Effects of diamines and their fluorinated groups on the color lightness and preparation of organosoluble aromatic polyimides from 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]‐hexafluoropropane

To investigate the position and amount of the CF₃ group affecting the coloration of polyimides (PIs), we prepared 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]hexafluoropropane ( 2 ) with four CF₃ groups with 2‐chloro‐5‐nitrobenzotrifluoride and 2,2‐bis(4‐hydroxyphenol)hexafluoropropane. A series of soluble and light‐colored fluorinated PIs ( 5 ) were synthesized from 2 and various aromatic dianhydrides ( 3a – 3f ). 5a – 5f had inherent viscosities ranging from 0.80 to 1.19 dL/g and were soluble in amide polar solvents and even in less polar solvents. The glass‐transition temperatures of 5 were 221–265 °C, and the 10% weight‐loss temperatures were above 493 °C. Their films had cutoff wavelengths between 343 and 390 nm, b* values (a yellowness index) ranging from 5 to 41, dielectric constants of 2.68–3.01 (1 MHz), and moisture absorptions of 0.03–0.29 wt %. In a comparison of the PI series 6 – 8 based on 2,2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane, 2,2‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]propane, and 2,2‐bis[4‐(4‐aminophenoxy)phenyl]propane, we found that the CF₃ group close to the imide group was more effective in lowering the color; this means that CF₃ of 5 , 7 , and 8f was more effective than that of 6c . The color intensity of the four PI series was lowered in the following order: 5 > 7 > 6 > 8 . The PI 5f , synthesized from diamine 2 and 4,4′‐hexafluoroisopropylidenediphthalic anhydride, had six CF₃ groups in a repeated segment, so it exhibited the lightest color among the four series. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 922–938, 2003     

Bounds to optimal burn‐in and optimal work size

Burn‐in is a widely used method to improve the quality of products or systems after they have been produced. In this paper, we consider the problem of determining the optimal burn‐in time and optimal work size maximizing the long‐run average amount of work saved per time unit in the computer applications. Assuming that the underlying lifetime distribution of the computer has an initially decreasing or/and eventually increasing failure rate function, an upper bound for the optimal burn‐in time is derived for each fixed work size and a uniform (with respect to the burn‐in time) upper bound for the optimal work size is also obtained. Furthermore, it is shown that a non‐trivial lower bound for the optimal burn‐in time can be derived if the underlying lifetime distribution has a large initial failure rate. Copyright © 2005 John Wiley & Sons, Ltd.     

Vibrations of a magnet levitated over a flat superconductor

Based on a dipole-dipole interaction model, we discuss the levitation force and related vibration problems to understand the effects of flux pinning in type-II superconductors, and the applications of levitation in superconducting systems.     

Low Cost, High Efficiency, Gain Flattened L Band EDFA Using FBGs as C Band Seed Generators

A low cost, coolerless 980nm diode pumped, gain flattened L band EDFA with fast transient control, high pump efficiency and gain clamping effect was realized by using FBGs as C band seed generators.     

Initial oxidation kinetics of copper (1 1 0) film investigated by in situ UHV-TEM

Previous studies of the initial stage of oxidation on clean single crystal of Cu(1 0 0) have been extended to the case of the Cu(1 1 0) surface. The dynamic observation of the nucleation and growth of Cu oxide by means of in situ ultra high vacuum transmission electron microscopy (UHV-TEM) shows a highly enhanced oxidation rate on Cu(1 1 0) surface as compared to Cu(1 0 0). The kinetic data on the nucleation and growth of the three-dimensional oxide islands agree well with our heteroepitaxial model of surface diffusion of oxygen.     

Nano-tribological study on a super-hydrophobic film formed on rough aluminium substrates

A novel super-hydrophobic stearic acid (STA) film with a water contact angle of 166^o was prepared by chemical adsorption on aluminum wafer coated with polyethyleneimine (PEI) film. The micro-tribological behavior of the super-hydrophobic STA monolayer was compared with that of the polished and PEI-coated Al surfaces. The effect of relative humidity on the adhesion and friction was investigated as well. It was found that the STA monolayer showed decreased friction, while the adhesive force was greatly decreased by increasing the surface roughness of the Al wafer to reduce the contact area between the atomic force microscope (AFM) tip and the sample surface to be tested. Thus the friction and adhesion of the Al wafer was effectively decreased by generating the STA monolayer, which indicated that it could be feasible and rational to prepare a surface with good adhesion resistance and lubricity by properly controlling the surface morphology and the chemical composition. Both the adhesion and friction decreased as the relative humidity was lowered from 65% to 10%, though the decrease extent became insignificant for the STA monolayer. The project supported by the National Natural Science Foundation of China (50375151, 50323007, 10225209) and the Chinese Academy of Sciences (KJCX-SW-L2)     

Synthesis and association of poly(N,N‐dimethylacrylamide) copolymers with perfluorocarbon pendent groups connected through polyethylene‐glycol tethers

The synthesis is reported of copolymers of N,N‐dimethylacrylamide (DMA) and methacrylates containing 2,2′‐dihydroperfluorodecanoyl (RF) groups separated from the methacrylate by long polyethylene glycol (PEG) tether groups (between 1000 and 14,000 Da). At concentrations of between 1 and 8 wt % the copolymers with macromonomer contents of 1 mol % or less give gels in organic solvents such as dioxane, THF, or methanol, as well as in water. Given the low molecular weights, this indicates very efficient association of very low numbers of RF groups. Association and gel formation is enormously enhanced in the presence of longer PEG tethers. This is consistent with smaller poly(N,N,‐dimethylacrylamide) (PDMA) intermolecular excluded volume effects that are mediated by the longer PEG tethers and possibly by the incompatibility of PEG and PDMA that may lead to the formation of PEG microdomains. This increases the local concentrations of the RF groups in the PEO domains that are not diluted by the PDMA chains, as would be the case in the absence of PEG tethers. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 360–373, 2004     

Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004     

Performance of various activators in ethylene polymerization based on an iron(II) catalyst system

Ethylisobutylaluminoxane (EBAO) and its analogues were synthesized by a reaction between an triethylaluminum (Et₃Al)/triisobutylaluminum (i‐Bu₃Al) mixture and 4‐fluorobenzeneboronic acid, phenylboronic acid, or n‐butaneboronic acid and subsequent hydrolysis with water. They were used as cocatalysts in ethylene polymerization catalyzed by an iron complex {[(ArN?C(Me))₂C₅H₃N]FeCl₂, where Ar is 2,6‐diisopropylphenyl}. Polyethylene with a high molecular weight and a narrow molecular weight distribution was prepared with modified EBAOs, and the performance of the iron complex at high polymerization temperatures was greatly improved. The activators for the iron complex also affected the polymerization activity and the molecular weight of the resultant polyethylene. It was suggested that the stereo and electronic effects of the substitute groups of aluminoxane contributed to the improved performance of the new activators. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1093–1099, 2004