电感耦合等离子体原子发射光谱法测定镍基单晶高温合金中Mo、W、Ta、Re、Ru时元素之间相互干扰的消除与校正的研究

称取镍基单晶高温合金0.100 0g于聚四氟乙烯烧杯中,先令其与盐酸9mL和硝酸1mL加热反应,待反应缓慢时滴加氢氟酸2mL并继续加热使样品完全溶解。加入500g·L^-1酒石酸溶液2mL,冷却至室温,在塑料容量瓶中加水定容至100.0mL。按仪器工作条件采用电感耦合等离子体原子发射光谱法测定其中5种合金元素(Mo、W、Ta、Re、Ru)的含量,选择分析谱线依次为204.598,207.911,240.063,197.312,240.272nm。结果发现:除了Re外,其余4种元素的测定中均受共存元素的光谱干扰,严重影响了测定结果的准确性。为克服其干扰,除了采用基体匹配法消除镍的基体干扰外,试验采用混合校正系数矩阵法对测定结果进行校准。通过一系列试验计算得到混合校准系数矩阵K,并应用于模拟样品的分析。结果表明:经过矩阵K的校准,所测定的5种元素的准确度显著提高,达到了消除共存元素之间光谱干扰的目的。通过精密度试验,测得上述5种元素测定值的相对标准偏差(n=11)均在1.5%以下,并通过标准加入法进行回收试验,测得5种元素的回收率为97.0%~105%。     

Asymmetric dimers can be formed by dewetting half-shells of gold deposited on the surfaces of spherical oxide colloids

Asymmetric dimers consisting of gold microcrystals and spherical silica colloids have been fabricated by depositing thin films of gold onto the spherical colloids to form half-shells, followed by annealing at elevated temperatures. The capability and feasibility of this procedure have been demonstrated with silica and titania beads of 0.2-2 mum in diameter and gamma-Fe2O3/polystyrene@SiO2 core-shell particles 0.5 mum in size. The dimensions of gold microcrystals could be conveniently varied in the range of 100-650 nm by controlling the thickness of gold films and/or the diameter of the spherical colloids. This method provides another route to asymmetric dimers made of colloidal particles that could be different in size, chemical composition, surface functionality, density or sign of surface charge, bulk property, or a combination of these properties.     

Synthesis and Mesogenic Properties of Liquid Crystals Containing Terminal Cyclohexylmethanol,Cyclopentylmethanol, Cyclobutylmethanol and Cyclopropylmethanol Moiety

Four series of compounds 11?50 containing terminal alicyclic rings such as cyclohexylmethyl, cyclopentylmethyl, cyclobutylmethyl, and cyclopropylmethyl rings were synthesized and their liquid crystal behavior studied. The ring size and the length of flexible alkoxy chain influence the phase formation in different ways. While the smaller ring and the shorter alkoxy chain tend to favor the formation of the N phase, the larger ring and the longer alkoxy chain tend to favor the formation of the SmC phase. All the compounds except 11 and 21 exhibit SmA phases. The widest temperature range of the N, SmA, and SmC phases are found in the compounds 41 , 46 , and 20 , respectively, which are 75 °C for 41 , 115 °C for 46 , and 100 °C for 20 .     

对固体圆二色光谱测试方法的再认识——兼谈“浓度效应”

对近期发展的固体圆二色(CD)光谱测试方法进行了概述、评价和比较, 着重探讨了“浓度效应”的存在使固体CD光谱失真的原因. 通过对本课题组和其他作者已报道的四种化合物的固体CD谱再测试的反思, 强调了依手性化合物的手性光谱学性质不同, 根据浓度梯度实验选择其合适测试浓度的必要性. 对固有手性的阻转异构化合物(S)-1,1'-联二萘酚(S-BINOL)进行了成膜法固体CD谱浓度梯度测试, 发现所得固体薄膜CD谱中也存在着“浓度效应”     

