Synthesis and structural characterization of novel,fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties

The synthesis and structural characterization of a series of novel, fluorinated poly(phthalazinone ether)s containing perfluorophenylene moieties are described. The monomers, 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a – 2d ), were conveniently and efficiently synthesized from phenols and phthalic anhydride in two steps via 2‐(4′‐hydroxybenzoyl)benzoic acids, which were first obtained by the Friedel–Crafts reaction in good yields and with high stereoselectivity and were then converted into 2a – 2d by fusion with hydrazine. All the polymers were prepared by nucleophilic aromatic substitution (S_NAr) polycondensation between the compounds perfluorobiphenyl and 4‐(4′‐hydroxyaryl)phthalazin‐1(2H)‐ones ( 2a ‐ 2d ). The resulting fluorinated polymers were readily soluble in common organic solvents (e.g., CHCl₃, tetrahydrofuran, dimethylformamide, dimethyl sulfoxide, N‐methylpyrrolidone, etc.) at room temperature. Their weight‐average molecular weights and the polydispersities ranged from (7.96–18.25) × 10³ to 1.31–2.71, respectively. Their glass‐transition temperatures varied from 213 to 263 °C. They were all stable up to 390 °C both in air and in argon. The 5% weight‐loss temperatures of these polymers in air and argon ranged from 393–487 to 437–509 °C, respectively. Wide‐angle X‐ray diffraction studies indicated they were all amorphous and could be attributed to the presence of kink nonplanar moiety, phenyl phthalazinone along the polymer backbone. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 925–932, 2004     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Soluble,saturated‐red‐light‐emitting poly(p‐phenylenevinylene) containing triphenylamine units and cyano groups

A conjugated poly(p‐CN‐phenylenevinylene) (PCNPV) containing both electron‐donating triphenylamine units and electron‐withdrawing cyano groups was prepared via Knoevenagel condensation in a good yield. Gel permeation chromatography suggested that the soluble polymer had a very high weight‐average molecular weight of 309,000. A bright and saturated red emission was observed under UV excitation in solution and film. Cyclic voltammetry showed that the polymer presented quasi‐reversible oxidation with a relatively low potential because of the triphenylamine unit. A single‐layer indium tin oxide/PCNPV/Mg–Ag device emitted a bright red light (633 nm). © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3947–3953, 2004     

Completely biodegradable composites of poly(propylene carbonate) and short,lignocellulose fiber Hildegardia populifolia

The composites of biodegradable poly(propylene carbonate) (PPC) reinforced with short Hildegardia populifolia natural fiber were prepared by melt mixing followed by compression molding. The mechanical properties, thermal properties, and morphologies of the composites were studied via static and dynamic mechanical measurements, thermogravimetric analysis, and scanning electron microscopy (SEM) techniques, respectively. Static tensile tests showed that the stiffness and tensile strength of the composites increased with an increasing fiber content. However, the elongation at break and the energy to break decreased dramatically with the addition of short fiber. The relationship between the experimental results and the compatibility or interaction between the PPC matrix and fiber was correlated. SEM observations indicated good interfacial contact between the short fiber and PPC matrix. Thermogravimetric analysis revealed that the introduction of short Hildegardia populifolia fiber led to a slightly improved thermooxidative stability of PPC. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 666–675, 2004     

The effect of compatibilization and rheological properties of polystyrene and poly(dimethylsiloxane) on phase structure of polystyrene/poly(dimethylsiloxane) blends

The compatibilization effect of polystyrene (PS)‐poly(dimethylsiloxane) (PDMS) diblock copolymer (PS‐b‐PDMS) and the effect of rheological properties of PS and PDMS on phase structure of PS/PDMS blends were investigated using a selective extraction technique and scanning electron microscopy (SEM). The dual‐phase continuity of PS/PDMS blends takes place in a wide composition range. The formation and the onset of a cocontinuous phase structure largely depend on blend composition, viscosity ratio of the constituent components, and addition of diblock copolymers. The width of the concentration region of the cocontinuous structure is narrowed with increasing the viscosity ratio of the blends and in the presence of the small amount diblock copolymers. Quiescent annealing shifts the onset values of continuity. The experimental results are compared with the volume fraction of phase inversion calculated with various theoretical models, but none of the models can account quantitatively for the observed data. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 898–913, 2004     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

Time-resolved chemiluminescence technique for the microdetermination of proteins based on their complexation with copper(II).

