成分和厚度的依赖

通过调整Mn的成分，系统地研究了Ni81Fe19/Ni100-xMnx双层膜的磁学性质，特别是交换偏置场(Hex)的变化.当Ni100-xMnx中Mn的原子百分比在534%到600%之间时，对于150nm的Ni81Fe19，得到了最大的交换偏置场175kA/m，同时由于Mn对Ni81Fe19层的扩散所造成的磁矩的降低小于20%；高角x射线衍射证明Ni100-xMnx的晶格常数随着Mn成分的改变而变化，Mn含量越多，其晶格常数越大；制备态Ni100-xMnx膜晶格常数与θ相NiMn膜晶格常数的接近程度与NiMn膜θ相形成的容易程度相对应.也研究了交换偏置场随着Ni１００-xMnx厚度的变化，第一次得到了当Ni100-xMnx中Mn的原子百分比为706%时，Ni81Fe19(150nm)/Ni100-xMnx(90nm)双层膜在经过240℃，5h退火后，可以有80kA/m的交换偏置场，此时铁磁层磁矩的大小几乎不变. 关键词： Ni81Fe19/Ni100-xMnx 交换偏置场     

Preparation and Selectivity of Molecularly Imprinted Polymer Coating on the Micro Pore Membrane of Polytetrafluoroethylene

In order to obtain mechanically stable membrane for practical application, the imprinted polymer was synthesized in the pores of polyfluoromembrane, the binding and transport ability of the membrane were studied.     

Internet中的物理资源

对Internet中的物理资源进行了较系统的介绍，主要内容有：综合物理网站、物理期刊网站和物理教学网站，其中重点介绍了美国和欧洲主要国家的物理网站和物理期刊网站，利用这些物理站点，可以方便的进行文献检索、物理会议查询，物理教学相关资料的查询和世界各大学物理系的查询；可以方便快捷的了解当今世界各国的物理教学学科研的最新进展，文中对各个物理站点的使用方法都一一做了详细的介绍，以方便读者使用。     

Highly strained InxGa(1−x)As−InyAl(1−y)As (x>0.8,y<0.3) layers for short wavelength QWIP and QCL structures grown by MBE

Highly strained quantum cascade laser (QCL) and quantum well infrared photodetector (QWIPs) structures based on In_xGa_(1−x)As−In_yAl_(1−y)As (x>0.8,y<0.3) layers have been grown by molecular beam epitaxy. Conditions of exact stoichiometric growth were used at a temperature of 420°C to produce structures that are suitable for both emission and detection in the 2–5 μm mid-infrared regime. High structural integrity, as assessed by double crystal X-ray diffraction, room temperature photoluminescence and electrical characteristics were observed. Strong room temperature intersubband absorption in highly tensile strained and strain-compensated In_0.84Ga_0.16As/AlAs/In_0.52Al_0.48As double barrier quantum wells grown on InP substrates is demonstrated. Γ–Γ intersubband transitions have been observed across a wide range of the mid-infrared spectrum (2–7 μm) in three structures of differing In_0.84Ga_0.16As well width (30, 45, and 80 Å). We demonstrate short-wavelength IR, intersubband operation in both detection and emission for application in QC and QWIP structures. By pushing the InGaAs–InAlAs system to its ultimate limit, we have obtained the highest band offsets that are theoretically possible in this system both for the Γ–Γ bands and the Γ–X bands, thereby opening up the way for both high power and high efficiency coupled with short-wavelength operation at room temperature. The versatility of this material system and technique in covering a wide range of the infrared spectrum is thus demonstrated.     

Performance of various activators in ethylene polymerization based on an iron(II) catalyst system

Ethylisobutylaluminoxane (EBAO) and its analogues were synthesized by a reaction between an triethylaluminum (Et₃Al)/triisobutylaluminum (i‐Bu₃Al) mixture and 4‐fluorobenzeneboronic acid, phenylboronic acid, or n‐butaneboronic acid and subsequent hydrolysis with water. They were used as cocatalysts in ethylene polymerization catalyzed by an iron complex {[(ArN?C(Me))₂C₅H₃N]FeCl₂, where Ar is 2,6‐diisopropylphenyl}. Polyethylene with a high molecular weight and a narrow molecular weight distribution was prepared with modified EBAOs, and the performance of the iron complex at high polymerization temperatures was greatly improved. The activators for the iron complex also affected the polymerization activity and the molecular weight of the resultant polyethylene. It was suggested that the stereo and electronic effects of the substitute groups of aluminoxane contributed to the improved performance of the new activators. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1093–1099, 2004     

Intramolecular energy transferable (2,2‐diphenylvinyl)phenyl substituted poly(p‐phenylenevinylene) derivative with efficient photoluminescence and electroluminescence

A poly(p‐phenylenevinylene) (PPV) derivative containing a bulky (2,2‐diphenylvinyl)phenyl group in the side chain, EHDVP‐PPV, was synthesized by Gilch route. The reduced tolane‐bisbenzyl (TBB) defects, as well as the structure of the polymer, was confirmed by various spectroscopic methods. The intramolecular energy transfer from the (2,2‐diphenylvinyl)phenyl side group to the PPV backbone was studied by UV‐vis and photoluminescence (PL) of the obtained polymer and model compound. The polymer film showed maximum absorption and emission peaks at 454 and 546 nm, respectively, and high PL efficiency of 57%. A yellow electroluminescence (λ_max = 548 nm) was obtained with intensities of 6479 cd/m² when the light‐emitting diodes of ITO/PEDOT/EHDVP‐PPV/LiF/Al were fabricated. The maximum power efficiency of the devices was 0.729 lm/W with a turn‐on voltage of 3.6 V. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5636–5646, 2004     

