Synthesis and characterization of poly(ethyleneimine) dendrimers

Poly(ethyleneimine) (PEI) dendrimers up to the third generation (G3) were prepared by a divergent synthesis method from an ethylenediamine (EDA) core. The amine terminals were bonded with vinylbromide by a Michael addition reaction. Then, the bromide terminals were converted to amine groups using a Gabriel amine synthesis method. PEI dendrimers displayed pH-dependent luminescence, and their emission intensities at pH 6 increased over time. Fluorescence intensities also increased with increasing dendrimer generation from G1 to G3. Air-bubbling in aqueous solutions of dendrimers made to incorporate detectable amount of oxygen in dendrimers. EDA also behaved similarly in luminescence and oxygen incorporation.

Preparation of siloxy focal dendron-protected TiO2 nanoparticles and their photocatalysis

TiO2 nanoparticles were synthesized at approximately 0 degrees C by hydrolyzing [(CH3)2CHO]4Ti in 1-propanol solutions of poly(amido amine) dendrons with a siloxy focal point and long alkyl chain spacers. Transmission electron microscopic photographs showed that TiO2 nanoparticle was 1-5 nm in size and protected by dendrons, when prepared at a mixing ratio 1:10 of Ti ion and dendron. At higher contents of Ti ion, TiO2 nanoparticles aggregated up to a maximum size of 90 nm, depending on the dendron generation (first to third). It was confirmed from X-ray photoelectron spectroscopy that Si-O-Ti covalent bond was formed in dendron-protected TiO2 nanoparticles. The ability of dendron-protected TiO2 nanoparticles as a photocatalyst for the photodegradation of 2,4-dichlorophenoxyacetic acid was higher than that of nonprotected nanoparticle and superior at higher generation. It was suggested that the dendrons protecting TiO2 nanoparticle have enough void volume to conserve guest molecules and behave effectively as a reservoir of guest molecules.     

Structures of Fibrous Supramolecular Assemblies Constructed by Amino Acid Surfactants: Investigation by AFM, SANS, and SAXS

Aqueous gel-like solutions of N-acyl-L-aspartic acids (C(n)Asp, n=14, 16, 18) and N-dodecanoyl-beta-alanine (C(12)Ala) were prepared at pH 5-6 at room temperature. Structures of supramolecular assemblies in the solutions were investigated by atomic force microscopy (AFM), small-angle neutron scattering (SANS), and small-angle X-ray scattering (SAXS). The cross-sectional radii, 22-30 ?, of helical, fibrous assemblies were obtained from analysis of SANS for 1% gel-like C(n)Asp solutions. Three Bragg spacings were observed in a SANS spectrum for a 6% C(16)Asp solution. C(n)Asp molecules are associated into the unit chain of a helical bilayer strand with a diameter of 50-60 ?. Unit chains where linear bilayers twist form a double strand with helical sense of approximately 650-? pitch. It was confirmed from AFM images that cylindrical fibers in a gel-like C(12)Ala solution had a circular cross-section. The SAXS spectrum showed characteristic Bragg spacings. Cylindrical C(12)Ala fibers consist of multilamellar layers of period approximately 34-?. The fibers are laterally organized with period 365-380 ?. Copyright 2000 Academic Press.     

Influence of hydrophilic–lipophilic balance of nonionic emulsifiers on emulsion copolymerization of styrene and methacrylic acid

Emulsion copolymerizations of styrene and methacrylic acid (MAA) with various nonionic emulsifiers having a hydrophilic–lipophilic balance (HLB) range of 13.7–17.2 were performed to clarify the influence of emulsification state on polymerization. The emulsification state with a lower-HLB value emulsifier was worse than that with a higher one. In the lowest HLB value, MAA was predominantly polymerized over styrene in the early stage of the copolymerization, resulting in predominant (heterogeneous) distribution of MAA units in the inside of the final polymer particles. In the higher-HLB emulsifiers, styrene and MAA were simultaneously copolymerized, resulting in a homogeneous MAA distribution. The percentage of incorporation of the nonionic emulsifier inside the particles was the highest (49% based on the total amount of the emulsifier) in the lowest HLB, whereas it was 1% in the highest HLB. Part CCLXXXIV of the series “Studies on suspension and emulsion”.     

Renewable microcolumns for automated DNA purification and flow-through amplification: from sediment samples through polymerase chain reaction

There is an increasing need for field-portable systems for the detection and characterization of microorganisms in the environment. Nucleic acids analysis is frequently the method of choice for discriminating between bacteria in complex systems, but standard protocols are difficult to automate and current microfluidic devices are not configured specifically for environmental sample analysis. In this report, we describe the development of an integrated DNA purification and polymerase chain reaction (PCR) amplification system and demonstrate its use for the automated purification and amplification of Geobacter chapellei DNA (genomic DNA or plasmid targets) from sediments. The system includes renewable separation columns for the automated capture and release of microparticle purification matrices, and can be easily reprogrammed for new separation chemistries and sample types. The DNA extraction efficiency for the automated system ranged from 3 to 25%, depending on the length and concentration of the DNA target. The system was more efficient than batch capture methods for the recovery of dilute genomic DNA even though the reagent volumes were smaller than required for the batch procedure. The automated DNA concentration and purification module was coupled to a flow-through, Peltier-controlled DNA amplification chamber, and used to successfully purify and amplify genomic and plasmid DNA from sediment extracts. Cleaning protocols were also developed to allow reuse of the integrated sample preparation system, including the flow-through PCR tube.     

