Thermal conductivity of poly(vinyl chloride)/polycaprolactone blends

Thermal diffusivity, heat capacity, and density of polyvinyl chloride/polycaprolactone (PVC/PCL) blends were measured by the laser flash method, DSC, and pycnometry, respectively. The thermal conductivity of the PVC/PCL blends was determined from the results. The miscibility of the blend and crystallinity of PCL were determined by DSC. The effect of blend structure on thermal conductivity is discussed. The phase compositions of the PVC/PCL blends are of three types depending on PCL content: i.e., up to 33%, from 33 to 70%, and above 70% PCL by weight. Thermal conductivity, thermal diffusivity, and heat capacity of the PVC/PCL blends are strongly affected by the phase composition of the blend, which changes in a complicated way with PCL content. © 1994 John Wiley & Sons, Inc.     

Laser cleaning of glass

The pulse lasers, YAG-, CO₂-, and N₂-lasers, are examined for use in the cleaning of glass. Cleaning is found to be due to the evaporation and sputtering of stains on the glass by the heat energy of the laser light. Only the N₂ laser can be used for the cleaning of the exit surface of the glass (the opposite side to the laser). A laser with a high peak power of about 10⁶J/s and short-pulse duration below 100 ns is found to be necessary in practice.     

Simple and rapid determination of trace amounts of gold(III), palladium(II), and platinum(IV) in industrial waste solutions after recovery of noble metals by combined use of GFAAS and anion-exchange separation.

A simple and rapid method for the analysis of trace amounts of gold(III), palladium(II), and platinum(IV) by the combined use of graphite furnace atomic absorption spectrometry and anion-exchange separation was proposed, and successfully applied to the rapid determination of metals in industrial waste solutions obtained from the final process of noble-metal recovery factories, because noble metals can be selectively and quantitatively separated to a high degree by using a small column containing only a 0.7 g-portion of a common anion-exchange resin and a dilute thiourea solution.     

Synthesis of aromatic poly(thioether ketone)

Aromatic poly(thioether ketone)s were prepared by the direct polycondensation of aromatic dicarboxylic acids with aryl compounds containing ether or sulfide structures using phosphorus pentoxide/methanesulfonic acid (PPMA) as a condensing agent and solvent. Polycondensation proceeded smoothly and produced aromatic poly(thioether ketone)s with inherent viscosities up to 0.73 dL/g. The synthesis of substituted aryl ketones by the reaction of substituted benzoic acids with aryl compounds in PMMA was studied in detail to demonstrate the feasibility of the reaction for polymer formation. The thermogravimetry of the aromatic poly(thioether ketone)s showed a 10% weight loss in air and nitrogen at around 450 and 460°C, respectively. © 1992 John Wiley & Sons, Inc.     

Synthesis and properties of poly(amic acid)s and polyimides based on 2,2′,6,6′‐biphenyltetracarboxylic dianhydride

Poly(amic acid)s (PAAs) having the high solution stability and transmittance at 365 nm for photosensitive polyimides have been developed. PAAs with a twisted conformation in the main chains were prepared from 2,2′,6,6′‐biphenyltetracarboxylic dianhydride (2,2′,6,6′‐BPDA) and aromatic diamines. Imidization of PAAs was achieved by chemical treatment using trifluoroacetic anhydride. Among them, the PAA derived from 2,2′,6,6′‐BPDA and 4,4′‐(1,3‐phenylenedioxy)dianiline was converted to the polyimide by thermal treatment. The heating at 300 °C under nitrogen did not complete thermal imidization of PAAs having glass‐transition temperatures (T_g)s higher than 300 °C to the corresponding PIs. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6385–6393, 2006