Based on the complexation between proteins and Cu(II) coupled with the time-resolved chemiluminescence (CL) technique, a highly sensitive and quantitative assay for measuring proteins in solution is described. The complexes of proteins with Cu(II) have a strongly catalytic effect on the luminol-H2O2 CL reaction. Because the CL emission produced by the complexes is much more long-lived than that by Cu(II), the CL signals originating from proteins can be easily identified and measured with a time-resolved technique. On this basis, bovine albumin fraction V (BAF V) can be quantitatively determined in the range of 0.01 - 5.0 microg/ml with a detection limit of 5.8 ng/ml. The results show that the proposed assay exhibits a small variation in the response values for the same amount of different proteins, as compared to the Lowry as well as Bradford assays. The CL assay has also been studied for the detection of immobilized proteins.     

Differential pulse anodic stripping voltammetric determination of traces of copper with a tobramycin-Nafion modified electrode.

A Nafion-modified glassy carbon electrode incorporated with tobramycin for the voltammetric stripping determination of Cu2+ has been explored. The electrode was fabricated by tobramycin containing Nafion on the glassy carbon electrode surface. The modified electrode exhibited a significantly increased sensitivity and selectivity for Cu2+ compared with a bare glassy carbon electrode and the Nafion modified electrode. Cu2+ was accumulated in HAc-NaAc buffer (pH 4.6) at a potential of -0.6 V (vs. SCE) for 300 s and then determined by differential pulse anodic stripping voltammetry. The effects of various parameters, such as the mass of Nafion, the concentration of tobramycin, the pH of the medium, the accumulation potential, the accumulation time and the scan rate, were investigated. Under the optimum conditions, a linear calibration graph was obtained in the concentration range of 1.0 x 10(-9) to 5.0 x 10(-7) mol l(-1) with a correlation coefficient of 0.9971. The relative standard deviations for eight successive determinations were 4.3 and 2.9% for 1.0 x 10(-8) and 2.0 x 10(-7) mol l(-1) Cu2+, respectively. The detection limit (three times signal to noise) was 5.0 x 10(-10) mol l(-1). A study of interfering substances was also performed, and the method was applied to the direct determination of copper in water samples, and also in analytical reagent-grade salts with satisfactory results.     

A Quantum Chemical Study on Recognition of Nitro-phenols by Calix[n]arenes

A PM3 calculation in vacuum of the inclusion complexation ofo-, m-, p-nitro-phenol with calix[n]arenes is performedsuccessfully. The pathways for inclusion process are describedand the most probable structures of the 1:1 complex are soughtthrough a potential energy scan. The energy differences betweenthe inclusion complexes and the hosts, by calculation, show thatthe most stable complexation is calix[4]-p-nitro phenol andcalix[6]-m-nitro phenol.     

Structure of a poly(2,5‐benzimidazole)/phosphoric acid complex

As‐cast films of poly(2,5‐benzimidazole) exhibit uniplanar orientation in which the planes of the aromatic rings lie parallel to the film surface. Upon doping with phosphoric acid, the original crystalline order is lost, but the doped film can be stretched to produce films with uniaxial orientation. After thermal annealing at 540 °C, nine Bragg reflections are resolved in the fiber diagram, and these are indexed by an orthorhombic unit cell with the dimensions a = 18.1 Å, b = 3.5 Å, and c = 11.4 Å, containing four monomer units of two chains. The absence of odd‐order 00l reflections points to a 2₁ chain conformation, which is probably planar so that the aromatic units can be stacked along the b axis. The water and phosphoric acid contents of the crystalline structure cannot be determined exactly because of the presence of extensive amorphous regions that probably have different solvation. The best agreement between the observed and calculated intensities is for an idealized structure containing two phosphoric acids and two water molecules per unit cell. However, the phosphoric acid is probably present mainly in the form of pyrophosphoric acid and its higher oligomers. In addition, the X‐ray data are consistent with a more disordered structure containing chains with random (up and down) polarity and a lack of c‐axis registry. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 2576–2585, 2004