Low-phosporous nickel-coated carbon microcoils: Controlling microstructure through an electroless plating process

Carbon microcoils (CMCs) have been coated with a nickel-phosphorus (Ni-P) film using an electroless plating process, with sodium hypophosphite as a reducing agent in an alkaline bath. CMC composites have potential applications as microwave absorption materials. The morphology, elemental composition and phases in the coating layer of the CMCs and Ni-coated CMCs were investigated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), respectively. The effects of process parameters such as pH, temperature and coating time of the plating bath on the phosphorus content and deposition rate of the electroless Ni-P coating were studied. The results revealed that a continuous, uniform and low-phosphorous nickel coating was deposited on the surface of the CMCs for 20 min at pH 9.0, plating bath temperature 70 °C. The as-deposited coatings with approximately 4.5 wt.% phosphorus were found to consist of a mix of nano- and microcrystalline phases. The mean particle size of Ni-P nanoparticles on the outer surface of the CMCs was around 11.9 nm. The deposition rate was found to moderately increase with increasing pH, whereas, the phosphorous content of the deposit exhibited a significant decrease. Moreover, the material of the coating underwent a phase transition between an amorphous and a crystalline structure. The thickness of the deposit and the deposition rate may be controlled through careful variation of the coating time and plating bath temperature.     

Synthesis and inclusion properties of pillar[n]arenes

A detailed study of the reaction conditions revealed that a quantitative cyclocondensation of 1,4-dialkoxy-2,5-bis(alkoxymethyl)-benzenes to pillar[n]arenes can be achieved by catalysis of p-toluenesulfonic acid in CH₂Cl₂. Major product of this new reaction is in each case a cyclopentamer (n = 5), but small amounts of the pillar[n]arenes with n = 6, 7 and 10 can be obtained as well. Different alkoxy groups in 1- and 4-position lead to regioisomers. All cyclooligomers exist in pillar structures as pair of enantiomers, which show a racemisation at room temperature, which is fast in terms of the NMR time scale. The racemisation process occurs by rotation of the 1,4-phenylene segments in the macrocyclic rings. Pillar[n]arenes exhibit novel host–guest behavior.     

可控表面磷原子修饰提升超细W2C纳米颗粒电解水析氢反应性能

研究高活性和稳定性的非贵金属基析氢催化剂对解决当前能源危机和环境污染问题具有重要意义.碳化钨具有与贵金属Pt类似的d带电子结构,因而成为一类新兴的非贵金属析氢催化剂,受到广泛关注.磷掺杂是提高催化剂析氢活性的有效方法之一,然而目前最常见的构筑磷掺杂方法是使用多金属氧酸盐(POMs,如H3PW12O40),其固定的W/P原子比导致W2C中的掺杂浓度难以调控,并且磷掺杂主要是进入碳载体而不是碳化物本身,从而导致无法明确杂原子对其电催化析氢活性的贡献.本文采用植酸(PA)为磷源设计合成了可控磷掺杂W2C纳米颗粒,并探讨了催化剂组分、杂原子掺杂位置与析氢性能之间的关系.深入研究了磷掺杂碳化钨(WCP)的化学结构和析氢活性.与原始的W2C催化剂相比,WCP具有更高的本征活性、更快的电子转移速率和更多的活性位数量,并且在酸性和碱性条件下均表现出较好的析氢性能.特别是过电位为-200 mV时,WCP催化剂的本征活性在酸性和碱性条件下分别为0.07和0.56 H2 s-1,高出纯W2C(0.01和0.05 H2 S-1)数倍.同时,在电流密度为-10 mA cm-2时,优化后的WCP催化剂在酸性和碱性条件下的析氢过电位分别降低了96和88 mV.XPS及EDS元素分析结果表明,随磷源添加量增加,磷掺杂从碳化钨表面逐渐向内部扩散,进一步说明磷取代位置与析氢活性之间的构效关系,高浓度的表面磷取代可以加速质子捕获过程,从而显著提高其析氢活性,而过量的内部磷取代会破坏W2C结构,降低电子转移速率,从而导致析氢性能下降.利用密度泛函理论计算深入研究了WCP具有较好析氢性能的原因,与内部磷取代相比,表面磷取代会使碳化钨表现出更合适的氢吸附自由能,并且更加有效地降低了氢释放势垒,从而优化了析氢反应动力学.综上,本文为元素掺杂工艺提供了新的思路,同时研究了表面异质原子对析氢活性的关键作用,为该类催化材料的构效关系研究提供了新思路.     

