Effects of the architecture and environment on polymeric molecular assemblies of novel amphiphilic diblock copolynorbornenes with narrow polydispersity via living ring‐opening metathesis polymerization

Diblock copolymers of 5‐(methylphthalimide)bicyclo[2.2.1]hept‐2‐ene (NBMPI) and 1,5‐cyclooctadiene were synthesized by living ring‐opening metathesis polymerization with a well‐defined catalyst {RuCl₂(CHPh)[P(C₆H₁₁)₃]₂}. Unhydrogenated diblock copolymers showed two glass transitions due to poly(NBMPI) and polybutadiene segments, such as two glass‐transition temperatures at ?86.5 and 115.3 °C for poly 1a and ?87.2 and 115.3 °C for poly 1b . However, only one melting temperature could be observed for hydrogenated copolymers, such as 119.8 °C for poly 2a and 121.7 °C for poly 2b . The unhydrogenated diblock copolymer with the longer poly(NBMPI) chain (poly 1a ; temperature at 10% mass loss = 400 °C) exhibited better thermal stability than the one with the shorter poly(NBMPI) chain (poly 1b ; temperature at 10% mass loss = 385 °C). Two kinds of hydrogenated diblock copolymers, poly 2a and poly 2b , exhibited relatively poor solubility but better thermal stability than unhydrogenated diblock copolymers because of the polyethylene segments. Poly[(hydrochloride quaternized 2‐norbornene‐5‐methyleneamine)‐b‐butadiene]‐1 (poly 3a ) was obtained after the hydrolysis and quaternization of poly 1a . Dynamic light scattering measurements indicated that the hydrodynamic diameters of the cationic copolymer (poly 3a ) in water (hydrodynamic diameter = 1580 nm without salt), methanol/water (4/96 v/v; hydrodynamic diameter = 1500 nm without salt), and tetrahydrofuran/water (4/96 v/v; hydrodynamic diameter = 1200 nm without salt) decreased with increasing salt (NaCl) concentration. The effect of temperature on the hydrodynamic diameter of hydrophobically modified poly 3a was also studied. The inflection point of the hydrodynamic diameter of poly 3a was observed at various polymer concentrations around 30 °C. The critical micelle concentration of hydrophobically modified poly 3a was observed at 0.018 g dL^?1. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2901–2911, 2006     

Vinyl copolymers containing pendant 1,4‐distyrylbenzene and 1,3,4‐oxadiazole chromophores: Preparation and optoelectronic properties

We prepared two vinyl copolymers P1 and P2 containing pendant distyrylbenzene and aromatic 1,3,4‐oxadiazole derivatives, respectively, from their precursor poly(styrene‐ran‐4‐vinylbenzyl chloride) (M_w = 11,400, PDI = 1.18), which had been prepared by the controlled radical polymerization (RAFT). Two main chain polymers containing similar isolated distyrylbenzene ( P3) and aromatic 1,3,4‐oxadiazole ( P4 ) chromophores were also synthesized for comparative study. The resulted copolymers ( P1 – P4 ) are soluble in common organic solvents and are basically amorphous materials with 5% weight‐loss temperature higher than 360 °C. The PL spectral results reveal that the architecture of P1 prevents the formation of inter‐ or intramolecular interaction. The HOMO and LUMO levels of P2 , estimated from cyclic voltammetric data, are ?5.96 and ?3.81 eV, respectively, which are much lower than those of P1 (?5.12 and ?3.11 eV). The emission of blend from P1 and P2 are contributed mainly from distyrylbenzene fluorophore (～450 nm) owing to efficient energy transfer. Moreover, the blend exhibits three kinds of redox behavior depending on their weight ratios. The luminance and current efficiency of the EL device lpar;ITO/PEDOT/ MEH ‐ PPV + P2 /Al) are 503 cd/m² and 0.11 cd/A, which can be improved to 1285 cd/m² and 0.44 cd/A, respectively, as the weight ratio of P2 increases from 0 to 20%. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5362–5377, 2006     

Effect of excess halide on the palladium‐catalyzed insertion‐triggered radical copolymerization of methyl acrylate and 1‐hexene

[Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) is a very efficient initiator of the radical polymerization of methyl acrylate, but it is not active in the polymerization of methyl methacrylate or in the copolymerization with 1‐hexene. The addition of an excess of NBu₄Cl to solutions of [Pd₂(μ‐Cl)₂(C₆F₅)₂(tht)₂] ( 1 ) provides an initiator system that copolymerizes methyl acrylate and 1‐hexene by an insertion‐triggered radical mechanism. Random copolymers are obtained with 11% incorporation of 1‐hexene in moderate yields (about 35%). Studies of the decomposition products obtained after the first insertion of methyl acrylate in the Pd? C₆F₅ bond of 1 show that the addition of excess halide in the presence of monomer favors the homolytic cleavage of the Pd? C bond, and the generation of the radicals that are active species in the polymerization, versus alternative evolution pathways. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5682–5691, 2006     