应用普通扫描仪作薄层色谱定量分析的初步研究

尝试应用普通扫描仪作薄层色谱定量分析。样品通过硅胶板层析展开后，用碘蒸汽显色，再用普通扫描仪记录其图像，通过图像分析技术计算出斑点中样品的量。结果表明，对油醇、油酸、月桂胺和焦谷氨酸油酯等长碳链有机化合物，样点在nmol级的范围内时计算量与实际量有良好的线性相关性。     

Direct electrochemistry and electrocatalysis of hemoglobin in gelatine film modified glassy carbon electrode

Direct electrochemical and electrocatalytic behavior of hemoglobin (Hb) immobilized on glass carbon electrode (GCE) containing gelatine (Gel) films was investigated. The characteristics of Hb/Gel film modified GC electrode were performed by using SEM microscopy, UV-vis spectroscopy and electrochemical methods. The immobilized Hb showed a couple of quasi-reversible redox peak with a formal potential of −0.38 V (versus SCE) in 0.1 M pH 7.0 PBS. The formal potential changed linearly from pH 4.03 to 8.41 with a slope value of −52.0 mV pH⁻¹, which suggested that a proton transfer was accompanied with each electron transfer (ET) in the electrochemical reaction. The Hb/gelatine/GCE displayed a rapid amperometric response to the reduction of H₂O₂ and nitrite.     

高稳定性CaO-ZrO2固体碱催化剂的表征和催化性能

用共沉淀法经高温焙烧制备了CaO摩尔分数从10%至50%的CaO-ZrO₂系列催化剂, 将其应用于碳酸丙烯酯和甲醇酯交换合成碳酸二甲酯过程, 并通过XRD, FT-IR, BET, ICP, CO₂-TPD, XPS等表征手段研究了催化剂的物性及其催化性能随组成变化的的规律. 结果表明, 当CaO摩尔分数高于30%时, 表面出现游离的CaO, 虽然具有强碱性和高活性, 但是稳定性差; 而当CaO摩尔分数低于30%时, Ca^2＋进入ZrO₂晶格, CaO与ZrO₂形成连续固溶体, 并且随着CaO含量的增加, 晶格氧的电荷密度增加, 催化剂的碱性增强, 使得CaO-ZrO₂催化剂在碳酸丙烯酯和甲醇酯交换合成碳酸二甲酯过程中获得了高活性和高稳定性.     

A New and Efficient Synthetic Method and Antibacterial Activities of Oxazolidinone Analogues

A series of novel oxazolidinone analogues were prepared by a new and efficient synthetic method and their antibacterial activities were determined. These compounds wer echaracterized by LC-MS and ^1H NMR.     

四元体系KCl-ZnCl2-HCl(～10.61%)-H2O(298.15K)的相平衡及其固相化合物

０引言研究发现，卤化物KX与ZnX２组成的复盐化合物是一种良好的激光基质材料犤１犦，在掺杂了稀土离子的这些化合物中已经实现了低温或室温下的激光输出犤２，３犦。在卤化物中，氯化物的发光强度又大于氟化物犤４犦。因此，我们以KCl与ZnCl２为研究对象，通过盐酸溶液中的相化学反应来了解它们之间可能形成新化合物的种类和溶液中的反应行为。本文对KCl与ZnCl２在２５℃１１％的盐酸－水四元体系中的相平衡关系进行了研究，并从体系中发现并得到了未见文献报道的５∶４型新化合物５KCl·４ZnCl２·３H２O。１实验部分１．１药品及…     

La0.8Ca0.2MnO3纳米线的制备及表征

利用Sol-gel法结合氧化铝模板技术制备了La0.8Ca0.2MnO3纳米线, 并研究了两种热处理方法对 La0.8Ca0.2MnO3纳米线结构和形貌的影响. 快速升温到800 ℃得到的La0.8Ca0.2MnO3纳米线较粗, 其直径大于氧化铝模板的孔径, 而经过缓慢升温到400 ℃预处理再升温到800 ℃得到的La0.8Ca0.2MnO3纳米线, 其直径和氧化铝模板的孔径相当, 都约为35 nm. X射线衍射和透射电镜分析结果表明, 两种方法得到的 La0.8Ca0.2MnO3纳米线都是具有钙钛矿结构的属于单斜晶系的多晶材料.