Morphology and microphase separation of star copolymers

Star copolymers have attracted significant interest due to their different characteristics compared with diblock copolymers, including higher critical micelle concentration, lower viscosity, unique spatial shape, or morphologies. Development of synthetic skills such as anionic polymerization and controlled radical polymerization have made it possible to make diverse architectures of polymers. Depending on the molecular architecture of the copolymer, numerous morphologies are possible, for instance, Archimedean tiling patterns and cylindrical microdomains at symmetric volume fraction for miktoarm star copolymers as well as asymmetric lamellar microdomains for star‐shaped copolymers, which have not been reported for linear block copolymers. In this review, we focus on morphologies and microphase separations of miktoarm (A_mB_n and ABC miktoarm) star copolymers and star‐shaped [(A‐b‐B)_n] copolymers with nonlinear architecture. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1–21     

Anisotropic Elastic-Viscoplastic Properties at Finite Strains of Injection-Moulded Low-Density Polyethylene

Injection-moulding is one of the most common manufacturing processes used for polymers. In many applications, the mechanical properties of the product is of great importance. Injection-moulding of thin-walled polymer products tends to leave the polymer structure in a state where the mechanical properties are anisotropic, due to alignment of polymer chains along the melt flow direction. The anisotropic elastic-viscoplastic properties of low-density polyethylene, that has undergone an injection-moulding process, are therefore examined in the present work. Test specimens were punched out from injection-moulded plates and tested in uniaxial tension. Three in-plane material directions were investigated. Because of the small thickness of the plates, only the in-plane properties could be determined. Tensile tests with both monotonic and cyclic loading were performed, and the local strains on the surface of the test specimens were measured using image analysis. True stress vs. true strain diagrams were constructed, and the material response was evaluated using an elastic-viscoplasticity law. The components of the anisotropic compliance matrix were determined together with the direction-specific plastic hardening parameters.