Surface characterization and barrier properties of plasma‐modified polyethersulfone/layered silicate nanocomposites

This study describes the preparation of polyethersulfone (PES)/layered silicate nanocomposites (PLSNs) by mixing PES polymer chain into organically‐modified layered silicate in 1‐methyl‐2‐pyrrolidinone (NMP) solution. Both X‐ray diffraction data and transmission electron microscopy images of PLSNs indicate that the silicate layers were almost exfoliated and randomly distributed into the PES matrix. The mechanical and barrier properties of PLSNs show remarkable enhancement in the storage modulus and water/oxygen permeability when compared with that of neat PES matrix. Surfaces modification of PES and PLSN films with various treated times, system pressures, and radio frequency (RF) powers were performed using a mixture of oxygen (O₂) and nitrogen (N₂) plasmas. The topographical and physical properties of plasma‐modified PES and PLSN surfaces were investigated using scanning probe microscopy (SPM), contact‐angle measurements, and X‐ray photoelectron spectroscopy (XPS). These results indicate that the surface roughness of PLSNs with the same condition of plasma modification is lower than that of neat PES matrix and is probably due to the increase of stiffness with the presence of inorganic layered silicates in PES matrix. The surface properties of the PES and PLSNs are also changed from hydrophobic to hydrophilic. The XPS spectra suggest that the exposure of the PES and PLSNs to the plasmas led to the combination of etching reactions of polymer surface initiated by plasma and the following addition reactions of new oxygen‐ and nitrogen‐containing functional groups onto polymer surfaces to change their surface properties. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3185–3194, 2006     

Sulfonated poly(aryl ether ether ketone ketone)s containing fluorinated moieties as proton exchange membrane materials

A series of sulfonated poly(aryl ether ether ketone ketone)s statistical copolymers with high molecular weights were synthesized via an aromatic nucleophilic substitution polymerization. The sulfonation content (SC), defined as the number of sulfonic acid groups contained in an average repeat unit, could be controlled by the feed ratios of monomers. Flexible and strong membranes in sodium sulfonate form could be prepared by the solution casting method, and readily transformed to their proton forms by treating them in 2 N sulfuric acid. The polymers showed high T_gs, which increased with an increase in SC. Membranes prepared from the present sulfonated poly(ether ether ketone ketone) copolymers containing the hexafluoroisopropylidene moiety (SPEEKK‐6F) and copolymers containing the pendant 3,5‐ditrifluoromethylphenyl moiety (SPEEKK‐6FP) had lower water uptakes and lower swelling ratios in comparison with previously prepared copolymers containing 6F units. All of the polymers possessed proton conductivities higher than 1 × 10^?2 S/cm at room temperature, and proton conductivity values of several polymers were comparable to that of Nafion at high relative humidity. Their thermal stability, oxidative stability, and mechanical properties were also evaluated. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2299–2310, 2006     

Preparation and characterization of rigid poly(vinyl chloride)/MMT nanocomposites. II. XRD,morphological and mechanical characteristics

A Haake torque rheometer equipped with an internal mixer is used to study the influence of the amount of sodium montmorillonite (Na⁺‐MMT) and organically modified MMT (O‐MMT) on X‐ray diffraction (XRD), morphology, and mechanical characteristics of rigid poly (vinyl chloride) (PVC)/Na⁺‐MMT and PVC/O‐MMT nanocomposites, respectively. Results of XRD and transmission electron microscopy (TEM) indicate that MMT is partially encapsulated and intercalated in the rigid PVC/Na⁺‐MMT nanocomposites. However, results of XRD and TEM show MMT is partially intercalated and exfoliated in the rigid PVC/O‐MMT nanocomposites. Tensile strength, yield strength, and elongation at break of the rigid PVC/MMT nanocomposites were improved simultaneously with adding 1–3 wt % Na⁺‐MMT or O‐MMT with respect to that of pristine PVC. However, the addition of Na⁺‐MMT or O‐MMT should be kept as not more than 3 wt % to optimize the mechanical properties and the processing stability of the rigid PVC/MMT nanocomposites. SEM micrographs of the fractured surfaces of the rigid PVC/Na⁺‐MMT and PVC/O‐MMT nanocomposites both before and after tensile tests were also illustrated and compared. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2145–2154, 2006     

Measurement and prediction of solubilities and diffusion coefficients of carbon dioxide in starch–water mixtures at elevated pressures

