Synthesis,characterization, and curing kinetics of novel ladder‐like polysilsesquioxanes containing side‐chain maleimide groups

Two ladder‐like polysilsesquioxanes (LPS) containing side‐chain maleimide groups have been synthesized successfully by reacting N‐(4‐hydroxyphenyl)maleimide (HPM) with LPS containing 100 mol % of chloropropyl groups (Ladder A ) and 50 mol % of each methyl and chloropropyl group (Ladder B ). HPM was synthesized by reacting maleic anhydride with 4‐aminophenol, and the resulting amic acid was imidized using p‐toluenesulfonic acid as a catalyst (Scheme 1 ). The LPSs were characterized by Fourier transform infrared (FTIR), ¹H nuclear magnetic resonance (NMR), proton‐decoupled ¹³C NMR, ²⁹Si NMR, wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Characterization indicated that these polymers had ordered ladder‐like structures with possible defects. These polymers were soluble in common solvents at ambient temperature, which suggested that they were not crosslinked. Both the polymers and the HPM were cured, and their kinetics were followed by dynamic DSC. The Ozawa and Kissinger methods were used to calculate activation energies for curing. Curing increased the temperature at which both 5% weight loss and maximum rate of weight loss were observed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4036–4046, 2004     

Amphiphilic membranes crosslinked and reinforced by POSS

This article concerns the synthesis and characterization of novel tricomponent amphiphilic membranes consisting of hydrophilic poly(ethylene glycol) (PEG) and hydrophobic polydimethylsiloxane (PDMS) segments cocrosslinked and reinforced by octasilane polyhedral oligomeric silsesquioxane (octasilane‐POSS) cages. Rapid and efficient network synthesis was effected by cocrosslinking diallyl‐telechelic PEG (A‐PEG‐A) and divinyl‐telechelic PDMS (V‐PDMS‐V) with pentamethylpentacyclosiloxane (D₅H), using Karstedt's catalyst in conjunction with Et₃N cocatalyst and water. Films were prepared by pouring charges in molds and crosslinking by heating at 60 °C for several hours. The films were characterized by sol fractions and equilibrium swelling both in hexane and water, extent of crosslinking, contact angle hysteresis, oxygen permeability, thermogravimetric analysis, and mechanical properties. The crosslinking of octasilane‐POSS achieved by the same catalyst system was studied in separate experiments. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4337–4352, 2004     

Behavior and surface energies of polybenzoxazines formed by polymerization with argon,oxygen, and hydrogen plasmas

Polybenzoxazine (PBZZ) thin films can be fabricated by the plasma‐polymerization technique with, as the energy source, plasmas of argon, oxygen, or hydrogen atoms and ions. When benzoxazine (BZZ) films are polymerized through the use of high‐energy argon atoms, electronegative oxygen atoms, or excited hydrogen atoms, the PBZZ films that form possess different properties and morphologies in their surfaces. High‐energy argon atoms provide a thermodynamic factor to initiate the ring‐opening polymerization of BZZ and result in the polymer surface having a grid‐like structure. The ring‐opening polymerization of the BZZ film that is initiated by cationic species such as oxygen atoms in plasma, is propagated around nodule structures to form the PBZZ. The excited hydrogen atom plasma initiates both polymerization and decomposition reactions simultaneously in the BZZ film and results in the formation of a porous structure on the PBZZ surface. We evaluated the surface energies of the PBZZ films polymerized by the action of these three plasmas by measuring the contact angles of diiodomethane and water droplets. The surface roughness of the films range from 0.5 to 26 nm, depending on the type of carrier gas and the plasma‐polymerization time. By estimating changes in thickness, we found that the PBZZ film synthesized by the oxygen plasma‐polymerization process undergoes the slowest rate of etching in CF₄ plasma. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4063–4074, 2004     

Fracture toughening of epoxy matrices with blends of resins of different molecular weights and other modifiers

The microstructure and fracture behavior of epoxy mixtures containing two monomers of different molecular weights were studied. The variation of the fracture toughness by the addition of other modifiers was also investigated. Several amounts of high‐molecular‐weight diglycidyl ether of bisphenol A (DGEBA) oligomer were added to a nearly pure DGEBA monomer. The mixtures were cured with an aromatic amine, showing phase separation after curing. The curing behavior of the epoxy mixtures was investigated with thermal measurements. A significant enhancement of the fracture toughness was accompanied by slight increases in both the rigidity and strength of the mixtures that corresponded to the content of the high‐molecular‐weight epoxy resin. Dynamic mechanical and atomic force microscopy measurements indicated that the generated two‐phase morphology was a function of the content of the epoxy resin added. The influence of the addition of an oligomer or a thermoplastic on the morphologies and mechanical properties of both epoxy‐containing mixtures was also investigated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3920–3933, 2004     

Viscosity,particle size distribution,and structural investigation of tetramethyloxysilane/2‐hydroxyethyl methacrylate sols during the sol–gel process with acid and base catalysts

The tetramethoxysilane (TMOS)/2‐hydroxylethyl methacrylate (HEMA) hybrid gels were synthesized with acid and base catalysts, via the in situ polymerization of HEMA, with and without the cosolvent methanol. With methanol in the TMOS/HEMA sol, the enhanced esterification and depolymerization reactions of the silanols resulted in a slower growth of silica particles. The silica particles that were synthesized with an acid catalyst were less than 40 nm. The thermal resistance of the poly(2‐hydroxyethyl methacrylate) (PHEMA) chains was enhanced by the addition of colloidal silica. The Fourier transform infrared characterizations and the exothermal peaks on the differential scanning calorimetry traces of these hybrid gels indicated chemical hybridization occurring as a result of condensation of the colloid silica and PHEMA at higher temperatures. Hence, the residual weight content of the hybrid gel after its synthesis with the base catalyst was even higher than the content of TMOS in the hybrid sol. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3476–3486, 2004     

