive perturbation method, a modified Schamel equation which describes the evolution of the slow electron acoustic double layer (SEADL) with the modified speed due to the presence of bi-ion species is investigated. The Sagdeev-like potential has been derived which accounts for the effect of the electron trapping and superthermality in a bi-ion plasma. It is found that the superthermality index, the trapping efficiency of electrons, and ion to electron temperature ratio are the inhibiting parameters for the amplitude of the slow electron acoustic double layers (SEADLs). However, the enhanced population of the cold ions is found to play a supportive role for the low frequency DLs in bi-ion plasmas. The illustrations have been presented with the help of the bi-ion plasma parameters in the Earth's ionosphere F-region.     

Ar?NO团簇的同步辐射光电离研究

利用国家同步辐射实验室合肥光源的真空紫外同步辐射，使NO分子和Ar原子混合物的超声分子束发生光电离，测量了Ar，NO和异类团簇Ar·NO的光电离效率谱. 在谱中，在与Ar原子的共振线对应的能量区域(11.5—12.0 eV)观察到一个强的类共振结构. 这个结果表明，在异类团簇Ar·NO的内部，稀有气体Ar原子的激发能转移到与它接触的分子NO上，使分子NO发生电离. 关键词： Ar·NO团簇 同步辐射 光电离 能量转移     

纳米隧道结的量子电容现象

利用STM针尖和二维Au纳米团簇构造的双隧道结，通过对单电子隧穿谱的测量，研究了纳米隧道结的电容随隧道结宽度的变化，发现电容随结宽度的变化偏离了经典电容的行为，为纳米隧道结的量子电容效应提供了实验证据。