The solubility and diffusion coefficient of carbon dioxide in intermediate‐moisture starch–water mixtures were determined both experimentally and theoretically at elevated pressures up to 16 MPa at 50 °C. A high‐pressure decay sorption system was assembled to measure the equilibrium CO₂ mass uptake by the starch–water system. The experimentally measured solubilities accounted for the estimated swollen volume by Sanchez–Lacombe equation of state (S‐L EOS) were found to increase almost linearly with pressure, yielding 4.0 g CO₂/g starch–water system at 16 MPa. Moreover, CO₂ solubilities above 5 MPa displayed a solubility increase, which was not contributed by the water fraction in the starch–water mixture. The solubilities, however, showed no dependence on the degree of gelatinization (DG) of starch. The diffusion coefficient of CO₂ was found to increase with concentration of dissolved CO₂, which is pressure‐dependent, and decrease with increasing DG in the range of 50–100%. A free‐volume‐based diffusion model proposed by Areerat was employed to predict the CO₂ diffusivity in terms of pressure, temperature, and the concentration of dissolved CO₂. S‐L EOS was once more used to determine the specific free volume of the mixture system. The predicted diffusion coefficients showed to correlate well with the measured values for all starch–water mixtures. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 607–621, 2006     

Effect of glass bead packing on the fibrillation of liquid‐crystalline polymer in polycarbonate

Polycarbonate (PC) was melt blended with small amount of liquid‐crystalline polymer (LCP) and various contents of glass beads (GB) having different diameters. The rheological measurements indicated that the GB addition increased the viscosity ratio and seemed unfavorable to the LCP fibrillation. However, the morphological observation showed that the LCP fibrillation was promoted by the GB addition and varied with the GB packing. With the increased GB packing by increasing the GB content and/or decreasing the GB diameter, LCP deformed from spheres and ellipsoids into stretched ellipsoids at lower shear rates and into long fibrils at higher shear rates. Although higher content of smaller GB jammed into the larger LCP droplets and inhibited the LCP fibrillation, very long LCP fibrils formed at higher shear rates at a high enough packing of GB. The relationship between GB packing and LCP fibrillation revealed two kinds of hydrodynamic effects of GB promoting the LCP fibrillation: at lower GB packing, the shear flow was enhanced by the high local shear between GB, in quantity; and for a high enough GB packing, the shear flow was changed, in quality, into elongational flow, which was more effective for the LCP fibrillation. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1020–1030, 2006     

Metallocene copolymers of propene and 1‐hexene: The influence of the comonomer content and thermal history on the structure and mechanical properties

The relationships between the structure and properties have been established for copolymers of propylene and 1‐hexene synthesized with an isotactic metallocene catalyst system. The most important factor affecting the structure and properties of these copolymers is the comonomer content. The thermal treatment, that is, the rate of cooling from the melt, is also important. These factors affect the thermal properties, the degree of crystallinity, and therefore the structural parameters and the viscoelastic behavior. A slow cooling from the melt favors the formation of the γ phase instead of the α modification. Regarding the viscoelastic behavior, the β relaxation, associated with the glass‐transition temperature, is shifted to lower temperatures and its intensity is increased as the 1‐hexene content raises. The microhardness values are correlated with those of the storage modulus deduced from dynamic mechanical thermal analysis curves, and good linear relations have been obtained between these parameters. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1253–1267, 2006     

Characterization and electrical properties of polypyrrole/multiwalled carbon nanotube composites synthesized by in situ chemical oxidative polymerization

This study describes the preparation of polypyrrole (PPy)/multiwalled carbon nanotube (MWNT) composites by in situ chemical oxidative polymerization. Various ratios of MWNTs, which served as hard templates, were first dispersed in aqueous solutions with the surfactant cetyltrimethylammonium bromide to form micelle/MWNT templates and overcome the difficulty of MWNTs dispersing into insoluble solutions of pyrrole monomer, and PPy was then synthesized via in situ chemical oxidative polymerization on the surface of the templates. Raman spectroscopy, Fourier transform infrared (FTIR), field‐emission scanning electron microscopy (FESEM), and high‐resolution transmission electron microscopy (HRTEM) were used to characterize the structure and morphology of the fabricated composites. Structural analysis using FESEM and HRTEM showed that the PPy/MWNT composites were core (MWNT)–shell (PPy) tubular structures. Raman and FTIR spectra of the composites were almost identical to those of PPy, supporting the idea that MWNTs served as the core in the formation of a coaxial nanostructure for the composites. The conductivities of these PPy/MWNT composites were about 150% higher than those of PPy without MWNTs. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1413–1418, 2006