Structure and properties of the mesophase of syndiotactic polystyrene. VIII. Solvent sorption behavior of syndiotactic polystyrene/p‐chlorotoluene mesophase membranes

A crystalline δ form of a syndiotactic polystyrene (sPS) membrane was prepared from a solution of sPS (1 wt %) and p‐chlorotoluene (p‐CT) by a solution‐casting method. The mesophase (δ empty form) of sPS was obtained by the extraction of the guest solvent from the δ form of sPS by a stepwise solvent‐extraction method. The sPS/p‐CT mesophase membrane [p‐CT (A‐M)] was used for the sorption of 1 mol % p‐CT for different times and for the sorption of different concentrations of p‐CT, chlorobenzene (CB), p‐xylene (p‐X), toluene, and chloroform for 48 h. The presence of solvents in the sPS membrane was confirmed by IR analysis. A thermal study revealed that the sorption amount of 1 mol % p‐CT increased with increasing immersion time, and the sorption amounts of different solvents increased with increasing solvent concentration. Differential scanning calorimetry results showed that the desorption peak temperature increased as the amount of the solvent increased in the clathrated sPS membrane. Wide‐angle X‐ray diffraction results showed that 2θ at 8.25° was slightly shifted toward 8°, and there was no change in the peak position at 10° for p‐CT (A‐M), which was immersed in different solvents (1 mol %); however, the intensity of 2θ at 10° was not similar for all the samples. Among the solvents used for the sorption studies at 1 mol %, p‐CT (A‐M) could sorb more p‐CT and CB than p‐X, toluene, and chloroform. The solvent sorption isotherm was the Langmuir sorption mechanism. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3439–3446, 2004     

Determination of nickel in alloys and plant leaves with salicylaldehyde 3-oxobutanoylhydrazone by spectrophotometry.

A simple and highly sensitive reagent of salicylaldehyde 3-oxobutanoylhydrazone (salicylaldehyde acetoacetic acid hydrazone, SAAH) was synthesized and studied for the spectrophotometric determination of nickel in detail. In the pH range 6, which greatly increased the selectivity, nickel reacted with SAAH to form a 1:1 yellow complex, having a sensitive absorption peak at 405 nm. Under the optimal conditions, Beer's law was obeyed over the range from 0.0117 to 0.1174 microg cm(-3). The apparent molar absorptivity was 3.025 x 10(5) dm3 mol(-1) cm(-1). The detection limit and the variation coefficient were found to be 1.752 ng cm(-3) and 1.0%, respectively. The method has been applied to the quantitative determination of nickel in different alloys and leaves.     

Fluorinated Copolymer-Oxide Hybrids

A fluorinated copolymer/metal oxide hybrid is fabricated by refluxing a high hydroxyl content fluorinated copolymer with tetraethoxysilane. The resulting organic-inorganic hybrids are transparent throughout the entire compositional range if processed with HCl as a catalyst. They exhibit a continuous variation in hardness, hydrophobicity, and abrasion resistance, intermediary between the properties of the pure polymer and that of a silica gel. The catalyst has a strong influence over the microstructure of the hybrid. ²⁹Si MAS-NMR indicates the presence of highly condensed silica clusters within the structure of the hybrid. If a Nd(III) alkoxide is used instead of TEOS, a Nd ³⁺-doped fluoropolymer is obtained. These results indicate that when a fluorinated copolymer contains groups amenable to hydrolysis and condensation, cross-linking with a metal alkoxide is possible, leading to an interesting families of hybrids.     

Wide‐angle X‐ray diffraction and differential scanning calorimetry study of the crystallization of poly(ethylene naphthalate), poly(butylene naphthalate), and their copolymers

The crystallization behavior of a series of poly(ethylene‐co‐butylene naphthalate) (PEBN) random copolymers was studied. Wide‐angle X‐ray diffraction (WAXD) patterns showed that the crystallization of these copolymers could occur over the entire range of compositions. This resulted in the formation of poly(ethylene naphthalate) or poly(butylene naphthalate) crystals, depending on the composition of the copolymers. Sharp diffraction peaks were observed, except for 50/50 PEBN. Eutectic behavior was also observed. This showed isodimorphic cocrystallization of the PEBN copolymers. The variation of the enthalpy of fusion of the copolymers with the composition was estimated. The isothermal and nonisothermal crystallization kinetics were studied. The crystallization rates were found to decrease as the comonomer unit content increased. The tensile properties were also measured and were found to decrease as the butylene naphthalate content of the copolymers increased. For initially amorphous specimens, orientation was proved by WAXD patterns after drawing, but no crystalline reflections were observed. However, the fast crystallization of drawn specimens occurred when they were heated above the glass‐transition temperature. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 843–860, 2004     

Bio‐based nanocomposites from functionalized plant oils and layered silicate

Some discovery work was done on the synthesis of clay nanocomposites based on renewable plant oils. Functionalized triglycerides, such as acrylated epoxidized soybean oil, maleinized acrylated epoxidized soybean oil, and soybean oil pentaerythritol maleates, combined with styrene were used as the polymer matrix. The miscibility of these monomers and clay organomodifier was assessed by solubility parameters. The formation of nanocomposites was confirmed by both X‐ray data and transmission electron microscopy. The morphology showed a mix of intercalated and partially exfoliated sheets. The flexural modulus increased 30% at only 4 vol % clay content, but there was no significant effect on flexural strength, glass‐transition temperature, and thermal stability. Property enhancement was related to the degree of exfoliation that depends on both the polarity and flexibility of the monomers. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1441–1450, 2004