Synthesis and characterization of well‐defined diblock and triblock copolymers of poly(N‐isopropylacrylamide) and poly(ethylene oxide)

Well‐defined diblock and triblock copolymers composed of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) (PEO) were successfully synthesized through the reversible addition–fragmentation chain transfer polymerization of N‐isopropylacrylamide (NIPAM) with PEO capped with one or two dithiobenzoyl groups as a macrotransfer agent. ¹H NMR, Fourier transform infrared, and gel permeation chromatography instruments were used to characterize the block copolymers obtained. The results showed that the diblock and triblock copolymers had well‐defined structures and narrow molecular weight distributions (weight‐average molecular weight/number‐average molecular weight < 1.2), and the molecular weight of the PNIPAM block in the diblock and triblock copolymers could be controlled by the initial molar ratio of NIPAM to dithiobenzoate‐terminated PEO and the NIPAM conversion. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 4873–4881, 2004     

Combined effects of clay modifications and compatibilizers on the formation and physical properties of melt‐mixed polypropylene/clay nanocomposites

The melt mixing technique was used to prepare various polypropylene (PP)‐based (nano)composites. Two commercial organoclays (denoted 20A and 30B) served as the fillers for the PP matrix, and two different maleated (so‐called) compatibilizers (denoted PP‐MA and SMA) were employed as the third component. The results from X‐ray diffraction (XRD) and transmission electron microscope (TEM) experiments revealed that 190 °C was an adequate temperature for preparing the nanocomposites. Nanocomposites were achieved only if specific pairs of organoclay and compatibilizer were simultaneously incorporated in the PP matrix. For example, PP/20A(5 wt %)/PP‐MA(10 wt %) and PP/30B(5 wt %)/SMA(5 wt %) composites exhibited nanoscaled dispersion of 20A or 30B in the PP matrix. Differential scanning calorimetry (DSC) results indicated that the organoclays served as nucleation agents for the PP matrix. Generally, their nucleation effectiveness increased with the addition of compatibilizers. The thermal stability enhancement of PP after adding 20A was confirmed with thermogravimetric analysis (TGA). The enhancement became more evident as a suitable compatibilizer was further added. However, for the 30B‐included composites, thermal stability enhancement was not evident. The dynamic mechanical properties (i.e., storage modulus and loss modulus) of PP increased as the nanocomposites were formed; the properties increment corresponded to the organoclay dispersion status in the matrix. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4139–4150, 2004     

Influence of solvents on the formation of ultrathin uniform poly(vinyl pyrrolidone) nanofibers with electrospinning

Although there have been many reports on the preparation and applications of various polymer nanofibers with the electrospinning technique, the understanding of synthetic parameters in electrospinning remains limited. In this article, we investigate experimentally the influence of solvents on the morphology of the poly(vinyl pyrrolidone) (PVP) micro/nanofibers prepared by electrospinning PVP solution in different solvents, including ethanol, dichloromethane (MC) and N,N‐dimethylformamide (DMF). Using 4 wt % PVP solutions, the PVP fibers prepared from MC and DMF solvents had a shape like a bead‐on‐a‐string. In contrast, smooth PVP nanofibers were obtained with ethanol as a solvent although the size distribution of the fibers was somewhat broadened. In an effort to prepare PVP nanofibers with small diameters and narrow size distributions, we developed a strategy of using mixed solvents. The experimental results showed that when the ratio of DMF to ethanol was 50:50 (w/w), regular cylindrical PVP nanofibers with a diameter of 20 nm were successfully prepared. The formation of these thinnest nanofibers could be attributed to the combined effects of ethanol and DMF solvents that optimize the solution viscosity and charge density of the polymer jet. In addition, an interesting helical‐shaped fiber was obtained from 20 wt % PVP solution in a 50:50 (w/w) mixed ethanol/DMF solvent. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3721–3726, 2004     

Differential pulse anodic stripping voltammetric determination of traces of copper with a tobramycin-Nafion modified electrode.

A Nafion-modified glassy carbon electrode incorporated with tobramycin for the voltammetric stripping determination of Cu2+ has been explored. The electrode was fabricated by tobramycin containing Nafion on the glassy carbon electrode surface. The modified electrode exhibited a significantly increased sensitivity and selectivity for Cu2+ compared with a bare glassy carbon electrode and the Nafion modified electrode. Cu2+ was accumulated in HAc-NaAc buffer (pH 4.6) at a potential of -0.6 V (vs. SCE) for 300 s and then determined by differential pulse anodic stripping voltammetry. The effects of various parameters, such as the mass of Nafion, the concentration of tobramycin, the pH of the medium, the accumulation potential, the accumulation time and the scan rate, were investigated. Under the optimum conditions, a linear calibration graph was obtained in the concentration range of 1.0 x 10(-9) to 5.0 x 10(-7) mol l(-1) with a correlation coefficient of 0.9971. The relative standard deviations for eight successive determinations were 4.3 and 2.9% for 1.0 x 10(-8) and 2.0 x 10(-7) mol l(-1) Cu2+, respectively. The detection limit (three times signal to noise) was 5.0 x 10(-10) mol l(-1). A study of interfering substances was also performed, and the method was applied to the direct determination of copper in water samples, and also in analytical reagent-grade salts with satisfactory results.