Mössbauer study of new vanadate glass with large charge-discharge capacity

Charge-discharge capacity and cyclicity of lithium ion battery (LIB) was evaluated in which 15Li₂O·10Fe₂O₃·xSnO₂·5P₂O₅·(70–x)V₂O₅ glass (x?=?0 and 20 in mol%, abbreviated as xLFSPV) was used as a cathode. A local structure of xLFSPV glass before and after charging was investigated by ⁵⁷Fe- and ¹¹⁹Sn-Mössbauer spectroscopies. ⁵⁷Fe-Mössbauer spectrum of xLFSPV glass with ‘x’ of 20 was composed of a doublet with isomer shift (δ) of 0.35_±0.02 mm s^???1 and quadrupole splitting (Δ) of 0.88_±0.03 mm s^???1 due to distorted Fe^IIIO₄ tetrahedra. ¹¹⁹Sn-Mössbauer spectrum of this glass consisted of a doublet with δ of 0.08_±0.01 and Δ of 0.52_±0.01 mms^???1 due to distorted Sn^VIO₆ octahedra. After discharging the battery from 4.5 to 1.0 V, larger δ of 0.40_±0.03 mm s^???1 and Δ of 0.94_±0.04 mm s^???1 were obtained, indicating that both iconicity of Fe-O bonds and local distortion of Fe^IIIO₄ tetrahedra were increased. On the contrary, identical δ of 0.09_±0.01 mm s^???1 and Δ of 0.50_±0.01 mm s^???1 were observed in the ¹¹⁹Sn-Mössbauer spectrum of 20LFSPV glass after the discharge, indicating that chemical environment of Sn^IVO₆ octahedra was not affected after the discharge. Charge-discharge curve of LIB containing 20LFSPV glass as a cathode active material recorded under the current density of 8.3 mA g^???1 (0.011 mA cm^???2) between 1.0 and 4.5 V showed a large initial charge capacity of 431.1 mAh g^???1 and discharge capacity of 382.3 mAh g^???1, respectively. These results indicate that 20LFSPV glass could be a new cathode active material for LIB.     

Electrocatalytic Oxidation of Amines on a Mediator‐Modified Electrode by Electrochemical Copolymerization of Nitroxyl Radical Precursor Containing Pyrrole Side Chain and Bithiophene

This paper describes the electrocatalytic oxidation of amines on TEMPO (2,2,6,6‐tetramethylpiperidine‐1‐oxyl)‐modified electrodes prepared by electrochemical copolymerization of TEMPO precursor containing pyrrole side chain and 2,2′‐bithiophene. The modified electrode exhibits electrocatalytic activity for the oxidation of primary and secondary amines. Cyclic voltammetric studies showed that the peak current of the cyclic voltammogram increased linearly with increasing concentration of amine in the sample solution.     

5,11-Diazadibenzo[hi,qr]tetracene: Synthesis,Properties, and Reactivity toward Nucleophilic Reagents

5,11-Diazadibenzo[hi,qr]tetracene was synthesized as a new nitrogen-substituted polycyclic heteroaromatic compound by Pd-catalyzed cycloisomerization of an alkyne precursor followed by oxidative cyclization with bis(trifluoroacetoxy)iodobenzene. The substitution of imine-type nitrogen atoms significantly enhanced its electron-accepting character and facilitated the direct nucleophilic addition of arylamines under strongly basic conditions to afford the desired amino-substituted products. The introduction of amino groups induced a remarkable red-shift in their absorption spectra; the tetrasubstituted product exhibited intense near-infrared absorbing property. Furthermore, the π-electronic system, which includes a redox-active 1,4-diazabutadiene moiety, underwent reversible interconversion to its corresponding reduced form upon reduction with NaBH₄ and aerobic oxidation.     

Dimesitylborylethynylated Arenes: Unique Electronic and Photophysical Properties Caused by Ethynediyl (C≡C) Spacers

Herein, we report the synthesis and electrochemical and photophysical properties of aromatic hydrocarbons having one or two dimesitylborylethynyl peripherals. The mono- ( 1 ) and diboryl compounds ( 2 ), readily prepared by nucleophilic substitution reaction, are fairly stable to air and moisture in the solid state. The inserted ethynediyl (C≡C) spacer cancels the steric hindrance between the bulky dimesitylboryl groups and aromatic rings, leading to effective π conjugation over the B−C≡C−Ar linkages, as revealed by cyclic voltammetry. Despite the small structural differences, the photophysical properties of the benzene, naphthalene, and anthracene derivatives are different. Virtually no emission was observed from the benzene derivatives, whereas the anthracene derivatives emitted with high quantum yields both in solution and in the solid state. Notably, the naphthalene derivatives showed aggregation-induced emission behavior. Unlike the common sterically congested triarylborane derivatives reported so far, the anthracene derivatives showed π–π*-type absorption and emission bands, which derive from efficient intramolecular orbital interactions between the boron centers and anthracene moieties, as supported by DFT calculations. As a result, the dimesitylborylethynyl substituents effectively lower the LUMO levels of the aromatic hydrocarbon parts, whereas the HOMO levels are almost unaffected, thereby leading to materials with controllable HOMO–LUMO gaps.     

Ultraviolet Photoelectron Spectra of Potassium Dosed Higher Fullerenes

Abstract

Ultraviolet photoelectron spectra of potassium dosed higher fullerenes are measured with a synchrotron radiation light source. Potassium dosing to higher fullerenes brings a new structure between the spectral onset of pristine fullerenes and the Fermi level. As the spectral edge of the new structure does not cross the Fermi level, potassium dosed higher fullerenes are not metallic but semiconductive. When the potassium is excessively dosed to the fullerenes, the lower binding energy structures above 5 eV become faint. In contrast to this phenomenon, four distinct structures appear between 5 and 14 eV.     

Near-IR Luminescent YbIII Coordination Polymers Composed of Pyrene Derivatives for Thermostable Oxygen Sensors

Oxygen-sensitive and near-infrared (NIR) luminescent Yb^III coordination polymers incorporating ligands based on pyrene derivatives were synthesized: Yb^III–TBAPy and Yb^III–TIAPy (TBAPy: 1,3,6,8-tetrakis(p-benzoate)pyrene; TIAPy: 1,3,6,8-tetrakis(3,5-isophthalic acid)pyrene). The coordination structures of these materials have been characterized by means of electrospray ionization mass spectrometry, X-ray diffraction analysis, and thermogravimetric analysis. Moreover, the porous structure of Yb^III–TIAPy has been evaluated by measuring its N₂ adsorption isotherm. The NIR luminescence properties of Yb^III–TBAPy and Yb^III–TIAPy have been examined by acquiring emission spectra and determining emission lifetimes under air or argon and in vacuo. Yb^III–TIAPy exhibited high thermal stability (with a decomposition temperature of 400 °C), intense luminescence (with an emission quantum yield under argon of 6.6 %), and effective oxygen-sensing characteristics. These results suggest that NIR luminescent Yb^III coordination polymers prepared using pyrene derivatives could have applications in novel thermo-stable oxygen sensors.