Improving the performance of all-solid-state supercapacitors by modifying ionic liquid gel electrolytes with graphene nanosheets prepared by arc-discharge

Ionic liquid gel polymers have widely been used as the electrolytes in all-solid-state supercapacitors, but they suffer from low ionic conductivity and poor electrochemical performance. Arc discharge is a fast, low-cost and scalable method to prepare multi-layered graphene nanosheets, and as-made graphene nanosheets （denoted as ad-GNSs） with few defects, high electrical conductivity and high thermal stability should be favorable conductive additive materials. Here, a novel ionic liquid gel polymer electrolyte based on an ionic liquid （EM1MNTF2） and an copolymer （P（VDF-HFP）） was modified by the addition of ad-GNSs as an ionic conducting promoter. This modified gel electrolyte shows excellent thermal stability up to 400 ℃ and a wide electrochemical window of 3 V. An all-solid-state supercapacitor based on commercial activated carbon was fabricated using this modified ionic liquid gel polymer electrolyte, which shows obviously improved electrochemical behaviors compared with those of the corresponding all-solid-state supercapacitor using pure ionic liquid gel polymer electrolyte. Specially, smaller internal resistance, higher specific capacitance, better rate performance and cycling stability are achieved. These results indicate that the ionic liquid gel polymers modified by ad-GNSs would be promising and suitable gel electrolytes for high performance all-solid-state electrochemical devices.     

A New Hydroxo‐bridged Chromium(III) Dimer [Cr(saltn)OH]2·4H2O: Synthesis,Crystal Structure and Magnetic Properties

A new hydroxo‐bridged dimeric Cr(III) complex [Cr(saltn)OH]₂·4H₂O [H₂saltn=N,N′‐bis(salicylidene)trimethylenediamine] has been synthesized and its structural and magnetic properties have been investigated. The complex crystallizes in the triclinic space group P‐1 with one dimeric formula unit in a cell of dimensions a=0.95828(19) nm, b=0.95926(19) nm, c=1.0437(2) nm, α=86.77(3)°, β=82.48(3)°, and γ=64.93(3)°. The geometry around each chromium(III) center is six‐coordinate, distorted‐octahedral. The bridging Cr₂O₂ unit is strictly planar, as required by the crystallographic symmetry. The Cr? O? Cr′ bridging angle is 99.94(16)°, and the distance between Cr…Cr′ is 0.3019 nm. The magnetic susceptibility of the complex has been examined in the range of 2‐300 K. By using the spin‐spin coupled model for an S₁=S₂=3/2 dimeric system , the magnetic data were fitted to give the parameters of g=2.01(1), J=‐0.85(2) cm^‐1, and zJ' =0.18(3)cm^‐1, indicating the presence of a weak antiferromagnetic spin‐exchange interaction between the Cr(III) ions in the binuclear complex.     

Photorefractivity of hyperbranched polyisophthalate endcapped with pendant carbazolyl and azobenzene groups

A novel hyperbranched polyisophthalate containing pendant carbazolyl and azobenzene groups at the terminals was synthesized, and its photorefractivity has also been evaluated by the effective electro-optic (EO) coefficient, two-beam couple (TBC) coefficient, diffraction efficiency and photorefractive (PR) response time. This PR polymer has a low glass transition temperature of 21 °C without any extra plasticizer added, which provides a necessary free volume for EO chromophore reorientation during the recording process at room temperature. The obtained PR film exhibited an effective EO coefficient of 30 pm V⁻¹, a TBC coefficient of 59 cm⁻¹, a diffraction efficiency of 17%, and a modulation index of 1.67 × 10⁻³ at the wavelength of 632.8 nm with an applied electric field of 80 V μm⁻¹ at room temperature. The TBC coefficient was found to be beam-intensity dependent, compared with what is found in inorganic crystals. Moreover, a fast PR response time of 10 ms was deduced at an erasing beam intensity of 1.0 W cm⁻².     

Ir（Ⅳ）—KBrO3—DBS—偶氮氯膦催化分光光度法测定微量铱的研究

ＫＢｒＯ３－ＤＢＳ偶氮氯膦在０．８ｍｌ．Ｌ＾－１的Ｈ２ＳＯ４介质中长时间加热亦无明显褪色现象，但在有微量铱存在时，褪色反应在３ｍｉｎ内完成，且与Ｉｒ（Ⅳ）的浓度有良好的线性关系，据此建立了微量铱的催化褪色分光光度分析法，其检出限为０．０１μｇ．１０ｍＬ＾－１铱的含量在０．０１－０．２０μｇ．１０ｍＬ＾－１范围内符合比尔定律。