用化学溶液方法在Ni-5at%W基底上制备La2Zr2O7过渡层的研究

La2Zr2O7(LZO)过渡层以其独特的物理化学性质越来越受到人们的关注。本文以乙酰丙酮镧和乙酰丙酮锆为前驱盐,丙酸为溶剂配置前驱液,用化学溶液方法(CSD)在具有立方织构的Ni-5at%W基底上制备了LZO过渡层薄膜。研究了前驱液成分、性质以及退火温度对LZO成相以及取向的影响。用常规XRD和X射线四环衍射仪分析了LZO薄膜的相成分和织构。结果显示,在1050℃下退火可以获得强立方织构的LZO薄膜,其中(222)峰的Phi扫描半高宽值为8.95°;(400)峰的Chi扫描半高宽值为6.8°。用高分辨扫描电子显微镜(FE-SEM)观察到LZO薄膜表面均匀致密,没有裂纹和空洞。     

Synthesis and Herbicidal Activity of Novel Sulfonylureas Containing Thiadiazol Moiety

Thirteen novel sulfonylureas containing thiadiazole moiety were synthesized in a two-step reaction. Their structures were determined using IR, ^1H NMR, HRFTMS, and elemental analysis. Herbicidal activities of these compounds were determined in the green house bio-assay. The results show that four compounds among them exhibit some activity toward four tested herbs.     

Decomposition Reaction of Zn-MPA（3-Mercaptopropionic Acid） Complex Under Microwave Irradiation

The thermal decomposition of Zn-MPA complex was investigated under microwave irradiation. ZnO and ZnS nanocrystals could be obtained by decomposing Zn-MPA（3-mercaptopropionic acid） complex under different reaction conditions. It was found that both the pH value of the solution and the molar ratio of Zn2＋ and MPA can play an important role in the formation of ZnO and ZnS nanocrystals. MPA mainly acts as an S source or as a complexing agent. This study provides a new route for the controllable preparation of semiconductor nanocrystals.     

Tailoring Pore Structure and Morphologies in Covalent Organic Frameworks for Xe/Kr Capture and Separation

As a rising star among porous solid materials, covalent organic frameworks(COFs) with excellent properties including but not limit to facilely controllable structure, high porosity, and multi-chemical functionality represent significant potential for efficient ¹²⁷Xe/⁸⁵Kr capture and separation. In this study, through tuning the length of the organic ligands, two-dimensional(2D) COF mate-rials with identical connection group but different pore properties, denoted as ATFG-COF and TpPa-COF with AA-stacking model and TpBD-COF with AB-stacking model were synthesized and tested for Kr and Xe adsorption for the first time. Adsorption measurements indicate that the narrower pore apertures and higher porosity are conducive for COF materials to capture Xe and Kr. Furthermore, the Henry's constant, isosteric heat of adsorption(Q_st), and ideal adsorbed solution theory(IAST) selectivity of ATFG-COF, the pore size of which is closest to the kinetic diameter of the Xe atom(0.41 nm) among 2D COF materials, were carried out based on the single component sorption isotherms. The results illustrate that the high isosteric heat values of Xe/Kr adsorption on ATFG-COF are 25 and 16 kJ/mol at room temperature, respectively. Henry's law predicts that the selectivity factor of Xe to Kr is 6.07, consistent with the adsorption selectivity(ca. 6) calculated based on the IAST.     

嵌段共聚物自组装的研究进展

嵌段共聚物自组装在光学、电子、信息、化学及生物领域有着广泛的应用前景.本文从实验观测、理论研究和计算机模拟三个方面概述了嵌段共聚物自组装领域的研究进展.在实验观测方面,着重介绍了嵌段共聚物在体相及膜中的自组装及外场调控作用方面的研究进展;理论方面则分别介绍了强分相理论、弱分相理论、自洽场理论、动态密度泛函方法和元胞动力学等在嵌段共聚物自组装领域的应用;计算机模拟方面就 Monte Carlo 模拟、耗散粒子动力学等方法在该领域的应用作了详细的阐述.     

江西九连山常绿阔叶林的物种多样性分析

基于线路调查和样方调查的基础上,研究了江西九连山国家级自然保护区内常绿阔叶林的主要植被群落的α多样性和β多样性,α多样性测度指标主要采用Patrick丰富度指数、Shannon-wiener多样性指数、Simpson优势度指数、Pielou均匀度指数和Margalef丰富度指数等5个指标,β多样性采     

ZnO本征缺陷的第一性原理计算

采用基于密度泛函理论的第一性原理赝势法对ZnO本征缺陷的几何结构、杂质形成能和电子结构进行了比较系统的研究。研究表明,OZn、Oi和VZn以受主的形式存在;ZnO和Zni以施主的形式存在。其中,Zni的形成能最小,因此Zni的存在正是未掺杂ZnO是n型半导体的原因。计算结果与其它研究者     

虾肝肠胞虫感染病理特征、18S rRNA基因序列及系统进化树分析

为调查浙江省部分地区虾肝肠胞虫(Enterocytozoon hepatopenaei,EHP)暴发来源及与其他宿主来源的微孢子虫进化关系,本研究利用形态学特征和分子鉴定,尝试对引起浙江多地凡纳对虾生长缓慢综合征的病原进行探究.同时基于18S rRNA基因序列分析该病原与其他地区及其他宿主来源微孢子虫的进化关系.结果显...     

发动机机油滤清器虑层强度分析及优化

针对机油滤清器工作工况下进出口压差、机油滤层强度及导流桩高度等问题, 通过试验测试与仿真相结合, 对滤清器初步设计进行了评估及优化, 以确保滤清器在工作工况下进出口压降及滤层强度能满足要求. 首先进行滤层性能试验, 得到滤层的惯性阻力系数和黏性阻力系数; 再通过滤层多孔介质CFD分析, 对滤清器进出口压降进行分析计算. 结果表明: 在-18℃、25℃和70℃的工况下, 进出口压降都小于10kPa, 满足相关要求. 针对滤层的最大主应力超过其抗拉强度的问题, 通过CAE仿真分析, 优化滤层与导流桩间隙, 将滤层最大主应力由110.1MPa降至36.99MPa, 小于其抗拉强度42.8MPa.     

电场的增强作用对介质膜光栅损伤形貌的影响

研究了电场在介质膜光栅结构中的增强效应对其抗激光损伤阈值的影响.使用傅里叶模式方法计算了电场在介质膜光栅浮雕结构内的分布.数值分析表明：电场在介质膜光栅中增强的最大值为入射光的2倍,其最大的位置出现在相对于入射光对面的光栅槽侧壁。实验测试介质膜光栅样品在1 064 nm和12 ns, 51.2°和TE偏振光入射时,其抗激光损伤阈值为6.61 J/cm2.对损伤形貌进行扫描电镜精确分析,发现介质膜光栅的初始损伤产生于电场在介质膜光栅内增强最大的位置处.