Electrochemical properties of protoporphyrin IX zinc(II) films

The electrochemical properties of protoporphyrin IX zinc(II) (ZnPP) films on indium-tin oxide (ITO) substrate have been studied for three types of films with different arrangements, which were an adsorbed film of ZnPP and LB films of ZnPP and its hybrid with hexadecyltrimethylammonium bromide. Cyclic voltammetry (CV) measurement showed that, as the adsorbed amount of ZnPP increases, an irreversible oxidation peak of ZnPP film is intensified. This reveals that electrochemical properties depend on the adsorbed amount rather than the orientation of porphyrin molecules. It was also supported from CV measurement and ultraviolet-visible absorption spectroscopy that porphyrins adsorbed on ITO substrate were desorbed after the single scan of potential. Additionally, photoresponse of these ZnPP films was investigated by photocurrent measurement. The photocurrent generation is due to carboxylic acid moieties but not ZnPP macrocycles.     

P NMR investigation of a ringing gel phase and adjacent phases

The temperature-surfactant concentration phase diagram was examined for the dodecyltrimethylammonium dimethylphosphate/3-methyl-3-methoxybutanol/water ternary system. The phase diagram contained a highly elastic gel phase which is known as a “ringing gel phase”. The ringing gel phase and adjacent phases in the ternary system were investigated by polarized optical microscopy, freeze-fracture transmission electron microscopy, and ³¹P NMR. Globular textures were observed in an optically isotropic gel phase. Since the globules were larger than those found in an isotropic solution, the texture consists of domains of aggregated units in the cubic (I₁) phase. Structure units of domains are equivalent to microemulsions which are constructed by surfactant molecules and swollen by alcohol in the isotropic (L₁) phase. Characteristic polarized microscopic textures were visualized in two phases with higher surfactant concentrations. These phases were identified as being hexagonal (H₁) and lamellar (L) liquid crystals which was confirmed by transmission electron microscopy. The ³¹P NMR signal of the ringing gel showed a sharp singlet the same as that of the L₁ phase, indicating the fully averaged anisotropic interaction of the aggregates. The characteristic NMR signals of the anisotropic hexagonal and lamellar liquid crystal phases displayed chemical shielding with an asymmetric lineshape.     

Synthesis of new-type donor–acceptor π-conjugated benzofuro[2,3-c]oxazolo[4,5-a]carbazole fluorescent dyes and their photovoltaic performances of dye-sensitized solar cells

New-type donor–acceptor π-conjugated benzofuro[2,3-c]oxazolo[4,5-a]carbazole fluorescent dyes with various lengths of non-conjugated alkyl chains containing a carboxyl group at the end position have been developed and their photovoltaic performances of dye-sensitized solar cells are investigated. It is found that in spite of the lengths of the alkyl chains, due to flexibility of alkyl chain, the cyano group of the dyes is located in close proximity to TiO₂ surface and thus a good electron communication between the dyes and TiO₂ surface is established.     

Preparation of disk-like cellulose particles

Disk-like cellulose particles were facilely prepared by stirring a dispersion of spongy cellulose particles that were prepared with a solvent-releasing method (SRM) with a magnetic stir bar. The obtained particles were thick and disk-like and retained their spongy structure in the wet state. The thick, disk-like particles became thinner in a specific direction upon drying because of capillary force. In contrast, when the same procedure was conducted using cellulose particles with dense structures, the particle shapes were not deformed, and disk-like shapes did not appear. Moreover, when the stirring was carried out using a shaking bath or a touch mixer, the shape transformation was not observed. These results suggest that the spongy structure of the cellulose particles would be a pseudo-plasticization state, which can cause the cellulose particles to deform. The disk-like particles formed as a result of the grinding of spongy cellulose particles between the stir bar and the vial. The number of disk-like particles and the degree of deformation increased with increasing of the stirring time, the speed and the contact area.     

Novel amphiphilic linear polymer/dendrimer block copolymer: Synthesis of poly(2-methyl-2-oxazoline)-block-poly(amido amine) dendrimer

Novel linear polymer/dendrimer block copolymers, poly(2-methyl-2-oxazoline)-block-poly(amido amine) dendrimers (water-soluble full-generation type 4 (G = 4.0 and 5.0) and amphiphilic half-generation type 5 (G = 3.5, 4.5, and 5.5)), were synthesized by divergent-growth dendrimer construction with ω-ethylenediamine-terminated poly(2-methyl-2-oxazoline), which was prepared by living ring-opening polymerization of 2-methyl-2-oxazoline. Assembly of the amphiphilic dendrimer-based block copolymer (G = 5.5) was investigated by surface tension measurements (critical micelle concentration, 0.49 wt.-%) and by small-angle neutron scattering analysis (spherical particles; assembled number, ca. 10³).