聚苯基单醚喹噁啉薄膜的性能与物理老化

研究了物理老化对聚苯基单醚喹啉薄膜的结构与力学性能的影响 .用差示扫描量热计 (DSC)及正电子湮没寿命谱 (PALS)方法表征了两种不同物理老化条件试样的凝聚结构以及自由体积的差别 .结果表明 ,物理老化使聚苯基单醚喹啉薄膜玻璃化转变温度移向高温 ,在其末端出现热焓吸收峰 ,分子链堆砌紧密使自由体积减小 ,分子可动性降低 .用动态力学分析 (DMTA)以及静态拉伸性能测试等方法研究了两类试样的力学性能 ,结果表明 ,物理老化后 ,试样的动态储能模量稍有增加 ,力学损耗降低 .而静态拉伸实验的断裂应变降低 ,屈服应力增加 ,断裂能降低 ,试样在宏观上由韧性断裂变为明显的脆性断裂 .     

激光核聚变中的一种X光解谱方法

本文在SAND迭代法的基础上,采取带有周期性光滑化的限幅迭代方法,求解激光核聚变中的X光能谱取得了较好的结果。这个方法适用于根据亚千X射线谱仪、多道k边滤波谱仪和多道滤波-荧光谱仪的测量结果回推靶等离子体的X射线能谱。计算结果表明,该方法完全抑制了数值不稳定性,消除了非物理的“负能谱”现象和解谱结果中的数值结构。特别是该方法对初始试探谱有很强的适应性,解谱计算结果与初始试探谱无关。     

Ligand Exchange Between Penta-Coordinated Phosphoryl Serine and Histidine Compounds

With the assistance of HPLC-ESI-MS/MS, the self-assembly products of serine and histidine penta-coordinated phosphorus compound were separated and identified. The expectative product was seryl-histidine dipeptide, but it was found that there was almost equimolar amount of histidyl-histidine dipeptide as well as seryl-histidine dipeptide. The mechanism was speculated that there was iigand exchange between penta-coordinated phosphoryl serine and histidine in the reaction process. As a result,two types of dipeptide were produced.     

低热-高压法制备PLGA多孔支架及其体外降解研究

采用低热-高压法制备了聚(dl-丙交酯／乙交酯)75／25(PLGA75／25)组织工程多孔支架。该方法避免了使用有机溶剂，支架的孔隙率在90％以上，孔径大小分布均匀。多孔支架经过酒精处理后，支架表面产生许多微小的凹陷；用藻酸钙改性处理后，支架形态保持良好。两种处理都使支架的压缩强度有所增大，亲水性增强。虽然孔隙率高的支架降解速率稍慢，但其体外降解规律基本一致：特性粘数争力学强度衰减快，而质量损失较慢，降解6周后，支架的质量损失仅为3％左右；体外降解3周后，支架的形态保持良好，可望在细胞移植争组织修复的早期发挥支撑作用。     

长链烷基苯异构体的气相色谱研究

长链烷基苯异构体的分离分析是石油化学中一个重要课题,曾有较多作者用气相色谱方法研究了长链烷基苯的分离及不同碳数的     

SYNTHESIS AND CATALYTIC PROPERTY OF POLYSTYRENE SUPPORTED PHENYLALANINE SCHIFF BASE COMPLEX OF Mn（Ⅱ） IN AEROBIC OXIDATION OF CYCLOHEXENE

The polystyrene supported phenylalanine Schiff base complex of Mn(Ⅱ)(PS-Sal-Phe-Mn)was prepared with chloromethylated styrene polymer beads, 2,4-dihydroxybenzaldehyde,L-phenylalanine and manganese(Ⅱ)acetate tetrahyrate., The polymeric ligand and the complex were characterized by FT-IR,, small area X-ray photoelectron spectroscopy(XPS), and ICP-AES. In the presence of the manganese complex, cyclohexene(1)was effectively oxidized by molecular oxygen without reductant. The major products of the reaction were 2-cyclohexen-1-ol(2),2-cyclohexen-1-one(3)and 2-cyclohexen-1- hydroperoxide(4), which was different with typical oxidation of cyclohexene. The influence of reaction temperature and additive for oxidation had been studied. The selectivity of 2-cyclohexen-l-hydroperoxide varied with reaction time and different additives. The mechanism of cyclohexene oxidation had also been discussed.     

物理老化对聚苯基单醚喹啉薄膜银纹化的影响

物理老化实质上是聚合物材料在 Tg 以下存放过程中 ,其凝聚态结构通过链段或更小运动单元的运动 ,从热力学非平衡态向平衡态过渡的一个结构弛豫过程[1] .在这一过程中 ,聚合物的密度、自由体积、焓、熵和力学性质随温度和时间产生变化 .因为银纹化是聚合物的特性 ,所以银纹化也将随结构回复过程而产生变化 .有关物理老化对聚合物银纹化的影响尚未得出一致的结论 [2～ 4 ] .聚苯基单醚喹啉 (结构见 Scheme1 )是一种高性能的芳杂环聚合物 [5] ,它可以在比较苛刻的条件下作为绝缘材料和膜材料使用 .有关这类高性能的芳杂环聚合物的物理老化…     

受限于纳米碳管中的乙醇分子的结构和扩散的分子模拟研究

利用分子模拟研究了常温常压下受限于(8,8) (管径1.081 nm)和(15,15) (管径 2.035 nm)单壁纳米碳管中的乙醇分子. 对受限分子的径向密度分布和氢键等静态性质以及扩散性质进行了分析. 结果显示在管内乙醇分子的平均氢键数目和主体相一致. 乙醇分子在(8,8)碳管内具有高度有序的结构, 而在(15,15)碳管内由于空间的增大导致结构有序度的降低, 其中分子取向已呈随机分布. 进一步对扩散系数的分析发现, 在管内乙醇分子的轴向扩散系数低于主体相, 特别在(8,8)碳管内乙醇分子几乎丧失了轴向扩散能力.     

全反式维甲酸合钇(Ⅲ)配合物对DNA的切割和键合作用(英)

以紫外光谱、荧光光谱、粘度法和凝胶电泳方法研究了全反式维甲酸合钇(Ⅲ)配合物与DNA的作用。结果表明，该配合物能在生理条件下比配体和金属离子更有效地切割质粒DNA，体系离子强度和pH值的变化对配合物的切割活性有较大影响，自由基捕捉剂的加入不影响配合物的切割活性。该配合物对DNA的切割可能通过水解机理进行。该配合物可使DNA的粘度增加，使EB-DNA体系的荧光强度和DNA溶液的紫外吸收强度降低。据此推断，该配合物主要以嵌入方式与DNA作用。     

β-环糊精在TiO2上的吸附及其对光催化影响研究

用酚酞法测定TiO2悬浮液中β-环糊精(β-CD)的量以及用β-CD溶液平衡的TiO2经过滤、洗涤和干燥后进行漫反射红外光谱和XPS能谱表征．结果表明：β-CD分别在纳米和P25型TiO2表面通过羟基间作用形成化学吸附，吸附量与溶液pH值有关，且最大吸附量在TiO2等电点附近．β-CD可提高两种TiO2对甲基橙光催化脱色速率.提高的效率与溶液pH值有关．实质上，提高的效率与β-CD在TiO2表面吸附量和甲基橙在TiO2表面的静电吸附量有关，即与甲基橙-β-CD—TiO2三元间的相互作用有关。