Preparation and photoluminescence characteristics of polysiloxane pendant tris(2,2′-bipyridine)ruthenium (II) complex

Polysiloxanes containing pendant tris(2,2′-bipyridine)ruthenium(II) complex (Ru(bpy)3²⁺) were prepared by reaction of polysiloxane-pendant 2,2′-bipyridine (PSiO-bpy) with cis-Ru(bpy)₂Cl₂. In methanol solution, the polymer pendant Ru(bpy)3²⁺ showed absorption maximum at 456nm and emission maximum at around 609nm, both of which are shifted to longer wavelength than the monomeric Ru(bpy)₃²⁺. The lifetime τ₀ of the excited polymer complex with low Ru(bpy)3²⁺ content was almost the same as that of the monomeric one in methanol (830ns), but τ₀ of the polymer with higher complex content was shorter because of a concentration quenching. In a solid state, τ₀ was much shorter (306–503ns) than that in a methanol solution contrary to the conventional polymeric system. Higher complex content in the polymer film caused higher glass transition temperature (Tg), but shorter τ₀. These results indicate concentration quenching in the polymer film. The excited polymer pendant Ru(bpy)3²⁺ was quenched by oxygen, and the relative emission intensity followed the Stern-Volmer equation. In a methanol solution the quenching rate constant (k_q) was the same order of magnitude as the monomeric complex, and independent of the complex content in the polymer. In a film, k_q was higher for the polymer with higher complex content.     

Study on controlling particle growth in seeded emulsion polymerization with regulated coagulation based on the electrostatic interactions

30wt% solid content, anionic seed copolymer latex P(methyl acrylate-co-methyl methacrylate) was prepared by conventional emulsion polymerization, and then the seeded emulsion polymerization was carried out accompanied with the electrostatic coagulation during the reaction in the presence of counter-ion species, such as cationic monomer and initiator. In this article, effects of cationic monomer (dimethyl aminoethyl methacrylate, DM) content, secondary monomer to seed polymer weight ratio, M/P and amount of emulsifier (polyoxyethylene nonylphenylether with 23 units of ethylene oxide, PEO23) were investigated on the effective particle growth and the stability of final latex. With 10wt% DM in monomer, M/P ratio at 2.0 were recommended. An optimal policy for handling the emulsifier content without the nucleation of secondary particles while achieving the controlled coagulative growth was proposed from the observations of polymer yield and particle size during the polymerization.